SABIC Innovative Plastics Ultem 2212 PEI (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Ultem 2212 PEI (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
20% Milled glass filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.43 g/cc | 1.43 g/cc | ASTM D 792 |
| Melt Flow | 13.2 g/10 min @Load 6.60 kg, Temperature 337 °C |
13.2 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 92.0 MPa | 13300 psi | Type I, 5 mm/min; ASTM D 638 |
| Elongation at Break | 6.0 % | 6.0 % | Type I, 5 mm/min; ASTM D 638 |
| Tensile Modulus | 4.27 GPa | 619 ksi | 5 mm/min; ASTM D 638 |
| Flexural Strength | 172 MPa | 24900 psi | 2.6 mm/min, 100 mm span; ASTM D 790 |
| Flexural Modulus | 5.10 GPa | 740 ksi | 2.6 mm/min, 100 mm span; ASTM D 790 |
| Izod Impact, Notched | 0.480 J/cm @Temperature 23.0 °C |
0.899 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| 3.84 J/cm @Thickness 3.20 mm |
7.19 ft-lb/in @Thickness 0.126 in |
reverse notched; ASTM D 256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C @Thickness 6.40 mm |
401 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |
| Glass Transition Temp, Tg | 217 °C | 423 °F | |
| UL RTI, Electrical | 170 °C | 338 °F | UL 746B |
| UL RTI, Mechanical with Impact | 170 °C | 338 °F | UL 746B |
| UL RTI, Mechanical without Impact | 170 °C | 338 °F | UL 746B |
| Flammability, UL94 | V-0 @Thickness 0.400 mm |
V-0 @Thickness 0.0157 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Arc Resistance | 0.00 - 60 sec | 0.00 - 60 sec | Tungsten, PLC code 7; ASTM D 495 |
| Comparative Tracking Index | 100 - 175 V | 100 - 175 V | PLC code 4; UL 746A |
| Hot Wire Ignition, HWI | 60 - 120 sec | 60 - 120 sec | PLC code 1; UL 746A |
| High Amp Arc Ignition, HAI | 15 - 30 arcs | 15 - 30 arcs | surface, PLC code 3; UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | 25.4 - 80.0 mm/min | 1.00 - 3.15 in/min | PLC code 2; UL 746A |
Users viewing this material also viewed the following:
- Dielectric Polymers NT-2802 Ultra Tack Tape (discontinued **)
- Overview of materials for Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced
- Mateck Highly Oriented Pyrolytic Graphite
- Solvay GEROPON® T/36 DF Surfactant
- Teknor Apex Sarlink® 4465 Thermoplastic Elastomer
- A. Schulman POLYFORT™ FPP 1876 22% Mineral Filled Copolymer, UV Inhibited Polypropylene
- Zotefoams Plastazote® LD24LC Low Density Polyethylene Foam, Large Cell
- Hexcel® HexWeb® CR III 5/32-5056-.001 Corrosion Resistant Specification Grade Aluminum Honeycomb
- A. Schulman ComAlloy Hiloy® 629 Nylon 6/6, Mineral Reinforced
Copyright © lookpolymers.com All Rights Reserved