SABIC Innovative Plastics LNP THERMOCOMP PH0400CX PA 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP PH0400CX PA 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* PH0400CX is a compound based on Nylon 6 resin. Added feature of this grade is: High Specific Gravity.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 4.00 g/cc | 0.145 lb/in³ | ASTM D792 |
| 4.00 g/cc | 0.145 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.170 % | 0.170 % | 50% RH, 24 hrs; ASTM D570 |
| 0.260 % | 0.260 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0044 - 0.0046 cm/cm @Time 86400 sec |
0.0044 - 0.0046 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0081 - 0.0083 cm/cm @Time 86400 sec |
0.0081 - 0.0083 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 92.0 MPa | 13300 psi | 5 mm/min; ISO 527 |
| 94.0 MPa | 13600 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 92.0 MPa | 13300 psi | 5 mm/min; ISO 527 |
| 94.0 MPa | 13600 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.3 % | 1.3 % | Type I, 5 mm/min; ASTM D638 |
| 1.5 % | 1.5 % | 5 mm/min; ISO 527 | |
| 1.6 % | 1.6 % | Flexural Strain, break, 2 mm/min; ISO 178 | |
| Elongation at Yield | 1.3 % | 1.3 % | Type I, 5 mm/min; ASTM D638 |
| 1.4 % | 1.4 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 13.98 GPa | 2028 ksi | 1 mm/min; ISO 527 |
| 17.7 GPa | 2570 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 157 MPa | 22800 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Yield Strength | 153 MPa | 22200 psi | 2 mm/min; ISO 178 |
| 155 MPa | 22500 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 12.9 GPa | 1870 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 13.26 GPa | 1923 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.710 J/cm | 1.33 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.31 J/cm | 8.07 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 27.0 kJ/m² | 12.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 14.0 J @Temperature 23.0 °C |
10.3 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 26.1 µm/m-°C @Temperature -30.0 - 30.0 °C |
14.5 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 40.1 µm/m-°C @Temperature -30.0 - 30.0 °C |
22.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM E 831 |
| Deflection Temperature at 1.8 MPa (264 psi) | 197 °C | 387 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 195 °C @Thickness 3.20 mm |
383 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Polimeri Europa SINKRAL G320 ABS (discontinued **)
- LG Chemical LUMID GP2309A(W) PA6+GF30%, General Purpose
- Lucobit Lucofin® 1411-t1 Polyolefin TPO Granules, White
- A. Schulman FORMION™ FI 389 Ionomer
- Formosa Plastics Formolene® L42009A Film (Butene Grade) LLDPE
- CP-Polymer-Technik Wellamid® 6000 MR 409 HWCP Mineral Nylon 6, Heat Stabilized, Conditioned
- Dow SE BR-1202C Stereospecific high cis-1,4 Polybutadiene (BR)
- Aremco HiE-Coat™ 840-MS High Emissivity Silicone-Ceramic Coating
- Ashley Polymers Ashlene® 149WO PBT Polyester, 45% Glass Reinforced
- Overview of materials for PVC, Wire and Cable Grade
Copyright © lookpolymers.com All Rights Reserved