Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 29.0 MPa | 4200 psi | 2 in/min; ASTM D638 |
RheTech Products T20P250-699UV 20% Talc Reinforced Polypropylene Copolymer, UV Stabilized, AC20157-120 Black Applications: Window trimCowl screensExterior componentsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | <= 29.0 MPa | <= 4210 psi | ISO/R527 |
Polykemi AB POLYfill PPC T16020 Polypropylene Copolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
Tensile Strength at Break | <= 29.0 MPa | <= 4210 psi | ISO/R527 |
Polykemi AB POLYfill PPH T15040 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
Tensile Strength at Break | <= 29.0 MPa | <= 4210 psi | ISO/R527 |
Polykemi AB POLYfill PPH T16040 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
Tensile Strength at Break | 29.0 MPa | 4210 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Geloy XTWE265 ASA Highly weatherable Geloy ASA profile extrusion grade for processes with simple or no calibration hardware.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength at Break | 29.0 MPa | 4210 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics GELOY XTWE265 ASA (Asia Pacific) Highly weatherable Geloy ASA profile extrusion grade for processes with simple or no calibration hardware. |
|||
Tensile Strength at Break | 29.0 MPa | 4210 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics GELOY CR7520 ASA General purpose ASA. Excellent weatherability, good flow/aesthetics and high impact. Rated F2 by UL. |
|||
Tensile Strength at Break | 29.0 MPa | 4200 psi | ASTM D638 |
Polymer Resources PPX-SF2 Modified PPO, Structural Foam Grade, Standard Flow
(Unverified Data**) Process: Foam MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Foam grades tested with foamed parts with a 10% weight reduction rel.. |
|||
Tensile Strength at Break | 29.0 MPa | 4210 psi | ASTM D638 |
Albis Plastics Cellulose Acetate Propionate CP808 (FDA), 17% Plasticizer
(discontinued **) Amorphous Cellulose Acetate Propionate (CAP)Characteristics: Strength, Hardness, Stiffness, Weatherability and Dimensional StabilityApplications: Brush Handles, Safety Glasses, Optical Products and .. |
|||
Tensile Strength at Break | 29.0 MPa | 4210 psi | ISO 527 |
FKuR Kunststoff Bio-Flex® S 5630 Compostable PLA Blend The BIO-FLEX® trade name indicates blends of co-polyester and PLA* with, depending on the particular grade, a very high content of natural resource material. BIO-FLEX® does not contain any sta.. |
|||
Tensile Strength at Break | 29.0 MPa | 4200 psi | ASTM D 638 |
LyondellBasell Hifaxâ„¢ AA56H Polypropylene Homopolymer Description: Hifaxâ„¢ AA56H medium high melt flow, 1,400 MPa flexural modulus, UL 94 V-2 flame retardant polypropylene homopolymer resin has an excellent combination of properties and processabil.. |
|||
Tensile Strength at Break | 29.0 MPa | 4210 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics SABIC PPCOMPOUND 19T1020 PP SABIC® PPcompound 19T1020 is a general purpose, talc filled, heat stabilized homopolymer polypropylene compound. This compound exhibits high flow and is suitable for injection molding application.. |
|||
Tensile Strength at Break | 29.0 MPa | 4210 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Valox® IQ325HP PBT (Asia Pacific) FDA compliant PBT resin, using chemically recycled post consumer PET Bottles. Fit to food contact applications. |
|||
Tensile Strength at Break | 29.0 MPa | 4210 psi | |
UBE UBEPOL BR15H HIPS (n-DM =0.03 wt %) Description: UBEPOL-BR15H is a in-between polymer of UBEPOL-BR15HB and UBEPOL-BR15HL.Information provided by UBE. |
|||
Tensile Strength at Break | 29.0 MPa | 4210 psi | |
UBE UBEPOL BR15HL HIPS (n-DM = 0.03 wt % and PH-3H = 0.03 wt %) Description: UBEPOL-BR15HL is a linear type of polymer with the high solution viscosity. In case of enlarging the dispersed rubber particle size in |
|||
Tensile Strength at Break | 29.0 MPa | 4210 psi | ISO 527 |
Eastman Drystar 0325 Copolyester This product-line is designed to meet the needs of converters seeking value-added solutions to their drying requirements of copolyesters. Eastman’s copolyesters are highly valued for their excellen.. |
|||
Tensile Strength at Break | 29.0 MPa | 4210 psi | ISO 527 |
Eastman Drystar 0603 Copolyester This product-line is designed to meet the needs of converters seeking value-added solutions to their drying requirements of copolyesters. Eastman’s copolyesters are highly valued for their excellen.. |
|||
Tensile Strength at Break | 29.0 MPa | 4210 psi | ASTM D638 |
Eastman Provista MP001 Copolymer Provista Copolymer MP001 is a resin specifically developed for extrusion into profiles where aesthetics such as high clarity and gloss, coupled with design flexibility, drive demand. Compared to com.. |
|||
Tensile Strength at Break | 29.0 MPa | 4210 psi | ISO 527-2/50 |
ExxonMobil Exxtral™ HMT 402 Performance Polyolefin Product Description: A specialty thermoplastic polyolefin resin with very high stiffness, high heat ageing resistance and detergent resistance designed for electrical applications such as washing ma.. |
|||
Tensile Strength at Break | 29.0 MPa | 4210 psi | ISO 527-1/-2 |
DuPont Performance Polymers Hytrel® 4069 Polyester Elastomer TPC-ET
(Unverified Data**) 40 Shore D High Performance Polyester ElastomerInformation provided by DuPont Performance Polymers |
|||
Tensile Strength at Break | 29.0 MPa | 4200 psi | ASTM D638 |
Chesterton ARC MXC Castable Extreme Wear Compound Description: An advanced ceramic composite, with flowable viscosity, for the repair and protection of all metal surfaces subjected to severe erosion, abrasion and chemical attack. It can be hand tro.. |
|||
Tensile Strength at Break | 29.0 MPa | 4210 psi | ISO 527-1/-2 |
DuPont Performance Polymers Hytrel® HTR8341G BK320 Polyester Elastomer TPC-ET
(Unverified Data**) 40 Shore D Slightly Lubricated High Viscosity Polyester Elastomer with Superior Fatigue Resistance Developed for Blow Molding Information provided by DuPont Performance Polymers |
|||
Tensile Strength at Break | 29.0 MPa | 4210 psi | ISO R 527 |
Addiplast Addilene J 110 Polypropylene Copolymer UnreinforcedInformation provided by Addiplast. |
|||
Tensile Strength at Break | 29.0 MPa | 4200 psi | ASTM D638 |
Americas Styrenics STYRON A-TECH® 1170 High Impact Polystyrene Product CharacteristicsGood impact resistanceConsistent colorabilityEasy processingFood Contact CompliantUL Classification 94HBTypical ApplicationsExtruded SheetSmall AppliancesRefrigeration Accesso.. |
|||
Tensile Strength at Break | 29.0 MPa | 4210 psi | ASTM D638 Die C |
3M Scotch-Weld™ EZ250060 Polyurethane Reactive (PUR) Easy 250 Wood Adhesive 3M™ Scotch-Weld™ Polyurethane Reactive (PUR) Easy 250 Wood Adhesive is 100% solid, warm temperature applied, moisture curing urethanes. This product bonds well to wood and wood bases surfaces as w.. |
|||
Tensile Strength at Break | 29.0 MPa | 4210 psi | ASTM D638 |
3M Dyneon™ THV 815GZ Fluorothermoplastic Granules Dyneon THV 815 GZ provides a balance of low permeation, thermal stability, and melt processability. IT can be used to prepare molded parts and extruded films, tubes, profiles, and wire coatings. It .. |
|||
Tensile Strength at Break | 29.0 MPa @Temperature 150 °C |
4210 psi @Temperature 302 °F |
ISO 527-2 |
Solvay Specialty Polymers Amodel® A-1240 L Polyphthalamide (PPA)
(discontinued **) Amodel A-1240 L is a 40% mineral filled polyphthalamide (PPA) that offers low warpage and excellent dimensional stability. This resin also has a high deflection temperature, flexural modulus and ten.. |
|||
Tensile Strength at Break | 29.0 MPa | 4210 psi | ASTM D638 |
SCG Chemicals EL-Lene™ H6140B High Density Polyethylene Blow Molding Key Characteristics:Good processabilityHigh stiffnessGood environmental stress cracking resistance (ESCR)High compressive and impact strengthExcellent appearanceOdorlessSafe for food contactGood pri.. |
|||
Tensile Strength at Break | 29.0 MPa | 4200 psi | 2 in/min; ASTM D638 |
RheTech Products HP510-01UV 28% Talc Reinforced High Performance Polypropylene Copolymer, UV Stabilized, Black Applications: Air ducts-structuralInterior trimI/P componentsCenter consolesInjection molding conditions reported in table.Information provided by RheTech Products. |