Polymer Property : Flexural Strength = 8410 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Strength | 58.0 MPa | 8410 psi | ASTM D790 |
| NYCOA 2326 HS Super-Tough, Heat Stabilized Nylon 6 Resin NYCOA 2326 HS is an impact modified, heat stabilized Nylon 6 resin, which offers outstanding toughness, impact strength and chemical resistance. NYCOA 2326 HS has been specially formulated to give a.. |
|||
| Flexural Strength | 58.0 MPa | 8410 psi | ISO 178 |
| Nilit FRIANYL A63 N-S20 Nylon 6.6 for injection molding Nylon 6.6 for injection molding, low viscosity, impact modified.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
| Flexural Strength | <= 58.0 MPa | <= 8410 psi | ISO 178 |
| Polykemi AB POLYfill PPH T15040CR Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
| Flexural Strength | <= 58.0 MPa | <= 8410 psi | ISO 178 |
| Polykemi AB POLYfill PPH T8040 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
| Flexural Strength | 58.0 MPa | 8410 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics LNP Faradex AS0039 ABS (Europe-Africa-Middle East) LNP* Faradex* AS0039 is a compound based on Acrylonitrile Butadiene Styrene resin containing Flame Retardant, Stainless Steel Fiber. Added features of this material include: EMI/RFI Shielding.This .. |
|||
| Flexural Strength | 58.0 MPa | 8410 psi | ISO 178 |
| Nilit RECONYL B S20 Recycled nylon 6 for injection molding Recycled nylon 6 for injection molding, impact modified (available only in black).Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
| Flexural Strength | 58.0 MPa | 8410 psi | |
| Lehmann & Voss LUVOCOM® 1850-7853 PBT, with PTFE Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Isotropic shrinkage characteri.. |
|||
| Flexural Strength | 58.0 MPa | 8410 psi | 2mm/min; ASTM D790 |
| Kingfa FRABS V-0 Flame Retardant ABS Features:UL 94 V-0 @ 1.5-3.0mmHigh toughnessFor extrusion moldingApplications:PlateElectric and electronic cabinetPCB boardInformation Provided by Kingfa Sci. & Tech. Co., Ltd. |
|||
| Flexural Strength | 58.0 MPa | 8410 psi | 2mm/min; ASTM D790 |
| Kingfa FRABS-518 Flame Retardant ABS Features:UL 94 V-0 @ 1.6-3.0mm, 5VB @ 2.0mmLow temperature impact resistanceApplications:Injection moldingPower tools accessoriesInformation Provided by Kingfa Sci. & Tech. Co., Ltd. |
|||
| Flexural Strength | 58.0 MPa | 8410 psi | 5 mm/min; ISO 178 |
| Gromax BTQ50-EQ00N1 Nylon 6, Impact Modified (Dry) Information provided by Gromax Enterprises Corp. |
|||
| Flexural Strength | 58.0 MPa | 8410 psi | ISO 178 |
| SABIC Innovative Plastics LNP LUBRILOY Z2000 PPO LNP* LUBRILOY* Z2000 is a compound based on PPO resin containing Proprietary Lubricant. Added feature of this material is: Wear Resistant. |
|||
| Flexural Strength | 58.0 MPa | 8410 psi | ISO 178 |
| SABIC Innovative Plastics LNP STAT-KON AX00756 ABS LNP STAT-KON* AX00756 is a compound based on ABS resin containing Stainless Steel. Added feature of this material is: Electrically Conductive. |
|||
| Flexural Strength | 58.0 MPa | 8410 psi | ISO 178 |
| SABIC Innovative Plastics LNP THERMOCOMP HB006 PA 11 (Asia Pacific) LNP* Thermocomp* HB006 is a compound based on Nylon 11 resin containing Glass Bead. |
|||
| Flexural Strength | 58.0 MPa | 8410 psi | ISO 178 |
| Styrolution Terluran® HI-12 ABS Terluran HI-12 is an injection molding grade of ABS with a very high toughness and easy flow.Very high toughnessEasy flowingUL 94 HB (1.6 & 3.2 mm)Information provided by Styrolution |
|||
| Flexural Strength | 58.0 MPa | 8410 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics LNP THERMOCOMP TF006 PU LNP THERMOCOMP TF006 is a compound based on Polyurethane containing 30% Glass Fiber. |
|||
| Flexural Strength | 58.0 MPa @Thickness 3.20 mm |
8410 psi @Thickness 0.126 in |
3-points, 2 mm/min, Injection Molded; ISO 178 |
| Styron MAGNUMâ„¢ 3904 Smooth Acrylonitrile Butadiene Styrene (ABS) Resin Overview: MAGNUMâ„¢ 3904 is an extrusion/thermoforming resin developed for high impact and other technical applications. The mass (continuous process) ABS technology of Styron ensures an ABS tech.. |
|||
| Flexural Strength | 58.0 MPa | 8410 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics XYLEX X8210 PC+POLYESTER PC+POLYESTER alloy. Unreinforced, transparent, impact modified for low temperature ductility |
|||
| Flexural Strength | 58.0 MPa | 8410 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics LNP THERMOCOMP MFB82I PP (Europe-Africa-Middle East) LNP* Thermotuf* MFB82I is a compound based on Polypropylene resin containing Glass Fiber, Glass Bead. |
|||
| Flexural Strength | 58.0 MPa | 8410 psi | ASTM D790 |
| A. Schulman POLYFORT™ FPP 1607 Talc Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 1607 is a 30% talc filled homopolymer polypropylene compound. Information provided by A. Schulman. |
|||
| Flexural Strength | 58.0 MPa | 8410 psi | ASTM D790 |
| A. Schulman POLYFORT™ FPP 1607 Talc Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 1607 is a 30% talc filled homopolymer polypropylene compound. Information provided by A. Schulman. |
|||
| Flexural Strength | 58.0 MPa | 8410 psi | ASTM D790 |
| A. Schulman POLYFORT™ FPP 1607 Talc Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 1607 is a 30% talc filled homopolymer polypropylene compound. Information provided by A. Schulman. |
|||
| Flexural Strength | 58.0 MPa | 8410 psi | ASTM D790 |
| A. Schulman POLYFORT™ FPP 1607 Talc Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 1607 is a 30% talc filled homopolymer polypropylene compound. Information provided by A. Schulman. |
|||
| Flexural Strength | 58.0 MPa | 8410 psi | ISO 178 |
| Breplast Bretene PP Polypropylene Composite Recovered polypropylene compositeInformation provided by Breplast S.p.A. |
|||
| Flexural Strength | 58.0 MPa | 8410 psi | ISO 178 |
| Azoty Tarnow™ TARNOFORM 400 LS POM Injection molding grade based on Tarnoform 400 modified with soluble light stabilizers improving weathering stability.Information provided by Zakłady Azotowe w Tarnowie-Moscicach S.A. |
|||
| Flexural Strength | 58.0 MPa | 8410 psi | ISO 178 |
| Cathay PA512 Renewable Engineering Polyamide Cathay engineering polyamides contain 26-100% renewably sourced material. Advantages: Operates at similar conditions to PA66; Suitable for injection, compounding and extrusion; Stable mechanical pr.. |
|||
| Flexural Strength | 58.0 MPa | 8410 psi | ASTM D790-07 |
| 3M Scotchkote™ 2400 Pipe Renewal Liner NSF/ANSI-61 certified polyurea formulation is 100% solids and contains no epoxy resin. It is designed to help solve a wide variety of problems common to potable water systems. It utilizes a trenchle.. |
|||
| Flexural Strength | 58.0 - 76.0 MPa @Strain 5.00 % |
8410 - 11000 psi @Strain 5.00 % |
ASTM D790 |
| Arkema Group KYNAR® 740 Polyvinylidene Fluoride Homopolymer - Injection Molding and Extrusion Characteristics: Natural resin - translucent, off-white hemispheres. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechanical strength, low permeabili.. |
|||
| Flexural Strength | 58.0 - 76.0 MPa @Strain 5.00 % |
8410 - 11000 psi @Strain 5.00 % |
ASTM D790 |
| Arkema Group KYNAR® 740-02 Polyvinylidene Fluoride Homopolymer - Injection Molding and Extrusion Characteristics: Natural resin - translucent, off-white hemispheres. Flame and smoke suppressant. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mecha.. |
|||
| Flexural Strength | <= 58.0 MPa | <= 8410 psi | ISO 178 |
| Polykemi AB POLYfill PPH T20040 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
| Flexural Strength | <= 58.0 MPa | <= 8410 psi | ISO 178 |
| Polykemi AB POLYfill PPH T5040DS Polypropylene Homopolymer, Mineral Reinforced, Detergent Resistant Information provided by Polykemi AB |
|||