Category | Polymer , Thermoplastic , Polypropylene (PP) |
Manufacturer | SABIC Innovative Plastics (GE Plastics) |
Trade Name | LNP THERMOCOMP |
Port | Shanghai port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Download PDF | SABIC Innovative Plastics LNP THERMOCOMP MFB82I PP (Europe-Africa-Middle East).pdf ![]() |
Price | EMAIL US sales@lookpolymers.com |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.32 g/cc | 0.0477 lb/in³ | ISO 1183 |
Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | on Tensile Bar; SABIC Method |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 50.0 MPa | 7250 psi | 5 mm/min; ISO 527 |
Elongation at Break | 3.5 % | 3.5 % | 5 mm/min; ISO 527 |
Tensile Modulus | 4.50 GPa | 653 ksi | 1 mm/min; ISO 527 |
Flexural Strength | 58.0 MPa | 8410 psi | 2 mm/min; ISO 178 |
Flexural Modulus | 3.80 GPa | 551 ksi | 2 mm/min; ISO 178 |
Izod Impact, Notched (ISO) | 14.0 kJ/m² | 6.66 ft-lb/in² | 80*10*4; ISO 180/1A |
Izod Impact, Unnotched (ISO) | 35.0 kJ/m² | 16.7 ft-lb/in² | 80*10*4; ISO 180/1U |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear, Parallel to Flow | 37.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
20.6 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
CTE, linear, Transverse to Flow | 125 µm/m-°C @Temperature 23.0 - 60.0 °C |
69.4 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
Deflection Temperature at 1.8 MPa (264 psi) | 133 °C | 271 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |