Gromax BTQ50-EQ00N1 Nylon 6, Impact Modified (Dry)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Impact Grade |
| Manufacturer | Gromax |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Gromax BTQ50-EQ00N1 Nylon 6, Impact Modified (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Gromax Enterprises Corp.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.06 g/cc | 1.06 g/cc | ISO 1183 |
| Moisture Absorption | 1.60 % | 1.60 % | ISO 62 |
| Maximum Moisture Content | 0.10 | 0.10 | Karl Fischer |
| Linear Mold Shrinkage, Flow | 0.017 cm/cm | 0.017 in/in | 60x60x2 mm; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.018 cm/cm | 0.018 in/in | 60x60x2 mm; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 70 | 70 | [N/mm<sup>2<sup>]; ISO 7619 |
| Tensile Strength | 39.2 MPa | 5690 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Break | 35 % | 35 % | 50 mm/min; ISO 527 |
| Flexural Strength | 58.0 MPa | 8410 psi | 5 mm/min; ISO 178 |
| Flexural Modulus | 1.43 GPa | 208 ksi | 5 mm/min; ISO 178 |
| Izod Impact, Notched | >= NB | >= NB | 5 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | ISO 180-1A |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179-1eU |
| Charpy Impact, Notched | 0.800 J/cm² @Temperature -30.0 °C |
3.81 ft-lb/in² @Temperature -22.0 °F |
ISO 179-1A |
| 2.00 J/cm² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1,-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | ISO 75-1,-2 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 245 - 260 °C | 473 - 500 °F | ISO 294 |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | ISO 294 |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2.00 - 6.00 hour | 2.00 - 6.00 hour |
Users viewing this material also viewed the following:
- Imerys Kaolexâ„¢ BN Kaolin
- Solvay Specialty Polymers Ixan® PVS 119 Polyvinylidene Chloride (PVDC)
- Special Metals DURANICKEL® 301 (UNS N03301) Annealed and Aged Rod and Bar
- Sichuan Deyang Haton® hGR515 Polyphenylene Sulfide/PA Alloy
- Sumitomo Bakelite North America RX® 1-520/RX® 1310 Short-Glass Reinforced Diallyl Phthalate
- SABIC Innovative Plastics LNP THERMOCOMP M7001XXH PP
- Polyplastics Duranex® CRN7000 Polybutylene Terephthalate (PBT), Low gas generation, Low contact contamination, FR, UL approved regrind 50%
- DuPont Teijin Films Melinex® CORE 1 & 3380 Polyester Film
- Dymax 9-20526 HGA and OHGA Disk Drive Adhesive
Copyright © lookpolymers.com All Rights Reserved