Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 155 MPa | 22500 psi | ISO 178 |
Panjin Zhongrun Chemerize 012P High Viscosity CoPEEK Information provided by Bieglo Gmbh. |
|||
Flexural Strength | 155 MPa | 22500 psi | |
Quadrant EPP Duratron® PAI T4301 PAI + graphite + PTFE, extruded (ISO Data) The addition of PTFE and graphite provides higher wear resistance and lower coefficient of friction compared to the unfilled grade as well as a lower tendency to stick-slip. Duratron T4301 PAI also .. |
|||
Flexural Strength | <= 155 MPa | <= 22500 psi | ISO 178 |
Polykemi AB POLYshine PBT D223 GF10 FR PBT, Glass-Fiber Reinforced, Flame Retardant Information provided by Polykemi AB |
|||
Flexural Strength | 155 MPa @Thickness 3.17 mm |
22500 psi @Thickness 0.125 in |
ASTM D790 |
PTS Tristar® PC-30GFR 30% Glass Reinforced Polycarbonate Information provided by Polymer Technology and Services, LLC (PTS). |
|||
Flexural Strength | 155 MPa | 22500 psi | at 5% strain; ASTM D790 |
Solvay Specialty Polymers Radel® R-7120 Polyphenylsulfone, 20% glass fiber
(discontinued **) RADEL R 7120 is a 20% glass fiber reinforced grade of RADEL R polyphenylsulfone developed specifically for aircraft interior applications. The product complies with the FAA regulation 14CFR Part 25 .. |
|||
Flexural Strength | 155 MPa @Temperature -40.0 °C |
22500 psi @Temperature -40.0 °F |
ASTM D790 |
BASF Capron® 8202 NL Nylon 6 (Conditioned)
(discontinued **) Information provided by BASF Corporation.Capron® is no longer a part of the BASF standard line. The BASF nylon products have been consolidated in the Ultramid ® line. |
|||
Flexural Strength | 155 MPa | 22500 psi | |
Lehmann & Voss LUVOCOM® 1850/CF/10/GF/10/GK/10/GS/5/FR PBT, with carbon fiber, glass fiber, glass spheres and glass flakes, fire protection Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High dimensionally stable precision parts, even at elevated temperatures and narrow tolerance r.. |
|||
Flexural Strength | 155 MPa | 22500 psi | |
Lehmann & Voss LUVOCOM® 50-8025 Polycarbonate, with glass fiber and PTFE Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.High-strength and high-stiff parts; low coefficient of expansi.. |
|||
Flexural Strength | 155 MPa | 22500 psi | 1.3 mm/min; ASTM D790 |
Lavergne VYPET VNT 615 FR PET 15% Glass Reinforced, Flame Retardant Vypet VNT 615 FR is a 15% fiberglass reinforced flame retardant PET injection molding compound designed for electrical and structural applications.Features: Flame retardant; UL yellow card file E216.. |
|||
Flexural Strength | 155 MPa | 22500 psi | 5 mm/min; ISO 178 |
Gromax BFG10-BN00N1 Nylon 6 10% Glass Filled (Dry) Information provided by Gromax Enterprises Corp. |
|||
Flexural Strength | 155 MPa | 22500 psi | ISO 178 |
Solvay TECHNYL® A 218G1 V25 Black 34N PA66, 25% glass fiber, Conditioned Description: Polyamide 66, reinforced with 25% of glass fiber, for injection molding. This grade shows an improved retention of properties after long term ageing in automotive cooling liquids. Avail.. |
|||
Flexural Strength | 155 MPa | 22500 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Valox® DR51 PBT (Europe-Africa-Middle East) VALOX DR51 is a 15% glass fiber reinforced PBT injection moulding resin with excellent mechanical, thermal and electrical performance. Applications: spotlights, appliance housings, handles. |
|||
Flexural Strength | 155 MPa | 22500 psi | |
SPS Guang Zhou POLLITEâ„¢ 1002G30 Flame-retarded/GF30%-Polycarbonate Characteristic: High mechanical properties, high rigidity, high heat resistant, good dimensional stability, good flame retardanceApplications: E/E parts, power tool, office suppliesInformation Provi.. |
|||
Flexural Strength | 155 MPa | 22500 psi | ISO 178 |
SABIC Innovative Plastics LNP Thermocomp JF003L PES LNP* Thermocomp* JF003L is a compound based on Polyethersulfone (PES) containing Glass Fiber. Characteristics of this grade are Low Extractable.This data was supplied by SABIC-IP for the Americas r.. |
|||
Flexural Strength | 155 MPa | 22500 psi | 3-Point Bending; ISO 178 |
Styron INSPIREâ„¢ DLGF 9621.00 Compounded Polypropylene, 60% LGF Overview: DLGF 9621.00 is a polypropylene homopolymer reinforced with 60% by weight of long glass fiber. PP-LGF60, Long Glassfiber Granulate). DLGF 9621.00 is produced by pultrusion/melt-impregnatio.. |
|||
Flexural Strength | 155 MPa | 22500 psi | 3-Point Bending; ISO 178 |
Styron INSPIREâ„¢ DLGF 9631.01 Z Polypropylene homopolymer, 60% LGF Overview: DLGF 9631.01 Z is based on polypropylene homopolymer and reinforced with 60% by weight of long glass fiber. (PP-LGF 60, Long Glassfiber Granulate). DLGF 9631.01 Z is produced by pultrusion.. |
|||
Flexural Strength | 155 MPa | 22500 psi | 3-Point Bending; ISO 178 |
Styron LGF 9621 Homopolymer Polypropylene Overview: LGF 9621 is polypropylene homopolymer reinforced with 60% by weight of long glass fibers. (PP-LGF60, Long Glass fiber Granulate). This PP-LGF60 is a ‘concentrate’ which has to be.. |
|||
Flexural Strength | 155 MPa | 22500 psi | 2mm/min; ISO 178 |
Teijin Panlite® GV-3430R High Flame Retardancy, Glass Fiber Reinforced Polycarbonate Resin GF 30% reinforced, improved flame retardance and mold release grade, meeting UL 94 V-2.Applications:Mechanical, electric and electronic components that need mechanical property e.g., stiffnessPrecis.. |
|||
Flexural Strength | 155 MPa | 22500 psi | ASTM-D790 |
Polyram Polytron P40B03 Copolymer Polypropylene, Chemically Coupled 40% Long Glass Fiber A CHEMICALLY COUPLED 40% LONG GLASS FIBERS REINFORCED BLACK POLYPROPYLENE, HEAT STABILIZED FOR INJECTION MOLDING APPLICATION.These products have significantly improved impact performance characteris.. |
|||
Flexural Strength | 155 MPa | 22500 psi | ASTM D790 |
Polyram PlusTek RA303G4 Nylon 6.6, 20% Glass Fiber 20% glass fiber reinforced, heat stabilized polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Flexural Strength | 155 MPa | 22500 psi | cond; ISO 178 |
DSM Novamid® 1010GN2-20 NAT/BK37 PA6-GF20 FR(17) 20% Glass Reinforced, Flame Retardant |
|||
Flexural Strength | 155 MPa | 22500 psi | ASTM D790 |
Beijing Chemical Industry KAIFA® 304-G20 PBT Resin 20% glass fiber reinforced, flame retardant, low bleeding, UV-resistantInformation provided by Beijing Chemical Industry Research Institute (Group) |
|||
Flexural Strength | 155 MPa | 22500 psi | |
Quadrant EPP Ketron® GF30 PEEK + glassfibres, extruded (ISO Data) This 30 % glass fibre reinforced grade offers a higher stiffness and creep resistance than Ketron PEEK-1000 and has a much better dimensional stability. This grade is very appropriate for structural.. |