Solvay Specialty Polymers Radel® R-7120 Polyphenylsulfone, 20% glass fiber  (discontinued **)

Category Polymer , Thermoplastic , Polysulfone (PSU) , Polyphenylsulfone, Glass or Carbon Fiber Reinforced
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Radel® R-7120 Polyphenylsulfone, 20% glass fiber  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
RADEL R 7120 is a 20% glass fiber reinforced grade of RADEL R polyphenylsulfone developed specifically for aircraft interior applications. The product complies with the FAA regulation 14CFR Part 25 Appendix F, offering vertical burn resistance, very low smoke generation, and, through the use of proprietary additives, low heat release values in the Ohio State University (OSU) rate of heat release method. It also generates low flaming-mode toxic gas emissions.This high-performance thermoplastic compound offers increased strength, stiffness, and creep resistance relative to unreinforced polyphenylsulfone. Additionally, this resin offers reliable toughness and good resistance to most fluids found in the aviation industry, as well as exceptional hydrolytic stability and high heat deflection temperature. Parts can be fabricated from RADEL R-7120 resin using conventional injection molding equipment. This product was formerly known as PXM-04098.
Physical Properties Metric English Comments
Density 1.42 g/cc
0.0513 lb/in³
ASTM D792
Melt Flow 12 g/10 min

@Load 2.16 kg,
Temperature 380 °C
12 g/10 min

@Load 4.76 lb,
Temperature 716 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 117 MPa
17000 psi
ASTM D638
Elongation at Break 2.2 %
2.2 %
ASTM D638
Tensile Modulus 7.30 GPa
1060 ksi
ASTM D638
Flexural Strength 155 MPa
22500 psi
at 5% strain; ASTM D790
Flexural Modulus 6.50 GPa
943 ksi
ASTM D790
Izod Impact, Notched 0.750 J/cm
1.41 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 180 °C
356 °F
ASTM D648
Processing Properties Metric English Comments
Melt Temperature 349 - 377 °C
660 - 711 °F
injection molding
Mold Temperature 107 - 163 °C
225 - 325 °F
Drying Temperature 165 - 177 °C

@Time 14400 sec
329 - 351 °F

@Time 4.00 hour