Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 71.0 MPa | 10300 psi | ASTM D790 |
PolyOne Geon™ Vinyl Rigid Molding M5240 Polyvinyl Chloride, Rigid (PVC, Rigid) Information provided by PolyOne |
|||
Flexural Strength | 71.0 MPa | 10300 psi | ASTM D790 |
PolyOne Geon™ Vinyl Rigid Molding M5700 Natural Polyvinyl Chloride, Rigid (PVC, Rigid) NOTE: Geon weatherable compounds contain pigments and ingredients that, along with processing conditions, contribute to the weathering performance of the PVC compounds. The weathering performance of.. |
|||
Flexural Strength | 71.0 MPa | 10300 psi | ASTM D790 |
PolyOne Geon™ Vinyl Rigid Molding M5731 Polyvinyl Chloride, Rigid (PVC, Rigid) NOTE: Geon weatherable compounds contain pigments and ingredients that, along with processing conditions, contribute to the weathering performance of the PVC compounds. Dark colored compounds do not.. |
|||
Flexural Strength | 71.0 MPa | 10300 psi | ASTM D790 |
Solvay Specialty Polymers Amodel® AT-5001 Polyphthalamide (PPA) Resin, at 50% RH
(discontinued **) AMODEL AT-5001 polyphthalamide resin is a neat ductile material that offers superior retention of properties after humid thermal aging, high impact at low temperature, and better mechanical properti.. |
|||
Flexural Strength | 71.0 MPa | 10300 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP BX02715 SAN LNP* LUBRICOMP* BX02715 is a compound based on SAN containing proprietary fillers. Added features of this grade include: Wear Resistant, Tight Dimensional Tolerance, Good for Water Meter Applicati.. |
|||
Flexural Strength | 71.0 MPa | 10300 psi | ASTM D790 |
PolyOne Stat-Tech™ NJ-10SS/000 Nylon 12 - 10% Stainless Steel Reinforced
(discontinued **) Data provided by PolyOne. |
|||
Flexural Strength | 71.0 MPa | 10300 psi | 2 mm/min; ISO 178 |
Ineos ABS Lustran® ABS 377 Plating, Injection Molding Grade |
|||
Flexural Strength | 71.0 MPa | 10300 psi | 2 mm/min; ISO 178 |
Ineos ABS Lustran® ABS 440 Injection Molding Grade Lustran® ABS 440 has medium impact strength and is injection molding grade. |
|||
Flexural Strength | 71.0 MPa | 10300 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP DX98306H PC (Asia Pacific) LNP* Lubricomp* DX98306H is a compound based on Polycarbonate resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated, Low Extractible. |
|||
Flexural Strength | 71.0 MPa | 10300 psi | ASTM D790 |
SABIC Innovative Plastics NORYL SE100V PPE+HIPS (Asia Pacific) |
|||
Flexural Strength | 71.0 MPa | 10300 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP WL0049 PBT LNP* LUBRICOMP* WL0049 is a compound based on PBT containing 20% PTFE. Added features include: Wear Resistant, Flame Retardant. |
|||
Flexural Strength | 71.0 MPa | 10300 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP Stat-kon CX01039 PS (Europe-Africa-Middle East) LNP* Stat-kon* CX01039 is a compound based on Polystyrene resin containing Proprietary Filler(s). Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP.. |
|||
Flexural Strength | 71.0 MPa | 10300 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics XYLEX X7300 PC+POLYESTER (Europe-Africa-Middle East) PC+POLYESTER unreinforced alloy. High flow, chemically resistant with excellent optical quality. UV-stabilized. |
|||
Flexural Strength | 71.0 MPa | 10300 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Xylex X7300OQ PC+POLYESTER (Europe-Africa-Middle East) PC+ POLYESTER unreinforced alloy developed for optical or lense market. High flow with good impact and excellent optical quality.This data was supplied by SABIC-IP for the Europe-Africa-Middle East.. |
|||
Flexural Strength | 71.0 MPa | 10300 psi | ASTM D790 |
Techmer ES Plastiblend® ABS 8009 FR Availability: North AmericaForms: PelletsFeatures: Flame Retardant and High Heat ResistanceInformation provided by TP Composites, Inc. |
|||
Flexural Strength | 71.0 MPa | 10300 psi | ASTM D790 |
Techmer ES Plastiblend® ABS E Availability: North AmericaForms: PelletsFeatures: High ViscosityProcessing Method: Blow Molding and ExtrusionInformation provided by TP Composites, Inc. |
|||
Flexural Strength | 71.0 MPa | 10300 psi | ASTM Test |
Styrolution Luran® S 778 T ASA Luran S 778 T is an injection molding ASA grade with enhanced toughness and heat resistance.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS. |
|||
Flexural Strength | 71.0 MPa | 10300 psi | ISO 178 |
SABIC Innovative Plastics LNP Thermocomp 9X04488 POLYPHENYLENESULFONE LNP* Thermocomp* 9X04488 is a compound based on POLYPHENYLENESULFONE resin containing Mineral.This data was supplied by SABIC-IP for the Americas region. |
|||
Flexural Strength | 71.0 MPa | 10300 psi | ASTM D790 |
SABIC Innovative Plastics NORYL EBN90 PPE+PS (Asia Pacific) PPE + PS, FR Blow molding grade |
|||
Flexural Strength | 71.0 MPa | 10300 psi | ASTM D790 |
A. Schulman SCHULAMID® 66 MV3HI High Impact Nylon 6/6 Information provided by A. Schulman. |
|||
Flexural Strength | 71.0 MPa | 10300 psi | ASTM D790 |
A. Schulman SCHULAMID® 66 MV3HI High Impact Nylon 6/6 Information provided by A. Schulman. |
|||
Flexural Strength | 71.0 MPa | 10300 psi | ASTM D790 |
A. Schulman SCHULAMID® E-17222 High Impact Nylon 66 Information provided by A. Schulman. |
|||
Flexural Strength | 71.0 MPa | 10300 psi | ASTM D790 |
A. Schulman SCHULAMID® 66 MV3HI High Impact Nylon 6/6 Information provided by A. Schulman. |
|||
Flexural Strength | 71.0 MPa | 10300 psi | ASTM D790 |
A. Schulman SCHULAMID® E-17222 High Impact Nylon 66 Information provided by A. Schulman. |
|||
Flexural Strength | 71.0 MPa | 10300 psi | |
Cosmic Plastics ID-40 Orlon Filled Ortho Diallyl Phthalate Molding Compound Data provided by the manufacturer. |
|||
Flexural Strength | 71.0 MPa @Strain 5.00 % |
10300 psi @Strain 5.00 % |
ASTM D790 |
Eastman Spectar® Clear Copolyester for Thermoforming Applications:Decorative Light-Transmitting PanelsHeavy gauge sheet displaysKey Attributes:Easy to print and decorateExcellent clarityExcellent thermoforming characteristicsGood chemical resistanceOd.. |
|||
Flexural Strength | 71.0 MPa | 10300 psi | 2 mm/min; ISO 178 |
Chi Mei Polylac® PA-777E ABS - High Heat Ultra High Heat |
|||
Flexural Strength | 71.0 MPa | 10300 psi | ASTM D790 |
A. Schulman ComAlloy Hiloy® 102 Polypropylene, Glass Reinforced Data provided by the manufacturer, ComAlloy International Company.20% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Flexural Strength | 71.0 MPa | 10300 psi | ASTM D790 |
Techmer ES Plastiblend® ABS 922 NAT Availability: North AmericaForms: PelletsInformation provided by TP Composites, Inc. |