Ineos ABS Lustran® ABS 440 Injection Molding Grade
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded |
| Manufacturer | Ineos ABS |
| Trade Name | Lustran® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos ABS Lustran® ABS 440 Injection Molding Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Lustran® ABS 440 has medium impact strength and is injection molding grade.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | ISO 294-4 |
| Melt Flow | 20 g/10 min @Load 10.0 kg, Temperature 220 °C |
20 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 112 | 112 | ISO 2039-2 |
| Tensile Strength at Break | 34.0 MPa | 4930 psi | 50 mm/min; ISO 527-1,-2 |
| Tensile Strength, Yield | 48.0 MPa | 6960 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Break | 20 % | 20 % | 50 mm/min; acc. ISO 527-1,-2 |
| Tensile Modulus | 2.50 GPa | 363 ksi | 1 mm/min; ISO 527-1,-2 |
| Flexural Strength | 71.0 MPa | 10300 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.40 GPa | 348 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² @Temperature -30.0 °C |
3.81 ft-lb/in² @Temperature -22.0 °F |
ISO 180-1A |
| 14.0 kJ/m² @Temperature -20.0 °C |
6.66 ft-lb/in² @Temperature -4.00 °F |
ISO 180-1A | |
| 19.0 kJ/m² @Temperature 23.0 °C |
9.04 ft-lb/in² @Temperature 73.4 °F |
ISO 180-1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 96.0 °C | 205 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C | 198 °F | ISO 75-1,-2 |
| Vicat Softening Point | 99.0 °C @Load 5.10 kg |
210 °F @Load 11.2 lb |
120°C/hour; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 90 % | 90 % | Angle 60°; ISO 2813 |
Users viewing this material also viewed the following:
- MV Labs SM100 Sm(C2H3O2)3·3H2O Samarium acetate hydrate
- PolyOne Geon™ Vinyl Flexible R235AE Polyvinyl Chloride, Flexible (PVC, Flexible)
- FKuR Kunststoff Fibrolon® F 8530 Biodegradable Wood-Plastic Compound, Fiber Reinforced
- Materion Beryllium Copper Alloy M25 Wire; 1/2HT (TH02) Temper; 1.3-12.7 mm Diameter (UNS C17300)
- Latrobe Lescalloy® UT-18 VAC-ARC ; 4 in. round High Strength Alloy Steel
- Samsung Cheil Industries Infino® NH-1001T PC/ABS, Unreinforced FR
- Total PPH 5042 Polypropylene, Homopolymer
- A. Schulman FORMION™ FI 395 Ionomer
- BASF Paliotan® Yellow L 1145 Color Additive
- Axiall 14750 Moldings & Extrusions Flexible PVC
Copyright © lookpolymers.com All Rights Reserved