Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 95.0 - 130 MPa | 13800 - 18900 psi | ASTM D790 |
Prodways PLASTCure Model 300 3D Printing Polymer Good mechanical properties.Broad range of dental model applications.Information provided by Genistar. |
|||
Flexural Strength | 110 - 130 MPa | 16000 - 18900 psi | ASTM D790-03 |
Proto3000 Objet RGD525 High Temperature Prototyping Polymer Information provided by Proto3000 for their protoyping engineering services. |
|||
Flexural Strength | 100 - 130 MPa | 14500 - 18900 psi | Compression; ISO 178 |
Raschig Group DECAL® 666/8 Phenolic Glass-fiber reinforced phenolic molding compound with mineral fillers. High heat resistance, reduced mould shrinkage and post-shrinkage, good chemical resistance and mechanical properties. This prod.. |
|||
Flexural Strength | 100 - 130 MPa | 14500 - 18900 psi | Injection; ISO 178 |
Raschig Group MELOPAS® 2010 MF Melamine Organically and inorganically filled Melamine molding compound. Excellent surface hardness, good mechanical strength, good electrical properties. This product meets the allowed upper limits for heav.. |
|||
Flexural Strength | 90.0 - 130 MPa | 13100 - 18900 psi | Injection; ISO 178 |
Raschig Group MELOPLAS® 152 MF Cellulose-reinforced MF molding compound in white and colored shades. Very good electrical properties, high surface hardness, good abrasion- and UV-stability, very good resistance to chemicals - al.. |
|||
Flexural Strength | 100 - 130 MPa | 14500 - 18900 psi | Injection; ISO 178 |
Raschig Group MELOPLAS® 152.7 MF Cellulose-reinforced MF molding compound in white and colored shades. High surface hardness, very good UV stability, very good resistance to chemicals also to foodstuff ingredients, physiologically.. |
|||
Flexural Strength | 100 - 130 MPa | 14500 - 18900 psi | Injection; ISO 178 |
Raschig Group MELOPLAS® 181 MF Cellulose-reinforced, phenol-modified MF molding compound (MPF) in white and colored shades. High surface hardness, good electrical properties, good mechanical strength, high UV and heat resistanc.. |
|||
Flexural Strength | 100 - 130 MPa | 14500 - 18900 psi | Injection; ISO 178 |
Raschig Group MELOPLAS® 181.5 MF Cellulose-reinforced, phenol-modified MF molding compound (MPF) in white and colored shades. Very good electrical properties, high surface hardness, good mechanical strength, high UV and heat resis.. |
|||
Flexural Strength | 100 - 130 MPa | 14500 - 18900 psi | Compression; ISO 178 |
Raschig Group MELOPLAS® 2500 MF Cellulose-reinforced MF molding compound in white and colored shades. Very good electrical properties, high surface hardness, good abrasion- and UV-stability, very good resistance to chemicals - al.. |
|||
Flexural Strength | 110 - 130 MPa | 16000 - 18900 psi | Injection; ISO 178 |
Raschig Group MELOPLAS® 3025 MF Cellulose-reinforced and inorganically filled MF molding compound in white and colored shades. High surface hardness, good UV and heat stability, very good resistance to chemicals - also to foodstu.. |
|||
Flexural Strength | 110 - 130 MPa | 16000 - 18900 psi | Injection; ISO 178 |
Raschig Group RALUPOL® 4806 UP Glass-fiber reinforced polyester molding compound. Very low mold shrinkage and post-shrinkage, very good mechanical strength, very good electrical values, better performance values compared to UP 80.. |
|||
Flexural Strength | 85.0 - 130 MPa | 12300 - 18900 psi | Compression; ISO 178 |
Raschig Group RALUPOL® 5000 UP Polyester Glass-fiber reinforced polyester molding compound. Low mold shrinkage and post-shrinkage, very good electrical values, excellent heat resistance, good mechanical strength. This product meets the all.. |
|||
Flexural Strength | 100 - 130 MPa | 14500 - 18900 psi | DIN 54352 |
Schwartz Technical Plastics LAMINEX® 2010 Cotton Fabric, Phenolic Resin Impregnated, Fine Application: slippers, inserts for coupling boxes, rollneck bearingsInformation provided by Schwartz Technical Plastics GmbH |
|||
Flexural Strength | 110 - 130 MPa | 16000 - 18900 psi | At Rupture; ISO 178 |
Vyncolit 4221 XB Novolac Phenolic Mineral and organic filled phenolic molding compound with good mechanical properties.Information provided by Vyncolit, a Sumitomo Bak Group |
|||
Flexural Strength | 120 - 130 MPa | 17400 - 18900 psi | At Rupture; ISO 178 |
Vyncolit 4451 XB Novolac Phenolic Organic and mineral filled phenolic molding compound with excellent mechanical properties (highest notched impact strength).USES: Fuse holders, brush holders, circuit breakers, automotive ignition a.. |
|||
Flexural Strength | 100 - 130 MPa | 14500 - 18900 psi | Injection; ISO 178 |
Raschig Group MELOPLAS® 180 MF Wood flour-reinforced, phenol-modified MF molding compound (MPF) in dark colors. High surface hardness, good mechanical strength and electrical properties, good heat resistance. Self-extinguishing .. |
|||
Flexural Strength | 110 - 130 MPa | 16000 - 18900 psi | Injection; ISO 178 |
Raschig Group 5557 DAP
(discontinued **) Glass fiber-reinforced and inorganically filled diallylphthalate molding compound (DAP) in various colors. Good mechanical strength together with retention of high electrical properties under hot h.. |
|||
Flexural Strength | 100 - 130 MPa | 14500 - 18900 psi | ISO 178 |
Bulk Molding Compounds tetra-DUR N 4203 Bulk Molding Compound Highest dimensional stability under temp. Low profile.Typical Applications - Requiring mechanical strength, abrasion resistance, dimensional stability, electrical insulation, electrostatic dissipat.. |