Raschig Group 5557 DAP  (discontinued **)

Category Polymer , Thermoset , Diallyl Phthalate (DAP) , Diallyl Phthalate (DAP) Molding Compound, Short Glass Fiber Filled , Filled/Reinforced Thermoset
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Raschig Group 5557 DAP  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Glass fiber-reinforced and inorganically filled diallylphthalate molding compound (DAP) in various colors. Good mechanical strength together with retention of high electrical properties under hot humid conditions, long term retention of dimensional stability also under severe environmental conditions. Self-extinguishing (V-0/0,6 according to UL 94). Free of toxic heavy metals. Forms: Low dust granulate packed in moisture resistant cartons. Standard carton size: 20 kg palletized in 600 kg loads. Processing: Injection and transfer. Applications:ConnectorsBobbinsPotentiometersSwitchesInformation provided by the Raschig Group
Physical Properties Metric English Comments
Specific Gravity 1.80 - 2.00 g/cc
1.80 - 2.00 g/cc
ISO 1183
Apparent Bulk Density 0.750 - 0.900 g/cc
0.0271 - 0.0325 lb/in³
ISO 60
Linear Mold Shrinkage 0.0020 - 0.0045 cm/cm
0.0020 - 0.0045 in/in
Injection; ISO 2577
Mechanical Properties Metric English Comments
Flexural Strength 110 - 130 MPa
16000 - 18900 psi
Injection; ISO 178
Flexural Modulus 16.0 - 18.0 GPa
2320 - 2610 ksi
Injection; ISO 178
Compressive Strength 150 - 200 MPa
21800 - 29000 psi
ISO 604
Charpy Impact Unnotched 0.650 - 0.800 J/cm²

@Temperature 23.0 °C
3.09 - 3.81 ft-lb/in²

@Temperature 73.4 °F
Injection; ISO 179/ 1eU
Thermal Properties Metric English Comments
CTE, linear 45.0 - 55.0 µm/m-°C

@Temperature 20.0 - 70.0 °C
25.0 - 30.6 µin/in-°F

@Temperature 68.0 - 158 °F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) >= 200 °C
>= 392 °F
Injection; ISO 75-A
Flammability, UL94 V-0

@Thickness 1.00 mm
V-0

@Thickness 0.0394 in
Shrinkage 0.00 - 0.050 %
0.00 - 0.050 %
Post-shrinkage; ISO 2577
Electrical Properties Metric English Comments
Surface Resistance 1.00e+14 - 1.00e+15 ohm
1.00e+14 - 1.00e+15 ohm
IEC 60093
Dielectric Constant 4.5 - 5.5

@Frequency 100 Hz
4.5 - 5.5

@Frequency 100 Hz
IEC 60250
Dielectric Strength 15.0 - 20.0 kV/mm

@Thickness 1.00 mm
381 - 508 kV/in

@Thickness 0.0394 in
IEC 60243-1
Dissipation Factor 0.0050 - 0.010

@Frequency 100 Hz
0.0050 - 0.010

@Frequency 100 Hz
IEC 60250
Comparative Tracking Index >= 600 V
>= 600 V
CTI-M; IEC 60112
>= 600 V
>= 600 V
CTI; IEC 60112
Processing Properties Metric English Comments
Front Barrel Temperature 60.0 - 70.0 °C
140 - 158 °F
Melt Temperature 100 - 115 °C
212 - 239 °F
Mold Temperature 170 - 190 °C
338 - 374 °F
Descriptive Properties Value Comments
Water Absorption, max [mg] 15
ISO 62; 24h / 23°C