Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | <= 84.0 MPa | <= 12200 psi | ISO 178 |
Polykemi AB POLYabs N20 ABS Information provided by Polykemi AB |
|||
Flexural Strength | 84.0 MPa | 12200 psi | ASTM D790 |
PolyOne Geon™ Vinyl Dry Blend E7009 Polyvinyl Chloride, Rigid (PVC, Rigid) Recommended for whites and light pastel colors only. Not to be used for darker colors.Physical properties based on Geon E7009 white 1024 lot# UTCX 57572Information provided by PolyOne |
|||
Flexural Strength | 84.0 MPa | 12200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP BX03658N SAN LNP* LUBRICOMP* BX03658N is a compound based on SAN resin containing proprietary fillers. Added features of this grade include: Wear Resistant, Tight Dimensional Tolerances, good for Water Meter A.. |
|||
Flexural Strength | 84.0 MPa | 12200 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP DAL22 PC (Asia Pacific) LNP* Lubricomp* DAL22 is a compound based on Polycarbonate resin containing PTFE, Aramid Fiber. Added features of this material include: Internally Lubricated. |
|||
Flexural Strength | 84.0 MPa | 12200 psi | ASTM D790 |
Kotec Carbotex K-30F5 Polycarbonate, Wear Resistant Features: Wear resistance, TranslucentApplications: OA equipment, Communications, Precision parts, Machineries, E & E partsInformation provided by Kotec Corporation |
|||
Flexural Strength | 84.0 MPa | 12200 psi | ASTM D790 |
Kotec Carbotex K-30FR Polycarbonate, Flame Retardant Features: Non-brominated & non-chlorined flame retardant, Medium viscosity, TransparentApplications: OA equipment, Communications, Precision parts, Machineries, E & E parts, Safety products, Househo.. |
|||
Flexural Strength | 84.0 MPa | 12200 psi | ASTM D790 |
Kotec Carbotex KFR-30T12 Polycarbonate, Flame Retardant Features: Non-brominated & non-chlorined flame retardant, Medium viscosity, TransparentApplications: OA equipment, Communications, Precision parts, Machineries, E & E parts, Safety products, Househo.. |
|||
Flexural Strength | 84.0 MPa | 12200 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP DL003EU PC LNP LUBRICOMP* DL003EU is a compound based on Polycarbonate resin containing 15% PTFE. Added features of this material include: Easy Molding, UV Stabilized, Internally Lubricated. |
|||
Flexural Strength | 84.0 MPa | 12200 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP IBI16 PA 6/12 LNP LUBRICOMP* IBI16 is a compound based on Nylon 6/12 resin containing 30% Glass Bead, 2% Silicone. Added features of this material include: Wear Resistant. |
|||
Flexural Strength | 84.0 MPa | 12200 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP RL004S PA 66 LNP LUBRICOMP* RL004S is a compound based on Nylon 66 resin containing 20% PTFE. Added features of this material include: Heat Stabilized, Wear Resistant. |
|||
Flexural Strength | 84.0 MPa | 12200 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRILOY K2000 Acetal LNP LUBRILOY* K2000 is a compound based on Acetal resin containing Proprietary Lubricant. Added feature of this material is: Wear Resistant. |
|||
Flexural Strength | 84.0 MPa | 12200 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRILOY K2000 Acetal (Asia Pacific) LNP LUBRILOY* K2000 is a compound based on Acetal resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated. |
|||
Flexural Strength | 84.0 MPa | 12200 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRILOY K2000XXH Acetal LNP LUBRILOY* K2000XXH is a compound based on Acetal resin containing Proprietary Lubricant. Added features of this material are: Wear Resistant, Healthcare. |
|||
Flexural Strength | 84.0 MPa | 12200 psi | ASTM D 790 |
SABIC Innovative Plastics LNP Stat-kon DX07323 PC+ABS LNP* STAT-KON* DX07323 is a compound based on polycarbonate resin containing conductive fillers. Added features of this compound includes: ESD safe and excellent low-temperature impact performance, .. |
|||
Flexural Strength | 84.0 MPa | 12200 psi | ASTM D790 |
SABIC Innovative Plastics LNP STAT-KON DX07323 PC+ABS (Asia Pacific) LNP* STAT-KON* DX07323 is a compound based on polycarbonate resin containing conductive fillers. Added features of this compound includes: ESD safe and excellent low-temperature impact performance, .. |
|||
Flexural Strength | 84.0 MPa | 12200 psi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP KB003RXZ Acetal Copolymer LNP THERMOCOMP* KB003RXZ is a compound based on Acetal Copolymer resin containing 15% Glass Bead. Added features of this material include: Easy Release. |
|||
Flexural Strength | 84.0 MPa | 12200 psi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP WH0200B PBT LNP* Thermocomp* WH0200B is a compound based on PBT resin containing proprietary fillers. Added features include: High Specific Gravity. |
|||
Flexural Strength | 84.0 MPa | 12200 psi | ASTM D790 |
SABIC Innovative Plastics LNP STAT-LOY N30009 PC+ABS (Asia Pacific) LNP* Stat-loy* N30009 is a compound based on PC+ABS Blend resin containing Flame Retardant, Anti-Static. Added features of this material include: Antistat, Flame Retardant. |
|||
Flexural Strength | 84.0 MPa | 12200 psi | ASTM D790 |
SABIC Innovative Plastics LNP STAT-LOY NX03583 PC+ABS LNP STAT-LOY* NX03583 is a compound based on PC+ABS Blend resin. Added features of this material include: Antistat, Flame Retardant. |
|||
Flexural Strength | 84.0 MPa | 12200 psi | ASTM D790 |
SABIC Innovative Plastics LNP STAT-LOY NX03583 PC+ABS (Asia Pacific) LNP STAT-LOY* NX03583 is a compound based on PC+ABS Blend resin containing Anti-Static, Flame Retardant. Added features of this material include: Antistat. |
|||
Flexural Strength | 84.0 MPa | 12200 psi | ASTM D790 |
SABIC Innovative Plastics NORYL GTX GTX6009 PPE+PS+PA6 (Asia Pacific) PA6 based unfilled GTX for Wheel cover |
|||
Flexural Strength | 84.0 MPa | 12200 psi | ASTM D790 |
Unitika P-3001S Engineering Plastic P series resins are resins succeeding the characteristics of the neat polymer, U100, and improved in flowability and optical properties. Among many super engineering plastics, the resins are few tra.. |
|||
Flexural Strength | 84.0 MPa | 12200 psi | ISO 178 |
Polyplastics Duranex® 6370B Polybutylene Terephthalate (PBT), Anisotropy improvement, 30% GB filled DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers .. |
|||
Flexural Strength | 84.0 MPa | 12200 psi | ASTM D790 |
Unitika U-100 Engineering Plastic CAS No: 26590-50-1Information provided by Unitika Ltd. |
|||
Flexural Strength | 84.0 MPa | 12200 psi | ISO 178 |
Polyplastics Duranex® 601SA Polybutylene Terephthalate (PBT), Low density, Low wear, Mineral filled DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers .. |
|||
Flexural Strength | 84.0 MPa | 12200 psi | ASTM D790 |
Ashley Polymers Ashlene® 735LD Nylon 6 An impact modified, plasticized copolymer with improved impact resistance for injection molding.Data provided by the manufacturer |
|||
Flexural Strength | 84.0 MPa | 12200 psi | ASTM D790 |
Resinoid 1312 Phenolic Molding, Glass Reinforced Data provided by the manufacturer.The Resinoid 1300 and 7000 glass fiber reinforced series compounds feature mechanical strength, dimensional stability, electrical insulation, and heat resistance |
|||
Flexural Strength | 84.0 MPa | 12200 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP DL003E PC LNP LUBRICOMP* DL003E is a compound based on Polycarbonate resin containing 15% PTFE. Added features of this material include: Easy Molding, Internally Lubricated |
|||
Flexural Strength | 84.0 MPa | 12200 psi | 2 mm/min; ISO 178 |
Sax Polymers SAXALEN PPC344G25 Polypropylene Copolymer, 25% Glass Filled SAXALEN PPC344G25 is a 25% glass filled Polypropylene - Copolymer intended for injection molding.Information provided by SAX Polymers |