PolyOne Geon™ Vinyl Dry Blend E7009 Polyvinyl Chloride, Rigid (PVC, Rigid)

Category Polymer , Thermoplastic , Vinyl (PVC) , PVC, Rigid Grade
Manufacturer PolyOne Corporation
Trade Name Geon™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Geon™ Vinyl Dry Blend E7009 Polyvinyl Chloride, Rigid (PVC, Rigid).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Recommended for whites and light pastel colors only. Not to be used for darker colors.Physical properties based on Geon E7009 white 1024 lot# UTCX 57572Information provided by PolyOne
Physical Properties Metric English Comments
Specific Gravity 1.51 g/cc
1.51 g/cc
ASTM D792
Mechanical Properties Metric English Comments
Hardness, Shore D 80
80
ASTM D2240
Tensile Strength, Yield 47.0 MPa
6820 psi
Type I, 5.1 mm/min; ASTM D638
Tensile Modulus 3.07 GPa
445 ksi
Type I, 5.1 mm/min; ASTM D638
Flexural Strength 84.0 MPa
12200 psi
ASTM D790
Flexural Modulus 3.32 GPa
482 ksi
ASTM D790
Izod Impact, Notched 0.640 J/cm

@Thickness 3.18 mm,
Temperature 23.0 °C
1.20 ft-lb/in

@Thickness 0.125 in,
Temperature 73.4 °F
Compression Molded; ASTM D256A
Dart Drop Total Energy 74.7 J/cm

@Temperature 23.0 °C
0.140 ft-lb/mil

@Temperature 73.4 °F
Procedure A, C.125; ASTM D4226
141 J/cm

@Temperature 23.0 °C
0.264 ft-lb/mil

@Temperature 73.4 °F
Procedure B, C.125; ASTM D4226
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 59.0 µm/m-°C
32.8 µin/in-°F
ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 78.3 °C

@Treatment Temp. 50.0 °C,
Thickness 3.18 mm
173 °F

@Treatment Temp. 122 °F,
Thickness 0.125 in
Annealed; ASTM D648
79.4 °C

@Treatment Temp. 60.0 °C,
Thickness 3.18 mm
175 °F

@Treatment Temp. 140 °F,
Thickness 0.125 in
Annealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 73.9 °C

@Thickness 3.18 mm
165 °F

@Thickness 0.125 in
Compression Molded, Annealed at 50 deg.C; ASTM D648
78.3 °C

@Thickness 3.18 mm
173 °F

@Thickness 0.125 in
Compression Molded, Annealed at 60 deg.C; ASTM D648
Processing Properties Metric English Comments
Melt Temperature 193 - 210 °C
379 - 410 °F
Descriptive Properties Value Comments
Features Good Weather Resistance
Medium Impact Resistance
Forms Powder
Generic Material PVC, Rigid
Generic Name Polyvinyl Chloride, Rigid (PVC, Rigid)
Processing Method Extrusion
PVC Cell Classification 1-22434-42-0000
ASTM D4216
12364
ASTM D1784
Regional Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
Uses Profiles