SABIC Innovative Plastics LNP LUBRILOY K2000XXH Acetal

Category	Polymer , Thermoplastic , Acetal (POM)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP Lubriloy
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP LUBRILOY K2000XXH Acetal.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP LUBRILOY* K2000XXH is a compound based on Acetal resin containing Proprietary Lubricant. Added features of this material are: Wear Resistant, Healthcare.

Physical Properties	Metric	English	Comments
Density	1.40 g/cc	0.0506 lb/inÂ³	ASTM D792
	1.40 g/cc	0.0506 lb/inÂ³	ISO 1183
Moisture Absorption	0.330 %	0.330 %	50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow	0.022 cm/cm @Time 86400 sec	0.022 in/in @Time 24.0 hour	ASTM D955
	0.0221 cm/cm @Time 86400 sec	0.0221 in/in @Time 24.0 hour	ISO 294
Linear Mold Shrinkage, Transverse	0.0214 cm/cm @Time 86400 sec	0.0214 in/in @Time 24.0 hour	ISO 294
	0.023 cm/cm @Time 86400 sec	0.023 in/in @Time 24.0 hour	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	51.0 MPa	7400 psi	ASTM D638
	59.0 MPa	8560 psi	ISO 527
Tensile Strength, Yield	55.0 MPa	7980 psi	ASTM D638
	60.0 MPa	8700 psi	ISO 527
Elongation at Break	13.3 %	13.3 %	ISO 527
	32.4 %	32.4 %	ASTM D638
Elongation at Yield	9.0 %	9.0 %	ISO 527
	9.3 %	9.3 %	ASTM D638
Tensile Modulus	2.06 GPa	299 ksi	50 mm/min; ASTM D638
	2.56 GPa	371 ksi	1 mm/min; ISO 527
Flexural Strength	65.0 MPa	9430 psi	ISO 178
	84.0 MPa	12200 psi	ASTM D790
Flexural Modulus	2.42 GPa	351 ksi	ASTM D790
	2.42 GPa	351 ksi	ISO 178
Izod Impact, Notched	0.690 J/cm	1.29 ft-lb/in	ASTM D256
Izod Impact, Unnotched	13.56 J/cm	25.40 ft-lb/in	ASTM D4812
Izod Impact, Notched (ISO)	6.00 kJ/mÂ²	2.86 ft-lb/inÂ²	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	48.0 kJ/mÂ²	22.8 ft-lb/inÂ²	80104; ISO 180/1U
Dart Drop, Total Energy	6.00 J	4.43 ft-lb	Instrumented Impact Energy @ peak; ASTM D3763
Coefficient of Friction, Dynamic	0.38	0.38	ASTM D3702 Modified
Coefficient of Friction, Static	0.24	0.24	ASTM D3702 Modified
K (wear) Factor	20.1 x 10^-8 mmÂ³/N-M	10.0 x 10^-10 inÂ³-min/ft-lb-hr	Washer; ASTM D3702 Modified

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	115 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	63.9 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ASTM E 831
	115 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	63.9 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ISO 11359-2
CTE, linear, Transverse to Flow	111 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	61.7 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ASTM E 831
	111 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	61.7 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi)	158 Â°C @Thickness 3.20 mm	316 Â°F @Thickness 0.126 in	unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	87.0 Â°C	189 Â°F	Flatw 80104 sp=64mm; ISO 75/Af
	110 Â°C @Thickness 3.20 mm	230 Â°F @Thickness 0.126 in	unannealed; ASTM D648