Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 61.0 MPa | 8850 psi | ASTM D790-92 |
Multibase Multi-Pro® 2005 XRC Black 20% Filler Content Polypropylene Multi-Pro 2005 XRC is specifically designed for injection molded electronic industrial uses. This product shows higher heat distortion and notched izod than typical glass filled polypropylene. Thi.. |
|||
Flexural Strength | 61.0 MPa | 8850 psi | Method 1, 0.05"/min; ASTM D790 |
Proto3000 ABS-M30 Fused Deposition Modeling Polymer Description: ABS-M30 is up to 25-70 percent stronger than standard Stratasys ABS and is an ideal material for conceptual modeling, functional prototyping, manufacturing tools, and end-use-parts. ABS.. |
|||
Flexural Strength | 61.0 MPa | 8850 psi | Method 1, 0.05"/min; ASTM D790 |
Proto3000 ABS-M30i Fused Deposition Modeling Polymer Description: ABS-M30i is a high strength material well suited for the medical, pharmaceutical and food packaging industries. Parts manufactured with ABS-M30i material are biocompatible (ISO 10993 ce.. |
|||
Flexural Strength | 61.0 MPa | 8850 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP AL003 ABS LNP LUBRICOMP* AL003 is a compound based on Acrylonitrile Butadiene Styrene resin containing 15% PTFE. Added features of this material include: Internally Lubricated. |
|||
Flexural Strength | 61.0 MPa | 8850 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP AL003 ABS (Asia Pacific) LNP LUBRICOMP* AL003 is a compound based on Acrylonitrile Butadiene Styrene resin containing PTFE. Added features of this material include: Internally Lubricated. |
|||
Flexural Strength | 61.0 MPa | 8850 psi | ASTM D790 |
LG Chemical LUCEL HI-515 High Impact POM, Unreinforced LUCEL semi-crystalline acetal copolymer resins are produced by gas phase polymerization. LUCEL resins can be widely accepted as the replacement of thermosets, aluminum and zinc die-casts or other m.. |
|||
Flexural Strength | 61.0 MPa | 8850 psi | ISO 178 |
Lucite International Diakon® Rapide CLG 910B Enhanced Molding Acrylic Polymer Specially designed to reduce injection molding cycle times and therefore provide production cost benefits.Information provided by Lucite International |
|||
Flexural Strength | 61.0 MPa | 8850 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP HH0420A PA11 LNP* HH0420A is a compound based on Nylon 11 containing proprietary fillers. Added features of this material are High Specific Gravity. |
|||
Flexural Strength | 61.0 MPa | 8850 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP KAL22 Acetal Copolymer (Europe-Africa-Middle East) LNP* Lubricomp* KAL22 is a compound based on Acetal Copolymer resin containing PTFE, Aramid Fiber. |
|||
Flexural Strength | 61.0 MPa | 8850 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP KP002 Acetal Copoly LNP* LUBRICOMP* KP002 is a compound based on Acetal Copolymer resin containing 10% PTFE/Silicone. Added feature of this material is: Wear Resistant. |
|||
Flexural Strength | 61.0 MPa | 8850 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP KP002 Acetal Copoly (Asia Pacific) LNP* Lubricomp* KP002 is a compound based on Acetal Copolymer resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated. |
|||
Flexural Strength | 61.0 MPa | 8850 psi | ISO 178 |
Solvay TECHNYL® A 50H1 PA66, Conditioned Description: Flame retardant polyamide 66, unreinforced, heat stabilized, for injection molding.Available in: Asia Pacific, Europe, Latin America and North AmericaProduct Applications: This phospho.. |
|||
Flexural Strength | 61.0 MPa | 8850 psi | ISO 178 |
SABIC Innovative Plastics LNP STAT-KON RX08408 PA 66 LNP* STAT-KON* RX08404 is a compound based on Nylon 66 containing Carbon Powder. Added features of this material include: Electrically Conductive, High Impact. |
|||
Flexural Strength | 61.0 MPa | 8850 psi | ISO 178 |
SABIC Innovative Plastics LNP Stat-kon RX08408_NA1D004 PA 66 LNP* Stat-Kon* RX08404_NA1D004 is a compound based on Nylon 66 containing Carbon Powder. Characteristics of this grade include: Electrically Conductive, High Impact.This data was supplied by SABI.. |
|||
Flexural Strength | 61.0 MPa | 8850 psi | ISO 178 |
SABIC Innovative Plastics LNP STAT-LOY AF3009 ABS LNP* STAT-LOY* AF3009 is a compound based on ABS resin containing 10% Glass Fiber. Added features of this material include: Antistatic, Flame Retardant. |
|||
Flexural Strength | 61.0 MPa | 8850 psi | ISO 178 |
SABIC Innovative Plastics LNP STAT-LOY AF3009 ABS (Asia Pacific) LNP* Stat-loy* AF3009 is a compound based on Acrylonitrile Butadiene Styrene resin containing Glass Fiber, Flame Retardant. Added features of this material include: Antistat, Flame Retardant. |
|||
Flexural Strength | 61.0 MPa | 8850 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
SABIC Innovative Plastics LNP Thermocomp FF008L PE LNP* Thermocomp* FF008L is a compounding based on Polyethylene containing glass fiber. Added characteristics include Low Extractible.This data was supplied by SABIC-IP for the Americas region. |
|||
Flexural Strength | 61.0 MPa | 8850 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP HH0420A PA11 LNP* THERMOCOMP* HH0420A is a compound based on Nylon 11 containing proprietary fillers. Added features of this material are High Specific Gravity. |
|||
Flexural Strength | 61.0 MPa | 8850 psi | 3-point, 2 mm/min; ISO 178 |
Styron MAGNUM™ 3325 SLG Acrylonitrile Butadiene Styrene (ABS) Resin Overview: Super Low Gloss, Medium Heat, Medium Impact ABS resin for injection molded automotive interior trim applications Magnum 3325 SLG can achieve 60° Gardner gloss levels below 2.0 with low .. |
|||
Flexural Strength | 61.0 MPa | 8850 psi | ISO 178 |
SABIC Innovative Plastics LNP STAT-LOY W3000XXJ PBT LNP* STAT-LOY* W3000XXJ is a compound based on PBT. Added features of this grade include: Anti-Stat, Colorable, Healthcare |
|||
Flexural Strength | 61.0 MPa | 8850 psi | ASTM D790 |
Stratasys® ABSi Stratasys is the only company that gives engineers the ability to manufacture real ABSi industrial thermoplastic parts direct from digital files. ABSi parts can be used from conceptual prototyping t.. |
|||
Flexural Strength | 61.0 MPa | 8850 psi | ASTM D790 |
UBE UBESTA® 3035LU1 Rigid Piping Grade Nylon 12 Description: UBESTA contributes to the field of Utilities such as plastic pipe system evolutionary developed for gas industry. It is used for both burial and for rehabilitation of existing cast iron.. |
|||
Flexural Strength | 61.0 MPa | 8850 psi | 2 mm/min; ISO 178 |
Chi Mei Polylac® PA-747R ABS - Extrusion Attach case and refrigerator |
|||
Flexural Strength | 61.0 MPa @Temperature 23.0 °C |
8850 psi @Temperature 73.4 °F |
EN ISO 178 |
Ensinger TECASINT™ 2062 Polyimide, Anthrazit Gleamy, 15% Graphite, 10% PTFE (PI) TECASINT™ 2000 series of polyimide stock shapes provide a superior combination of high temperature and bearing and wear, properties that make it an ideal choice for the most demanding applications... |
|||
Flexural Strength | 61.0 MPa | 8850 psi | ASTM D790 |
Diamond Polymers NYLON 6615 Black, Super Tough Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc. |
|||
Flexural Strength | 61.0 MPa | 8850 psi | 2 mm/min; ISO 178 |
Chi Mei Polylac® PA-756S ABS - High Flow Super high flow, medium impact |
|||
Flexural Strength | 61.0 MPa | 8850 psi | ISO 178 |
Azoty Tarnow™ TARNOFORM 300 UV POM Injection molding grade based on Tarnoform 300 modified with carbon black giving best weathering stability.Information provided by Zakłady Azotowe w Tarnowie-Moscicach S.A. |
|||
Flexural Strength | 61.0 MPa | 8850 psi | ISO 178 |
Azoty Tarnow™ TARNOFORM 500 UV POM High flow injection molding grade based on Tarnoform 500 modified with carbon black giving best weathering stability.Information provided by Zakłady Azotowe w Tarnowie-Moscicach S.A. |
|||
Flexural Strength | 61.0 MPa | 8850 psi | ASTM D790 |
A. Schulman ComAlloy Comtuf® 420 Polyester - PBT, High Impact Modified Data provided by the manufacturer, ComAlloy International Company. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been integrated into the A Sc.. |
|||
Flexural Strength | 61.0 MPa | 8850 psi | ASTM D790 |
Plenco 7321 Phenolic, Nodular, Injection Molded PLENCO 07321 is an organic fiber reinforced phenolic molding compound, offering improved mechanical strength and excellent dimensional stability. Type ASTM 5948 CFI-5, and UL recognized under compon.. |