Stratasys® ABS-M30
| Category | Polymer , Rapid Prototyping Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | Stratasys |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Stratasys® ABS-M30.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
ABS-M30 is 25-70 percent stronger than standard Stratasys ABS and is an ideal material for conceptual prototyping, design verification, and direct digital manufacturing. ABS-M30 has greater tensile, impact, and flexural strength than standard ABS. Layer bonding is significantly stronger than that of standard ABS, for a more durable part. This results in more realistic functional tests and higher quality parts for end use. When combined with a Stratasys FDM mc™ series system, ABS-M30 gives you Real Parts™ that are stronger, smoother, and with better feature detail.Information provided by Stratasys®
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 109.5 | 109.5 | ASTM D785 |
| Tensile Strength, Ultimate | 36.0 MPa | 5220 psi | Type 1, 2"/min; ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| 52 % | 52 % | Flexural; ASTM D790 | |
| Tensile Modulus | 2.413 GPa | 350.0 ksi | ASTM D638 |
| Flexural Strength | 61.0 MPa | 8850 psi | Method 1, .05"/min; ASTM D790 |
| Flexural Modulus | 2.317 GPa | 336.1 ksi | ASTM D790 |
| Izod Impact, Notched | 1.39 J/cm @Temperature 23.0 °C |
2.60 ft-lb/in @Temperature 73.4 °F |
Method A; ASTM D256 |
| Izod Impact, Unnotched | 2.83 J/cm @Temperature 23.0 °C |
5.30 ft-lb/in @Temperature 73.4 °F |
Method A; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 88.2 µm/m-°C @Temperature 20.0 °C |
49.0 µin/in-°F @Temperature 68.0 °F |
ASTM E831 |
| CTE, linear, Transverse to Flow | 84.6 µm/m-°C @Temperature 20.0 °C |
47.0 µin/in-°F @Temperature 68.0 °F |
ASTM E831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 96.0 °C @Thickness 3.17 mm |
205 °F @Thickness 0.125 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 82.0 °C @Thickness 3.17 mm |
180 °F @Thickness 0.125 in |
unannealed; ASTM D648 |
| Vicat Softening Point | 99.0 °C | 210 °F | Rate B/50; ASTM D1525 |
| Glass Transition Temp, Tg | 108 °C | 226 °F | DSC (SSYS) |
| Flammability, UL94 | HB @Thickness 0.850 mm |
HB @Thickness 0.0335 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 28.0 kV/mm | 711 kV/in | IEC 60112 |
Users viewing this material also viewed the following:
- Nye Lubricants 380L (RL) Synthetic Oil
- PSM Industries PM Krupp M4 Powder Metallurgy Steel Alloy
- LG Chemical Acrylic Acid
- Haynes Hastelloy® C-22® alloy, 20% cold worked sheet, aged 100 hours at 500°C
- Trelleborg B800 Commercial Nitrile Rubber
- BNZ Materials BNZ-23A Insulating Firebrick
- Arlon CuClad 250 PTFE/Woven Fiberglass Laminate Microwave Printed Circuit Board Substrate
- Ascend Performance Materials Vydyne® 88X Nylon 66/6 Copolymer
- AK Steel ZINCGRIP® GA Hot Dip Galvannealed Carbon Steel, Bake Hardenable (BH 210)
Copyright © lookpolymers.com All Rights Reserved