Lucite International Diakon® Rapide CLG 910B Enhanced Molding Acrylic Polymer
| Category | Polymer , Thermoplastic , Acrylic (PMMA) , Acrylic, General Purpose, Molded |
| Manufacturer | Lucite International |
| Trade Name | Diakon® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lucite International Diakon® Rapide CLG 910B Enhanced Molding Acrylic Polymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Specially designed to reduce injection molding cycle times and therefore provide production cost benefits.Information provided by Lucite International
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | ISO 1183 |
| Water Absorption | 0.30 % | 0.30 % | ISO 62 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | |
| Melt Flow | 6.0 g/10 min | 6.0 g/10 min | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 96 | 96 | ISO 2039-2 |
| Tensile Strength | 66.0 MPa | 9570 psi | ISO 527 |
| Elongation at Break | 3.1 % | 3.1 % | ISO 527 |
| Flexural Strength | 61.0 MPa | 8850 psi | ISO 178 |
| Flexural Modulus | 3.10 GPa | 450 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 19.0 kJ/m² | 9.04 ft-lb/in² | ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 71.0 µm/m-°C | 39.4 µin/in-°F | ASTM E831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 219 °F | ISO 75B |
| Deflection Temperature at 1.8 MPa (264 psi) | 101 °C | 214 °F | ISO 75A |
| Vicat Softening Point | 105 °C | 221 °F | ISO 306B |
| 112 °C | 234 °F | ISO 306A | |
| Flammability, UL94 | HB | HB | |
| Glow Wire Test | 650 °C | 1200 °F | IEC 695-2-1 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.49 | 1.49 | ISO 489 |
| Haze | 0.50 % | 0.50 % | ASTM D1003 |
| Transmission, Visible | 92 % | 92 % | ASTM D1003 |
Users viewing this material also viewed the following:
- LNP ULTEM® JD7107 Polyetherimide (discontinued **)
- Fiberfil® J-60/20/E4 Polypropylene Homopolymer, 20% Glass Reinforced, Chemically coupled
- SABIC Innovative Plastics Valox® 357 PBT (Asia Pacific)
- Techmer ES HiFill® PA6 GF33 L UV BK 33% Glass Filled
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 0.50 PHR Zinc Stearate
- Covestro Makrolon® ET3127 Polycarbonate
- Cosmic Plastics 6120F Short Glass Fiber Filled Ortho Diallyl Phthalate Molding Compound
Copyright © lookpolymers.com All Rights Reserved