Polymer Property : Flexural Strength = 47.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	47.0 MPa	6820 psi
Plastcom SLOVALEN PH 92 T 40 PP, 40% mineral filling FeaturesModified homopolymer PP for injection moulding with the content of 40% microground, floated, chemically modified talc. Stable towards oxidants. General application in all industry branches -..
Flexural Strength	<= 47.0 MPa	<= 6820 psi	ISO 178
Polykemi AB POLYfill PPC TS16020 LE Polypropylene Copolymer, Mineral Reinforced, Low Emission Information provided by Polykemi AB
Flexural Strength	<= 47.0 MPa	<= 6820 psi	ISO 178
Polykemi AB POLYfill PPH TS15020 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB
Flexural Strength	<= 47.0 MPa	<= 6820 psi	ISO 178
Polykemi AB POLYfill PPHC T15020 Polypropylene, Mineral Reinforced Information provided by Polykemi AB
Flexural Strength	47.0 MPa	6820 psi
Quadrant EPP Symalit® 1000 ECTFE, unfilled, lining industries (ISO Data) Symalit 1000 ECTFE is made from a fluoropolymer resin that is a copolymer of ethylene and chlorotrifluoroethylene. It exhibits good mechanical properties combined with an excellent chemical resistan..
Flexural Strength	47.0 MPa @Temperature 23.0 °C	6820 psi @Temperature 73.4 °F	2.5 mm/min; ASTM D790
Solvay Specialty Polymers Halar® 300LC Polyethylene, Chlorotrifluoroethylene (ECTFE) (discontinued **) Information provided by Solvay Specialty Polymers.
Flexural Strength	47.0 MPa @Temperature 23.0 °C	6820 psi @Temperature 73.4 °F	2.5 mm/min; ASTM D790
Solvay Specialty Polymers Halar® 513LC Polyethylene, Chlorotrifluoroethylene (ECTFE) (Unverified Data**)& Information provided by Solvay Specialty Polymers.
Flexural Strength	47.0 MPa	6820 psi	ASTM D790
LG Chemical LUCEL HI-525 High Impact POM, Unreinforced LUCEL semi-crystalline acetal copolymer resins are produced by gas phase polymerization. LUCEL resins can be widely accepted as the replacement of thermosets, aluminum and zinc die-casts or other m..
Flexural Strength	47.0 MPa	6820 psi	ASTM D790
LG Chemical LUPOL HF-3208H High Flow Polypropylene, 20% Mineral Fillers, General Purpose LUPOL resins, based on polyolefin with a wide range of characteristics, are a family of low cost engineering plastics.Applications: Automotive: Bumper cover, instrument panel, glove box, air cleaner..
Flexural Strength	47.0 MPa	6820 psi	ISO 178
Solvay TECHNYLÂ® A 238 Black 21 N PA66, Conditioned Description: Unreinforced and modified polyamide 66, with improved impact resistance, heat stabilized, for injection molding.Available in: EuropeProduct Applications: TECHNYL A 238 offers excellent ..
Flexural Strength	47.0 MPa	6820 psi	2.5 mm/min; ASTM D790
Solvay Specialty Polymers HalarÂ® 1450LC Ethylene Chlorotrifluoroethylene Copolymer (ECTFE) Low ViscosityAdditional Properties: Crystallization Heat - ASTM D3418 40.0 J/g; Heat of Fusion - ASTM D3418 42.0 J/g; Thermal Stability - TGA 405 Â°CInformation provided by Solvay Specialty Polyme..
Flexural Strength	47.0 MPa	6820 psi	2.5 mm/min; ASTM D790
Solvay Specialty Polymers HalarÂ® 500LC Ethylene Chlorotrifluoroethylene Copolymer (ECTFE) Low ViscosityUses: Wire & Cable ApplicationsAdditional Properties: Crystallization Heat - ASTM D3418 40.0 J/g; Heat of Fusion - ASTM D3418 42.0 J/g; Thermal Stability - TGA 405 Â°CInformation prov..
Flexural Strength	47.0 MPa	6820 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP STAT-LOY 93000LTH Acrylic LNP* STAT-LOY* 93000LTH is a compound based on Acrylic resin. Added features of this material include: Antistatic, Transparent and Formulation Locked.
Flexural Strength	47.0 MPa	6820 psi	ISO 178
SABIC Innovative Plastics LNP STAT-LOY A30009 ABS LNP* STAT-LOY* A30009 is a compound based on ABS. Added features of this material include: Antistatic, Flame Retardant.
Flexural Strength	47.0 MPa	6820 psi	ISO 178
SABIC Innovative Plastics LNP Thermocomp FF008L PE LNP* Thermocomp* FF008L is a compounding based on Polyethylene containing glass fiber. Added characteristics include Low Extractible.This data was supplied by SABIC-IP for the Americas region.
Flexural Strength	47.0 MPa	6820 psi	ASTM Test
Styrolution LuranÂ® S 776 SE ASA Luran S 776 SE is a general purpose extrusion ASA grade with good toughness and strength, used for sheet and profile extrusions.Information provided by STYROLUTION, which is a joint venture between ..
Flexural Strength	47.0 MPa	6820 psi	2.5 mm/min; ASTM D790
Solvay Specialty Polymers HalarÂ® 902 Ethylene Chlorotrifluoroethylene Copolymer (ECTFE) High ViscosityAdditional Properties: Crystallization Heat - ASTM D3418 28.0 J/g; Heat of Fusion - ASTM D3418 28.0 J/g; Thermal Stability - TGA 405 Â°CInformation provided by Solvay Specialty Polym..
Flexural Strength	47.0 MPa	6820 psi	ASTM D790
Videolar 825 E High Impact Polystyrene (HIPS) Grade designed specially for extrusion and thermoformingCharacteristics make it especially suitable for industrial packaging deep draw thermoforming and custom multilayer sheet extrusionFeatures: St..
Flexural Strength	47.0 MPa	6820 psi	ASTM D790
Aclo Accutech Polypropylene Homopolymer HP0334T10L1 Talc Reinforced
Flexural Strength	47.0 MPa	6820 psi	ASTM D790
Aclo Accutech Polypropylene Homopolymer HP0334T40L1 Talc Reinforced
Flexural Strength	47.0 MPa	6820 psi	ASTM D790
Aclo Accutech Polypropylene Homopolymer HP0336M40CL Mica Reinforced Coupled
Flexural Strength	47.0 MPa	6820 psi	ASTM D790
Aclo Accutech Polypropylene Homopolymer HP0339T30L1 Talc Reinforced
Flexural Strength	47.0 MPa	6820 psi	ISO 178
BASF Ultramid® 1C PA6/66 (Conditioned) Description: Ultramid® 1C forms flexible, scratch-resistant coatings or tough, resilient, abrasion-resistant coverings on plastics, films, nonwovens, fabrics, leather, paper, wood, or metal.Informa..
Flexural Strength	47.0 MPa	6820 psi	ASTM D790
Aclo Accutech Polypropylene Homopolymer HP0339T40L1 Talc Reinforced
Flexural Strength	<= 47.0 MPa	<= 6820 psi	ISO 178
Polykemi AB POLYfill PP HBK1501515 Polypropylene, Multifiller High Gloss Information provided by Polykemi AB
Flexural Strength	<= 47.0 MPa	<= 6820 psi	ISO 178
Polykemi AB POLYfill PPH TS8020 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB
Flexural Strength	47.0 MPa	6820 psi	1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics LNP Thermocomp FF006 PE LNP Thermocomp FF-1006 is a glass filled Polyethylene.This data was supplied by SABIC-IP for the Americas region.