Aclo Accutech Polypropylene Homopolymer HP0339T30L1 Talc Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Talc Filler |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene Homopolymer HP0339T30L1 Talc Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | MD; ASTM D955 |
| Melt Flow | 21 g/10 min | 21 g/10 min | ASTM D1238 |
| Ash | 30 % | 30 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 83 | 83 | ASTM D785 |
| Tensile Strength at Break | 30.0 MPa | 4350 psi | ASTM D638 |
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | ASTM D638 |
| Elongation at Break | 10 % | 10 % | ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | ASTM D638 |
| Tensile Modulus | 2.20 GPa | 319 ksi | ASTM D638 |
| Flexural Strength | 47.0 MPa | 6820 psi | ASTM D790 |
| Flexural Modulus | 3.20 GPa | 464 ksi | ASTM D790 |
| Izod Impact, Notched | 0.251 J/cm | 0.470 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C | 266 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 71.1 °C | 160 °F |
Users viewing this material also viewed the following:
- Potters Industries Q-Cel® 7028 Hollow Engineered Glass Microspheres
- Premix Thermoplastics PREBLACK CP 731-40 Black Universal Masterbatch, 40% Carbon Black
- Microcell Composite Company CELLIFF® F-1020ST Polymer Foam
- Unitika elitel UE3203 Polyester, Pellet
- DSM Novamid® 1013C5 PA6
- Chosun Refractories CTC-65SH Monolithic Refractories for Ladle and Tundish
- EMS-Griltech Grilon® TN 2200 White Nylon 6 Fiber
- Ashley Polymers Ashlene® 1410B Polycarbonate, 8-10% Glass Reinforced
Copyright © lookpolymers.com All Rights Reserved