Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 207 MPa | 30000 psi | |
Pyrotek TS-102 Thermoset Electrical Insulation Product (Nema Grade: X) Paper reinforcement, Phenolic Resin, Natural Color. High mechanical strength. Electrical properties are secondary.ApplicationsSuperstructure support pads Bus bar insulators Pot cradle insulators E.. |
|||
Flexural Strength | 207 MPa @Thickness 3.17 mm |
30000 psi @Thickness 0.125 in |
LW |
Industrial Laminates/Norplex MC507U Glass Fabric Description: MC507U is a utility grade, glass fabric/silicone resin binder composite product that can be substituted for NEMA G-7, in most heating, appliance insulation and some bearing applications.. |
|||
Flexural Strength | 207 MPa | 30000 psi | ASTM D790 |
MRC Polymers EMAREXâ„¢ 300 GF33 Nylon 6, 33% Glass Fiber Filled Available in Black onlyCan be UV and Heat StabilizedProperty data for DAM samples.Information provided by MRC Polymers Inc. |
|||
Flexural Strength | 207 MPa | 30000 psi | ASTM D790 |
Techmer ES Elastoblend® PA6 GF30 IM L 30% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 30% Filler by WeightAdditive: Impact Modifier and LubricantFeatures: Impact Modified and LubricatedUL File N.. |
|||
Flexural Strength | 207 MPa | 30000 psi | ASTM D790 |
Solvay Specialty Polymers Ryton® R-7-121NA Polyphenylene Sulfide (PPS), GlassMineral Filled Ryton® R-7-121NA and R-7-121BL glass fiber and mineral filled polyphenylene sulfide compounds provide good mechanical strength with good flow and low maintenance molding using conventional moldin.. |
|||
Flexural Strength | 207 MPa | 30000 psi | ASTM D790 |
Techmer ES HiFill® PA6 CF20 RM BK 20% Carbon Fiber Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber Reinforcement, 20% Filler by WeightAppearance: BlackFeatures: Low Moisture AbsorptionTPCI# 9720102Information provided by.. |
|||
Flexural Strength | 207 MPa | 30000 psi | ASTM D790 |
Techmer ES HiFill® PA6 GF20 HS L BK 20% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 20% Filler by Weight Additive: Lubricant and Heat StabilizerFeatures: Heat Stabilized and LubricatedAppearan.. |
|||
Flexural Strength | 207 MPa | 30000 psi | ASTM D790 |
Techmer ES HiFill® PA6/6 GF33 NAT001 Y 33% Glass Filled (Conditioned) Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 33% Filler by WeightAdditive: Lubricant and Heat StabilizerFeatures: Lubricated and Heat StabilizedUL File N.. |
|||
Flexural Strength | 207 MPa | 30000 psi | ASTM D790 |
Techmer ES Plaslube® J-1/CF/10/TF/20 BK PA66 |
|||
Flexural Strength | 207 MPa | 30000 psi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP JF006 PES LNP* THERMOCOMP* JF006 is a compound based on Polyethersulfone resin containing 30% Glass Fiber. |
|||
Flexural Strength | 207 MPa | 30000 psi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP JF008E PES LNP* THERMOCOMP* JF008E is a compound based on Polyethersulfone containing 40% Glass Fiber. Characteristics of this grade are: Easy Molding. |
|||
Flexural Strength | 207 MPa | 30000 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP RF006EUC PA 66 LNP* THERMOCOMP* RF006EUC is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added features of this material include Easy Molding, UV Stabilized. |
|||
Flexural Strength | 207 MPa | 30000 psi | ASTM D790 |
Chase Plastics CP Pryme® N120L (Dry) Nylon 6, 20% Glass Fiber Reinforced, Lubricated Features: LubricatedForm: PelletsInformation provided by Chase Plastics. |
|||
Flexural Strength | 207 MPa @Temperature -40.0 °C |
30000 psi @Temperature -40.0 °F |
ASTM Test |
BASF Ultramid® 8260 40% Mineral Filled PA6 (Dry) Ultramid 8260 is a 40% mineral reinforced PA6 injection molding compound. It possesses high stiffness, dimensional stability and heat resistance combined with excellent processability including low.. |
|||
Flexural Strength | 207 MPa | 30000 psi | |
Aremco AREMCOLOX™ 502-1900-YTZP Dense Yttria Stabilized Zirconium Oxide This grade offers a high flexural strength for a zirconia. The fine grain size lends itself to be used in cutting tools where a very sharp edge can be achieved and maintained due to its high wear re.. |
|||
Flexural Strength | 207 MPa | 30000 psi | ASTM D790 |
A. Schulman ComAlloy Hiloy® 414 Polyester - PBT, Glass Reinforced Data provided by the manufacturer, ComAlloy International Company.45% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Flexural Strength | 207 MPa | 30000 psi | ASTM D790 |
Adell BT-17 Nylon 6, 35% Glass Reinforced; Impact Modified Data provided by Adell Plastics, Inc. |
|||
Flexural Strength | 207 MPa | 30000 psi | ASTM D790 |
A. Schulman ComAlloy Hiloy® 757 Carbon Fiber Reinforced, Flow Enhanced, PPS Alloy Data provided by the manufacturer, ComAlloy International Company.30% Carbon Fiber Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Flexural Strength | 207 MPa | 30000 psi | ASTM D790 |
PolyOne Stat-Tech™ ES-06CF-09GF/000 Polyethersulfone, Glass/Carbon Fiber Filled
(discontinued **) Description/Features:Glass/Carbon Fiber ReinforcedInformation provided by PolyOne Corporation. |
|||
Flexural Strength | 207 MPa | 30000 psi | ASTM D790 |
Techmer ES HiFill FR® PA6/6 GF25 FR NAT005 25% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 25% Filler by WeightAdditive: Heat Stabilizer and LubricantFeatures: Flame Retardant, Heat Stabilized, High Flow and Lubri.. |