- PolyOne Stat-Tech™ ES-06CF-09GF/000 Polyethersulfone, Glass/Carbon Fiber Filled (discontinued **)
PolyOne Stat-Tech™ ES-06CF-09GF/000 Polyethersulfone, Glass/Carbon Fiber Filled (discontinued **)
| Category | Polymer , Thermoplastic , Polyethersulfone (PES) |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Stat-Tech™ ES-06CF-09GF/000 Polyethersulfone, Glass/Carbon Fiber Filled
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Glass/Carbon Fiber ReinforcedInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.44 g/cc | 1.44 g/cc | ASTM D792 |
| Water Absorption | 0.38 % @Thickness 0.508 mm |
0.38 % @Thickness 0.0200 in |
24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 131 MPa | 19000 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Yield | 3.0 % | 3.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 207 MPa | 30000 psi | ASTM D790 |
| Flexural Modulus | 7.58 GPa | 1100 ksi | ASTM D790 |
| Izod Impact, Notched | 0.641 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
1.20 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 213 °C | 415 °F | Unannealed, 0.125 in bars; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1e+05 - 5.00e+7 ohm-cm | 1e+05 - 5.00e+7 ohm-cm | ASTM D257 |
| Surface Resistivity per Square | 10000 - 500000 ohm | 10000 - 500000 ohm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 354 - 382 °C | 670 - 720 °F | Molding |
| Mold Temperature | 93.3 - 121 °C | 200 - 250 °F | |
| Drying Temperature | 135 - 149 °C | 275 - 300 °F | |
| Dry Time | 4 hour | 4 hour |
Users viewing this material also viewed the following:
- PlastiComp Complet® LGF60 - PA66 Nylon 66, 60% Long Glass Fiber Reinforced
- Park Electrochemical Nelco® NH9410 PTFE Laminate, Woven-Glass and Ceramic Reinforced
- LG Chemical LUMID GP2330BL PA66+GF33%, General Purpose
- Haynes 625 alloy, plate, as annealed at 1025°C, rapid cooled
- Sumitomo Bakelite North America 2008A Glass Reinforced Hardware Grade Epoxy
- Esstech V-117-1095 Barium Borosilicate Glass
- Fainplast Compounds GS 92 Flexible PVC, Injection Molding for Technical Items
- Arkema Group Rilsan® MB 3750 Nylon 11, Transparent Grade (Conditioned)
- 3M OFM0302 Outdoor UL Recognized White Polyester Label Product
- Arkema Group Orgalloy® RS 6030 Nylon 6 Alloy, 30% Glass Fiber (Conditioned)
Copyright © lookpolymers.com All Rights Reserved