SABIC Innovative Plastics LNP THERMOCOMP JF008E PES
| Category | Polymer , Thermoplastic , Polyethersulfone (PES) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP JF008E PES.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* JF008E is a compound based on Polyethersulfone containing 40% Glass Fiber. Characteristics of this grade are: Easy Molding.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.69 g/cc | 1.69 g/cc | ASTM D792 |
| Moisture Absorption | 0.320 % | 0.320 % | 50% RH, 24 hrs; ASTM D570 |
| 0.490 % | 0.490 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0070 cm/cm @Time 86400 sec |
0.0050 - 0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 146 MPa | 21200 psi | 5 mm/min; ISO 527 |
| 152 MPa | 22000 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 146 MPa | 21200 psi | 5 mm/min; ISO 527 |
| 152 MPa | 22000 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.5 % | 1.5 % | 5 mm/min; ISO 527 |
| 1.7 % | 1.7 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 1.5 % | 1.5 % | 5 mm/min; ISO 527 |
| 1.7 % | 1.7 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 13.76 GPa | 1996 ksi | 1 mm/min; ISO 527 |
| 15.38 GPa | 2231 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 207 MPa | 30000 psi | ISO 178 |
| 208 MPa | 30200 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Yield Strength | 209 MPa | 30300 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 12.17 GPa | 1765 ksi | 2 mm/min; ISO 178 |
| 12.29 GPa | 1783 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.770 J/cm | 1.44 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.68 J/cm | 10.6 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 34.0 kJ/m² | 16.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 13.0 J @Temperature 23.0 °C |
9.59 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 5.00 µm/m-°C @Temperature -30.0 - 30.0 °C |
2.78 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 1.00 µm/m-°C @Temperature -30.0 - 30.0 °C |
0.556 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 231 °C | 448 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 212 °C @Thickness 3.20 mm |
414 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 211 °C | 412 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 207 °C @Thickness 3.20 mm |
405 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Nilit Nilamid B3 H G10 50% Glass Fiber Reinforced PA6
- Latrobe LSSâ„¢ 135M Nitriding Steel (ASTM A355 Class A)
- SABIC Innovative Plastics Valox® IQ507 PBT+PC (Europe-Africa-Middle East)
- STAR Thermoplastic Alloys & Rubbers StarGrip GP 55-9000 TPE
- SABIC Innovative Plastics LNP THERMOCOMP RF008 PA 66 (Asia Pacific)
- A. Schulman FORMION™ FI 342 Ionomer
- Ashley Polymers Ashlene® 742L-33G Nylon 6/66, 33% Glass Reinforced
- Haynes 625 alloy, 30% cold reduction
- Proto3000 PPSF Fused Deposition Modeling Polymer
Copyright © lookpolymers.com All Rights Reserved