Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 193 MPa | 28000 psi | ASTM D790 |
Oxford Polymers PEI 10GF-Natural PEI, 10% Glass Fiber Reinforced Product Description: Glass Fiber (10% Reinforced), Polyetherimide injection molding grade Processing and Delivery Form: Pellets and Injection Molding Additives: Release AgentsSpecial Characteristic.. |
|||
Flexural Strength | 193 MPa | 28000 psi | ASTM D790 |
Ravago Manufacturing Americas Hylon® N1033L Nylon 6/6 (Cond)
(discontinued **) Information provided by Ravago. |
|||
Flexural Strength | 193 MPa | 28000 psi | ASTM D790 |
IDI Composites A-205 Thermoset Polyester, Sheet AUTOMOTIVE - Versatile family of compounds specifically designed for automotive structural applications. Low shrink characteristics, heat resistance, long-term dimensional stability, and corrosion r.. |
|||
Flexural Strength | 193 MPa | 28000 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP RFP36S PA 66 LNP* LUBRICOMP* RFP36S is a compound based on Nylon 66 resin containing 30% Glass Fiber, 15% PTFE/Silicone. Added features of this material include: Wear Resistant, Heat Stabilized. |
|||
Flexural Strength | 193 MPa | 28000 psi | ASTM D790 |
SABIC Innovative Plastics LNP STAT-KON DE003P PC (Asia Pacific) LNP STAT-KON* DE003P is a compound based on Polycarbonate resin containing Carbon Fiber. Added features of this material include: Electrically Conductive. |
|||
Flexural Strength | 193 MPa | 28000 psi | ASTM D790 |
Techmer ES HiFill® PA6 GF20 L BK002 20% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 20% Filler by Weight Additive: LubricantFeatures: Lubricated and High FlowAppearance: BlackTPCI# 8376102Info.. |
|||
Flexural Strength | 193 MPa | 28000 psi | ISO 178 |
SABIC Innovative Plastics LNP Thermocomp HX05073 PA 11 LNP THERMOCOMP* HX05073 is a compound based on Nylon 11 resin containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region. |
|||
Flexural Strength | 193 MPa | 28000 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP RF005 PA 66 LNP* THERMOCOMP* RF005 is a compound based on Nylon 66 resin containing 25% Glass Fiber. |
|||
Flexural Strength | 193 MPa | 28000 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOTUF VF008 PA 66 (Asia Pacific) LNP THERMOTUF* VF008 is a compound based on Nylon resin containing Glass Fiber. Added features of this material include: High Impact. |
|||
Flexural Strength | 193 MPa | 28000 psi | ASTM D790 |
Techmer ES Electrablend® PA6/6 03004 GF20 Carbon/20% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber Reinforcement/Glass Fiber Reinforcement, 20% Filler by WeightAdditive: Lubricant, Impact Modifier and Heat StabilizerFeatu.. |
|||
Flexural Strength | 193 MPa | 28000 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP OF006A PPS - Branched LNP* THERMOCOMP* OF006A is a compound based on PPS - Branched resin containing 30% Glass Fiber. |
|||
Flexural Strength | 193 MPa | 28000 psi | ASTM D790 |
Chase Plastics CP Pryme® AH100 Acetal Homopolymer Information provided by Chase Plastics. |
|||
Flexural Strength | 193 MPa | 28000 psi | ASTM D790 |
A. Schulman SCHULADUR® A GF30 30% Glass Fiber Reinforced PBT Information provided by A. Schulman. |
|||
Flexural Strength | 193 MPa @Temperature 22.8 °C |
28000 psi @Temperature 73.0 °F |
ASTM D790 |
Ensinger TECAPEI® 10% Glass Reinforced, made from Ultem® 2100 PEI TECAPEI™ is an amorphous thermoplastic polyetherimide (PEI) made from Sabic Innovative Plastics' Ultem® 1000 and 2000 series resins. The unreinforced 1000 series materials are translucent amber in.. |
|||
Flexural Strength | 193 - 200 MPa | 28000 - 29000 psi | |
Bulk Molding Compounds BMC 1608 Very High Strength, Corrosion Resistant BMC 1608 is a very high strength, general purpose, corrosion resistant material. Recommended for compression molding only. UL® recognized. Meets FDA requirements for food contact. This material was.. |
|||
Flexural Strength | 193 MPa | 28000 psi | ASTM D790 |
Techmer Lehvoss Compounds Luvotech™ J-4/30/V0 NAT PA6/12
(discontinued **) Techmer Lehvoss Compounds, a JV between Techmer ES and Lehmann&Voss&Co. has been terminated. |