Oxford Polymers PEI 10GF-Natural PEI, 10% Glass Fiber Reinforced

Category Polymer , Thermoplastic , Polyetherimide (PEI) , Polyetherimide (PEI), 10% Glass Fiber
Manufacturer Oxford Polymers
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Oxford Polymers PEI 10GF-Natural PEI, 10% Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: Glass Fiber (10% Reinforced), Polyetherimide injection molding grade Processing and Delivery Form: Pellets and Injection Molding Additives: Release AgentsSpecial Characteristics: Easy flowInformation provided by Oxford Polymers
Physical Properties Metric English Comments
Density 1.34 g/cc
0.0484 lb/in³
ASTM D792
Water Absorption at Saturation 0.250 %
0.250 %
ASTM D570
Linear Mold Shrinkage, Flow 0.00500 cm/cm

@Thickness 3.17 mm
0.00500 in/in

@Thickness 0.125 in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 114 MPa
16600 psi
ASTM D638
Elongation at Break 5.80 %
5.80 %
ASTM D638
Flexural Strength 193 MPa
28000 psi
ASTM D790
Flexural Modulus 4.48 GPa
650 ksi
ASTM D790
Izod Impact, Notched 0.587 J/cm

@Thickness 3.17 mm
1.10 ft-lb/in

@Thickness 0.125 in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 207 °C
405 °F
Unannealed; ASTM D648
Processing Properties Metric English Comments
Rear Barrel Temperature 343 °C
650 °F
Middle Barrel Temperature 349 °C
660 °F
Front Barrel Temperature 354 °C
670 °F
Nozzle Temperature 357 °C
675 °F
Melt Temperature 352 °C
665 °F
Mold Temperature 135 °C
275 °F
Drying Temperature <= 149 °C
<= 300 °F
Dry Time 4.00 - 6.00 hour
4.00 - 6.00 hour