SABIC Innovative Plastics LNP Thermocomp HX05073 PA 11
| Category | Polymer , Thermoplastic , Nylon , Nylon 11 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp HX05073 PA 11.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* HX05073 is a compound based on Nylon 11 resin containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.26 g/cc | 0.0455 lb/in³ | ISO 1183 |
| 1.263 g/cc | 0.04563 lb/in³ | ASTM D 792 | |
| Moisture Absorption at Equilibrium | 0.15 % @Time 86400 sec |
0.15 % @Time 24.0 hour |
50% RH; ASTM D 570 |
| Linear Mold Shrinkage, Flow | 0.0011 cm/cm @Time 86400 sec |
0.0011 in/in @Time 24.0 hour |
ISO 294 |
| 0.0010 - 0.0020 cm/cm @Time 86400 sec |
0.0010 - 0.0020 in/in @Time 24.0 hour |
ASTM D 955 | |
| Linear Mold Shrinkage, Transverse | 0.0062 cm/cm @Time 86400 sec |
0.0062 in/in @Time 24.0 hour |
ISO 294 |
| 0.0060 - 0.0070 cm/cm @Time 86400 sec |
0.0060 - 0.0070 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 130 MPa | 18900 psi | ISO 527 |
| 134 MPa | 19400 psi | ASTM D 638 | |
| Elongation at Break | 6.2 % | 6.2 % | ASTM D 638 |
| 6.3 % | 6.3 % | ISO 527 | |
| Tensile Modulus | 7.08 GPa | 1030 ksi | 1 mm/min; ISO 527 |
| 7.37 GPa | 1070 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 193 MPa | 28000 psi | ISO 178 |
| 195 MPa | 28300 psi | ASTM D 790 | |
| Flexural Modulus | 6.20 GPa | 899 ksi | ASTM D 790 |
| 6.64 GPa | 963 ksi | ISO 178 | |
| Izod Impact, Notched | 2.56 J/cm @Temperature 23.0 °C |
4.80 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 14.31 J/cm @Temperature 23.0 °C |
26.81 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 25.0 kJ/m² @Temperature 23.0 °C |
11.9 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 87.0 kJ/m² @Temperature 23.0 °C |
41.4 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 6.00 J | 4.43 ft-lb | Multiaxial Impact; ISO 6603 |
| 16.0 J @Temperature 23.0 °C |
11.8 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 34.3 µm/m-°C @Temperature -40.0 - 40.0 °C |
19.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 34.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
19.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 99.7 µm/m-°C @Temperature -40.0 - 40.0 °C |
55.4 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 99.7 µm/m-°C @Temperature -40.0 - 40.0 °C |
55.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 174 °C | 345 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 178 °C @Thickness 3.20 mm |
352 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- Omni Plastics OmniTuff™ HPP GRC40 Homopolymer Polypropylene Glass Reinforced
- MetalTek RENE® 77 Centri-Vac Nickel Cobalt Based Alloy
- SSAB Tunnplat Aluzink 350A YP High-strength Metal-coated Steel
- Teknor Apex Monprene® MP-2750L1 Thermoplastic Elastomer
- ExxonMobil 460 Mobilgear SHC Series
- Lubrizol Estane® 54611 Polyester-Based Thermoplastic Polyurethane
- Clariant Renol R66G13HSL Nylon 66, 13% Glass Fiber, Heat Stabilized, Lubricated, Economy
- 3M Scotchrap™ Pipe Primer
- Beijing Ranger Chem SM-601X75 Solvent Based Epoxy Resin
Copyright © lookpolymers.com All Rights Reserved