SABIC Innovative Plastics LNP THERMOCOMP OF006A PPS - Branched
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP OF006A PPS - Branched.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* OF006A is a compound based on PPS - Branched resin containing 30% Glass Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.58 g/cc | 0.0571 lb/in³ | ASTM D792 |
| 1.58 g/cc | 0.0571 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.0600 % | 0.0600 % | 23°C / 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0013 - 0.0030 cm/cm @Time 86400 sec |
0.0013 - 0.0030 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0070 cm/cm @Time 86400 sec |
0.0040 - 0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0040 - 0.0070 cm/cm @Time 86400 sec |
0.0040 - 0.0070 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 129 MPa | 18700 psi | ASTM D638 |
| 129 MPa | 18700 psi | ISO 527 | |
| Elongation at Break | 1.2 % | 1.2 % | ISO 527 |
| 1.3 % | 1.3 % | ASTM D638 | |
| Tensile Modulus | 12.48 GPa | 1810 ksi | 1 mm/min; ISO 527 |
| 12.73 GPa | 1846 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 193 MPa | 28000 psi | ASTM D790 |
| 220 MPa | 31900 psi | ISO 178 | |
| Flexural Modulus | 11.25 GPa | 1632 ksi | ASTM D790 |
| 11.88 GPa | 1723 ksi | ISO 178 | |
| Izod Impact, Notched | 0.690 J/cm | 1.29 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.05 J/cm | 7.59 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 31.0 kJ/m² | 14.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 8.00 J | 5.90 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 23.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
13.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 24.1 µm/m-°C @Temperature -40.0 - 40.0 °C |
13.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 45.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
25.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 45.7 µm/m-°C @Temperature -40.0 - 40.0 °C |
25.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 266 °C | 511 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 267 °C @Thickness 3.20 mm |
513 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Flammability, UL94 | V-0 @Thickness 0.450 mm |
V-0 @Thickness 0.0177 in |
UL 94 by SABIC-IP |
Users viewing this material also viewed the following:
- MV Labs LI200 LiBr Lithium bromide
- Polymax® Maxelast® F02-141J TPE, Halogen Free Extrusion Grade
- Parker Chomerics SOFT-SHIELD® 5000 Low Closure Force EMI Gasket
- Resinlab® CYNERGY CA6810 Adhesive
- Heatbath/Park Marquench Oil M
- SABIC Innovative Plastics NORYL GTX GTX914 PPE+PA (Asia Pacific)
- China-Yixing Longly Refractories Alumina Plates and Pieces Microcrystal Wear-Resistant Alumina Ceramic Lining Plates and Pieces
- Arlon 28561R015 0.015" (0.381 mm) Uncured Silicone Rubber with Fiberglass Substrate
- 3M Jet-melt™ 3731 Polyolefin Bonding Adhesive
- 3M Scotchcal™ 3632-20 Translucent Film
Copyright © lookpolymers.com All Rights Reserved