- Polymer Property : Melt Flow = 15 g/10 min
Polymer Property : Melt Flow = 15 g/10 min Product List
Physical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 15 g/10 min @Load 2.16 kg, Temperature 230 °C |
15 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| RheTech Products CS30P100-01UV 30% Ceramic Sphere Reinforced Polypropylene, UV Stabilized, Black Applications: Consumer goodsHousingsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Melt Flow | 15 - 30 g/10 min @Load 2.16 kg, Temperature 210 °C |
15 - 30 g/10 min @Load 4.76 lb, Temperature 410 °F |
ASTM D1238 |
| NatureWorks® Ingeo™ 6201D Fiber Grade PLA NatureWorks® PLA polymer 6201D is a thermoplastic fiber-grade resin derived primarily from annually renewable resources. Available in pellet form, 6201D is designed for extrusion into mechanically .. |
|||
| Melt Flow | 15 g/10 min @Load 2.16 kg, Temperature 230 °C |
15 g/10 min @Load 4.76 lb, Temperature 446 °F |
Procedure A Condition L; ASTM D1238 |
| Network Polymers NPP 25-1503 G10 Description: Glass Reinforced PolypropyleneInformation provided by Network Polymers Inc. |
|||
| Melt Flow | 15 - 20 g/10 min @Load 2.16 kg, Temperature 230 °C |
15 - 20 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238/L |
| NIZHNEKAMSKNEFTEKHIM PP 1500P (V30G) Propylene Homopolymer Product obtained by polymerization of propylene in presence of complex metalorganic catalysts. It incorporates increased long-term thermal stability, thermal-oxidative degradation resistance when P.. |
|||
| Melt Flow | 15 - 20 g/10 min @Load 2.16 kg, Temperature 265 °C |
15 - 20 g/10 min @Load 4.76 lb, Temperature 509 °F |
ASTM D1238 |
| Polymer Resources PC/TP-GP1-HF PC/Polyester Alloy, High Melt Flow High Melt Flow, Good Chemical ResistanceProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by .. |
|||
| Melt Flow | 15 g/10 min @Load 1.20 kg, Temperature 224 °C |
15 g/10 min @Load 2.65 lb, Temperature 435 °F |
|
| Dow Pellethane® 2102-90AR Polyurethane Elastomer, Polyester Polycaprolactone Based
(discontinued **) PELLETHANE® 2102-90AR elastomer is a polyester polycaprolactone based polyurethane elastomer which combines excellent resistance to fuels and oils with enhanced mold release, low compression set, a.. |
|||
| Melt Flow | 15 g/10 min @Load 2.16 kg, Temperature 330 °C |
15 g/10 min @Load 4.76 lb, Temperature 626 °F |
ASTM D1238 |
| Covestro Apec® DP9-9343 High-Heat Polycarbonate, UV Stabilized
(discontinued **) Information provided by Bayer Corporation, Plastics DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and has officially adopted its new name – Covestro. This produ.. |
|||
| Melt Flow | 15 - 20 g/10 min | 15 - 20 g/10 min | ASTM D3275 |
| Solvay Specialty Polymers Halar® 558 Polyethylene, Chlorotrifluoroethylene (ECTFE)
(Unverified Data**)< Halar 558 fluoropolymer is a resin grade for foam extrusion applications, including primary insulations, coaxial cable cores, cross-webs, fire alarm cable, jackets, and foam tubing. Like other grade.. |
|||
| Melt Flow | 15 - 20 g/10 min | 15 - 20 g/10 min | |
| Lehmann & Voss LUVOCOM® 50/CF/10/TF/15/BK 100 Polycarbonate, with carbon fiber and PTFE Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.High-strength and high-stiff parts; low coefficient of expansi.. |
|||
| Melt Flow | 15 g/10 min @Load 5.00 kg, Temperature 200 °C |
15 g/10 min @Load 11.0 lb, Temperature 392 °F |
ISO 1133 |
| Kraton® D42070 B (O/E SBS) Branched Copolymer Description: Kraton® D4270B is an oiled, branched copolymer based on styrene and butadiene with a polystyrene content of 32%. It is supplied from South America in the physical form identified: D4.. |
|||
| Melt Flow | 15 g/10 min @Load 2.16 kg, Temperature 230 °C |
15 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| IRPC Polimaxx Polene 1100PK Polypropylene Homopolymer CHARACTERISTICS: HIGH FLOW, GOOD STIFFNESS, GOOD PROCESSABILITY, GOOD MELT STABILITYAPPLICATIONS: MULTI - FILAMENT FOR BELTS, FIBRES FOR CARPETS INJECTION MOLDING FOR THIN WALL PARTS, HOUSEWARES |
|||
| Melt Flow | 15 - 30 g/10 min @Load 2.16 kg, Temperature 170 °C |
15 - 30 g/10 min @Load 4.76 lb, Temperature 338 °F |
ISO 1133 |
| Lubrizol Advanced Materials PEARLBOND® 520 Linear Thermoplastic Polyurethane Pearlbond™ 520 is a linear, polycaprolactone-copolyester polyurethane, supplied in form of white spherical granules with a very high crystallization rate and a very high thermoplasticity level... |
|||
| Melt Flow | 15 g/10 min @Load 1.20 kg, Temperature 300 °C |
15 g/10 min @Load 2.65 lb, Temperature 572 °F |
ISO 1133; ASTM D1238 |
| Styron CALIBREâ„¢ 2091-15 Polycarbonate Resin Overview: CALIBREâ„¢ MEGARADâ„¢ 2091 Polycarbonate Resins are designed for single use medical devices (SUDs) that require gamma and electron-beam irradiation and an accelerated schedule for de.. |
|||
| Melt Flow | 15 g/10 min @Load 1.20 kg, Temperature 300 °C |
15 g/10 min @Load 2.65 lb, Temperature 572 °F |
ISO 1133 |
| Styron CALIBREâ„¢ 7100-15 Polycarbonate CALIBREâ„¢ 7100-15 glass-reinforced resin offers increased modulus and improved heat distortion resistance, with minimal shrinkage. It also offers outstanding UL-94 flammability ratings. CALIBR.. |
|||
| Melt Flow | 15 g/10 min @Load 1.20 kg, Temperature 300 °C |
15 g/10 min @Load 2.65 lb, Temperature 572 °F |
ISO 1133 |
| Styron CALIBREâ„¢ 7101-15 Polycarbonate CALIBREâ„¢ 7101-15 glass-reinforced resin offers increased modulus and improved heat distortion resistance, with minimal shrinkage. It also offers outstanding UL-94 flammability ratings. CALIBR.. |
|||
| Melt Flow | 15 g/10 min @Load 2.16 kg, Temperature 190 °C |
15 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| A. Schulman POLYBATCH™ Beige 1266E Concentrate Based In Polyethylene DescriptionPOLYBATCH® 1266E is a beige color concentrate based in polyethylene. This concentrate was designed to provide opacity and color in polyolefin film and molding applications. POLYBATCH®.. |
|||
| Melt Flow | 15 g/10 min | 15 g/10 min | ASTM D1238 |
| Tipco Tipcolene® NPI 200 IN - 25% Talc/Mineral Reinforced Polypropylene Copolymer with Very High Flow, Stiffness & Impact Strength 20% Mineral Reinforced, Very High Stiffness & Very High Impact PP CopolymerApplications: Automotive DashboardsProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries .. |
|||
| Melt Flow | 15 g/10 min | 15 g/10 min | ASTM D1238 |
| Westlake Elevate™ EF526 16% Ethylene Vinyl Acetate Copolymer Westlake Elevate™ EF526 resin is a 16% EVA copolymer designed for cast film, extrusion coatings, and thermal laminations.Application/UsesThermal laminationsCast FilmExtrusion CoatingsThis resin gra.. |
|||
| Melt Flow | 15 g/10 min @Load 2.16 kg, Temperature 190 °C |
15 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| A. Schulman POLYBATCH™ Blue 4300 Concentrate Based In Polyethylene DescriptionPOLYBATCH® 4300 is a blue color concentrate based in polyethylene. This concentrate was designed to provide opacity and color in polyolefin film and molding applications. POLYBATCH® 4.. |
|||
| Melt Flow | 15 g/10 min @Load 2.16 kg, Temperature 190 °C |
15 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| A. Schulman POLYBATCH™ Ivory 9035 Concentrate Based In Polyethylene DescriptionPOLYBATCH® 9035 is an ivory color concentrate containing based in polyethylene. This concentrate was designed to provide color and opacity in film and molding applications. POLYBATCH®.. |
|||
| Melt Flow | 15 g/10 min @Load 2.16 kg, Temperature 250 °C |
15 g/10 min @Load 4.76 lb, Temperature 482 °F |
ISO 1133 |
| Polyram RamSter PF340S6 PBT, 30% Glass Beads 30% Glass beads reinforced PBT for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
| Melt Flow | 15 g/10 min @Load 5.00 kg, Temperature 240 °C |
15 g/10 min @Load 11.0 lb, Temperature 464 °F |
ISO 1133 |
| Covestro Bayblend® FR 3010 Polycarbonate + ABS, Flame Retardant Grade Injection molding gradeincreased heat resistanceVicat/B 120 temperature = 110 °CUL-listing 94 V-0 (1.5 mm) antimony-, chlorine- and bromine-free flame retardantglow wire test (GWFI): 960 °C (.. |
|||
| Melt Flow | 15 g/10 min | 15 g/10 min | ASTM D1238 |
| Engineered Plastics EPPC 1514G Polycarbonate Gray injection grade. Property values below represent typical values. Information provided by Engineered Plastics Corporation. |
|||
| Melt Flow | 15 g/10 min @Load 5.00 kg, Temperature 200 °C |
15 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Diamond Polymers SBS 1001 Styrene Butadiene Block Copolymer Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc. |
|||
| Melt Flow | 15 g/10 min @Load 2.16 kg, Temperature 230 °C |
15 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D 1238 |
| Cossa Polimeri ESTAPROP KUR 1520 TG05 Polypropylene, 10% Mineral Filled PP copolymer 10% mineral fillerElastomer modified, very high impact strength at low temperatureInformation provided by Cossa Polimeri S.r.l. |
|||
| Melt Flow | 15 g/10 min @Load 10.0 kg, Temperature 220 °C |
15 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D-1238 |
| Bhansali Engineering Abstron HR-60 ABS Heat Resistant High, Medium Impact Heat Resistant Grades with good flowInformation provided by Bhansali |
|||
| Melt Flow | 15 g/10 min | 15 g/10 min | ASTM D1238 |
| Aaron Industries AAROPRENE® ATPR ECATPR2040 Black Thermoplastic SEBS Rubber AAROPRENE® ATPR 2000 Series Elastomeric CompoundFeatures: A black, thermoplastic SEBS Rubber compound specifically designed for the injection molding of industrial gaskets. |
|||
| Melt Flow | 15 g/10 min @Load 5.00 kg, Temperature 300 °C |
15 g/10 min @Load 11.0 lb, Temperature 572 °F |
ASTM D1238 |
| BLUESTAR LXS 115 PPE-PS Typical Applications: Auto connect partsFire RatedInformation provided by Polymer Technology and Services, LLC (PTS). |
|||
| Melt Flow | 15 - 25 g/10 min | 15 - 25 g/10 min | ASTM D1238 |
| Polymer Resources PPX-MF-FR1 Modified PPO, UL 94 V-0 with HDT of 190 F, Mineral Reinforced
(Unverified Da Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||
| Melt Flow | 15 g/10 min @Load 10.0 kg, Temperature 220 °C |
15 g/10 min @Load 22.0 lb, Temperature 428 °F |
Melt Volume Rate (ml/10 min); ISO 1133 |
| Chi Mei Polylac® PA-746Y ABS
(discontinued **) Medium flow, high impact |
|||