NatureWorks® Ingeo™ 6201D Fiber Grade PLA

Category Polymer , Renewable/Recycled Polymer , Thermoplastic , Polylactic Acid (PLA) Biopolymer
Manufacturer NatureWorks LLC
Trade Name Ingeo™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF NatureWorks® Ingeo™ 6201D Fiber Grade PLA.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
NatureWorks® PLA polymer 6201D is a thermoplastic fiber-grade resin derived primarily from annually renewable resources. Available in pellet form, 6201D is designed for extrusion into mechanically drawn staple fibers or continuous filament, using conventional fiber spinning and drawing equipment. 6201D is typically well suited for fiber processes where lower fiber shrinkage is desired: partially orientated yarn (POY), fully drawn yarn (FDY), staple fibers, and continuous filament. NatureWorks® PLA 6201D can be converted into a broad range of fiber products. Potential applications for PLA polymer 6201D include Woven and knitted 100% continuous filament apparel; Woven and knitted, intimate staple blend fabrics including blends with cotton, wool, and other fibers; Woven and knitted fabrics and netting for civil engineering applications; Home furnishings
Physical Properties Metric English Comments
Specific Gravity 1.24 g/cc
1.24 g/cc
ASTM D792
Melt Density 1.08 g/cc

@Temperature 230 °C
0.0390 lb/in³

@Temperature 446 °F
ASTM D1238
Viscosity Measurement 3.1
3.1
Relative Viscosity; CD Internal Viscotek Method
Melt Flow 15 - 30 g/10 min

@Load 2.16 kg,
Temperature 210 °C
15 - 30 g/10 min

@Load 4.76 lb,
Temperature 410 °F
ASTM D1238
Mechanical Properties Metric English Comments
Elongation at Break 10 - 70 %
10 - 70 %
Fiber; ASTM D2256/ASTM D3822
Tenacity 0.221 - 0.441 N/tex
2.50 - 5.00 g/denier
ASTM D2256/ASTM D3822
Thermal Properties Metric English Comments
Melting Point 160 - 170 °C
320 - 338 °F
ASTM D3418
Glass Transition Temp, Tg 55.0 - 60.0 °C
131 - 140 °F
ASTM D3417
Shrinkage 5.0 - 15 %
5.0 - 15 %
Boiling Water; ASTM D2102
5.0 - 15 %

@Temperature 130 °C,
Time 600 sec
5.0 - 15 %

@Temperature 266 °F,
Time 0.167 hour
Hot Air; ASTM D2102
Processing Properties Metric English Comments
Drying Temperature 80.0 °C

@Time 14400 sec
176 °F

@Time 4.00 hour
Dew Point -35.0 °C
-31.0 °F
Drying Air Flow Rate >= 14.2 l/min
>= 0.500 ft³/min (CFM)