Polyram RamSter PF340S6 PBT, 30% Glass Beads
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Glass Bead Filled |
| Manufacturer | Polyram |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram RamSter PF340S6 PBT, 30% Glass Beads.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
30% Glass beads reinforced PBT for injection molding applicationsInformation provided by Polyram Ram On Ind.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.53 g/cc | 0.0553 lb/in³ | DIN 53479 |
| Water Absorption | 0.50 % | 0.50 % | DIN 53495 |
| Moisture Absorption at Equilibrium | 0.15 % | 0.15 % | 23° C, 50% RH; DIN 53714 |
| Linear Mold Shrinkage | 0.0198 cm/cm | 0.0198 in/in | |
| Melt Flow | 15 g/10 min @Load 2.16 kg, Temperature 250 °C |
15 g/10 min @Load 4.76 lb, Temperature 482 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 57.0 MPa | 8270 psi | ASTM-D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM-D638 |
| Flexural Strength | 95.0 MPa | 13800 psi | ASTM D790 |
| Flexural Modulus | 2.30 GPa | 334 ksi | ASTM-D790 |
| Izod Impact, Notched | 0.350 J/cm @Temperature 23.0 °C |
0.656 ft-lb/in @Temperature 73.4 °F |
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 225 °C | 437 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | DIN 53461 |
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | DIN 53461 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
|
| Glow Wire Test | 650 °C | 1200 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | DIN 53482 |
| Dielectric Constant | 3.6 @Frequency 1e+6 Hz |
3.6 @Frequency 1e+6 Hz |
VDE 0303/4 |
| Dielectric Strength | 25.0 kV/mm | 635 kV/in | VDE 0303/4 |
Users viewing this material also viewed the following:
- ExxonMobil Escorene® LD-737 EVA Copolymer for Specialty Applications (discontinued **)
- Henkel Hysol EA 9896 WPP Peel Ply
- Microcell Composite Company CELLAMP® 5000 Pellets
- Teknor Apex Chemlon® ALF20 Nylon 66, Unreinforced
- A. Schulman POLYTROPE™ TPP 1008-01 Injection Molding Reactor Grade Olefinic Thermoplastic Elastomer
- Hexcel® HexForce™ 1522 Fiber Glass Fabric
- Chi Mei Polyrex® PH-88 Polystyrene - High Impact
- ExxonMobil 22 Mobil EAL Arctic Series
- LNP Verton™ UF-700-10 Polyphthalamide, Long Glass Fiber Reinforcement (discontinued **)
Copyright © lookpolymers.com All Rights Reserved