- Polymer Property : Melt Flow = 3.6 g/10 min
Polymer Property : Melt Flow = 3.6 g/10 min Product List
Physical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 3.6 g/10 min | 3.6 g/10 min | Condition 230/2-8; ASTM D1238 |
| Plaskolite Optix® CA-75 General Purpose Acrylic Resin Injection Molding and Extrusion Grade Pellets. Highest heat resistance, medium flow. |
|||
| Melt Flow | 3.6 g/10 min @Load 2.16 kg, Temperature 190 °C |
3.6 g/10 min @Load 4.76 lb, Temperature 374 °F |
Procedure A; ASTM D1238 |
| PolyOne Maxxam™ SY 89-23-7 Polypropylene, Unspecified (PP, Unspecified) Maxxam ™ SY 89-23-7 is a polypropylene copolymer compound with a pre-dispersed blowing agent for up to 60% expansion. The compound offers consistent cell structure, dielectric properties, and stren.. |
|||
| Melt Flow | 3.6 g/10 min | 3.6 g/10 min | Condition 230/2-8; ASTM D1238 |
| Plaskolite West Optix® CA-75 General Purpose Acrylic Resin Injection Molding and Extrusion Grade Pellets. Highest heat resistance, medium flow. |
|||
| Melt Flow | 3.6 g/10 min @Load 2.16 kg, Temperature 190 °C |
3.6 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Polimeri Europa Clearflex® CM 406 Hexene Copolymer Linear Low Density Polyethylene Clearflex CM 406 is a hexene copolymer linear low density polyethylene (C6-LLDPE), with antioxidants, suitable for cast film extrusion.Films manufactured with Clearflex CM 406 are characterized by h.. |
|||
| Melt Flow | 3.6 g/10 min @Load 5.00 kg, Temperature 200 °C |
3.6 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM Data |
| Americas Styrenics Styron® 8100 MFD High Impact Polystyrene
(discontinued **) STYRON 8100 MFD high impact polystyrene is designed for microfloppy diskettes (MFD) applications. It offers easy processing, coloring, abrasion resistance, impact strength, and high heat resistance... |
|||
| Melt Flow | 3.6 - 4.6 g/10 min @Load 2.16 kg, Temperature 230 °C |
3.6 - 4.6 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238/L |
| NIZHNEKAMSKNEFTEKHIM PP 1500K Propylene Homopolymer Product obtained by polymerization of propylene in presence of complex metalorganic catalysts. It incorporates increased long-term thermal stability, thermal-oxidative degradation resistance when P.. |
|||
| Melt Flow | 3.6 g/10 min | 3.6 g/10 min | Exxon Method |
| ExxonMobil Escorene® LD-401 EVA for Electrical Insulation
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A crosslinkable, 9.9% vinyl acetate copolymer designed for electrical applications.Applications: Base resin for fully formulated low voltage cable i.. |
|||
| Melt Flow | 3.6 g/10 min @Load 5.00 kg, Temperature 200 °C |
3.6 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Ineos Styrenics 166H General Purpose Polystyrene (NAFTA) Description: Polystyrene 166H is a high molecular weight general purpose polystyrene with good flow and crystal clarity. Polystyrene 166H offers good processing characteristics while yielding parts .. |
|||
| Melt Flow | 3.6 g/10 min @Load 5.00 kg, Temperature 200 °C |
3.6 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Ineos Styrenics Avantra® 525K High Impact Styrenic Polymer (NAFTA) Description: Specialty and super-high impact grades for a variety of applications such as refrigerator liners, consumer electronics housings, recreation equipment and sporting goods, toys, office pr.. |
|||
| Melt Flow | 3.6 g/10 min @Load 5.00 kg, Temperature 200 °C |
3.6 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Ineos Styrenics Avantra® 585K Q402 Rubber Modified Polystyrene Avantra® 585K Q402 is a high-impact grade of polystyrene with extremely high surface gloss and excellent practical toughness. Although Avantra® 585K Q402 can be processed by any method applic.. |
|||
| Melt Flow | 3.6 - 5.4 g/10 min @Load 2.16 kg, Temperature 190 °C |
3.6 - 5.4 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238-00 |
| Ipiranga Petrochem HD 7255 LS-L HDPE IPQ produces High Density Polyethylene (HDPE) for use by different segments of the plastics molding industry in several processes, including blow molding, extrusion and injection molding.To produce .. |
|||
| Melt Flow | 3.6 g/10 min @Load 2.16 kg, Temperature 190 °C |
3.6 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Iran Petrochemical (PCC) 6040UA High Density Polyethylene HD-6040UA is an ultra-violet light stabilized high density polyethylene injection grade with a narrow molecular weight distribution, specially developed for injection molding of heavy duty parts for.. |
|||
| Melt Flow | 3.6 g/10 min @Load 1.20 kg, Temperature 300 °C |
3.6 g/10 min @Load 2.65 lb, Temperature 572 °F |
Calculated from Volume Flow Rate of 3 cm<sup>3</sup>/10min.; ISO 1133 |
| Mitsubishi Xantar® 27 R Polycarbonate Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances .. |
|||
| Melt Flow | 3.6 g/10 min @Load 1.20 kg, Temperature 300 °C |
3.6 g/10 min @Load 2.65 lb, Temperature 572 °F |
Calculated from Volume Flow Rate of 3 cm<sup>3</sup>/10min.; ISO 1133 |
| Mitsubishi Xantar® 27 U Polycarbonate Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances .. |
|||
| Melt Flow | 3.6 g/10 min @Load 1.20 kg, Temperature 300 °C |
3.6 g/10 min @Load 2.65 lb, Temperature 572 °F |
Calculated from Volume Flow Rate of 3 cm<sup>3</sup>/10min.; ISO 1133 |
| Mitsubishi Xantar® MX 1071 FD Polycarbonate Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances .. |
|||
| Melt Flow | 3.6 - 10 g/10 min | 3.6 - 10 g/10 min | |
| Shandong Dongyue Shenzhou New Material Co DS603B Fluorinated Ethylene Propylene Dispersion (DS603A/B) Conformable with: Q/DYS 004-2007Fluorinated Ethylene Propylene concentrated dispersion is the copolymer of TFE and HFP, stabilized with non-ionic surfactant. It endow FEP products which can't be pr.. |
|||
| Melt Flow | 3.6 g/10 min @Load 5.00 kg, Temperature 200 °C |
3.6 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Samsung Cheil Industries Starex® VE-0857 ABS, Unreinforced FR Information provided by Samsung Cheil Industries. |
|||
| Melt Flow | 3.6 g/10 min @Load 5.00 kg, Temperature 200 °C |
3.6 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D 1238 |
| Styrolution PS 7800 HIPS Extremely high surface glossGood processabilityUL Classification 94 HBInformation provided by Styrolution |
|||
| Melt Flow | 3.6 g/10 min @Load 5.00 kg, Temperature 200 °C |
3.6 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Samsung Cheil Industries Starex® VE-0857 ABS, Unreinforced FR Information provided by Samsung Cheil Industries. |
|||
| Melt Flow | 3.6 g/10 min @Load 5.00 kg, Temperature 200 °C |
3.6 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D 1238 |
| Styrolution PS 2610 GPPS Extruded packaging; Thermoforming applicationsExcellent toughnessHigh melt strengthGood flow and processabilityInformation provided by Styrolution |
|||
| Melt Flow | 3.6 g/10 min | 3.6 g/10 min | |
| UBE UBEPOL BR13HB HIPS (n-DM =0.03 wt %) Description: UBEPOL-BR13HB is characterized by its low solution viscosity compared with conventional grades and short dissolution time in styrene monomer. Its main merits are as follows:Short dissol.. |
|||
| Melt Flow | 3.6 g/10 min | 3.6 g/10 min | |
| UBE UBEPOL BR15HB HIPS (n-DM =0.03 wt %) Description: UBEPOL-BR15HB is characterized by the highest branching of these 3 grades and is adapted by many PS manufacturers.Information provided by UBE. |
|||
| Melt Flow | 3.6 g/10 min | 3.6 g/10 min | |
| UBE UBEPOL BR15HL HIPS (n-DM =0.03 wt %) Description: UBEPOL-BR15HL is a linear type of polymer with the high solution viscosity. In case of enlarging the dispersed rubber particle size in |
|||
| Melt Flow | 3.6 g/10 min @Load 2.16 kg, Temperature 235 °C |
3.6 g/10 min @Load 4.76 lb, Temperature 455 °F |
ASTM D1238R |
| UBE UBESTA® 3030JI5L Plasticized Automotive Grade Nylon 12 Description: UBE UBESTA® Automotive grade Nylon 12Comments: meet SAE J844, DIN73378 HIPHLInformation provided by UBE. |
|||
| Melt Flow | 3.6 g/10 min @Load 2.16 kg, Temperature 235 °C |
3.6 g/10 min @Load 4.76 lb, Temperature 455 °F |
ASTM D1238R |
| UBE UBESTA® 3030JI7 Plasticized Industrial Grade Nylon 12 Description: UBE UBESTA® Industrial grade Nylon 12Comments: low migrationInformation provided by UBE. |
|||
| Melt Flow | 3.6 g/10 min @Load 2.16 kg, Temperature 190 °C |
3.6 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| ExxonMobil LLDPE LL 1236.86 Linear Low Density Polyethylene Resin Product Description: LL 1236 Series resins are butane LLDPEs with increased stiffness and a high melt index. They can be used alone or as a component in packaging and industrial film, blown or cast... |
|||
| Melt Flow | 3.6 g/10 min @Load 2.16 kg, Temperature 190 °C |
3.6 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| ExxonMobil LLDPE LL 4004EL Wire & Cable Linear Low Density Polyethylene Resin (European Grade) Product Description: LL 4004EL is a C4 Ziegler Natta LLDPE, especially designed for Low Voltage power cable insulation, using the two-step silane cross-linking process. Sufficient Cu-inhibitor shoul.. |
|||
| Melt Flow | 3.6 g/10 min @Load 2.16 kg, Temperature 190 °C |
3.6 g/10 min @Load 4.76 lb, Temperature 374 °F |
ExxonMobil Method |
| ExxonMobil Vistamaxx™ 3000 Propylene-based Elastomer Product Description: Vistamaxx 3000 propylene-based elastomer is an olefinic elastomer produced using ExxonMobil Chemical's EXXPOL™ Technology. It has moderate elastomeric properties, is easy to .. |
|||
| Melt Flow | 3.6 g/10 min @Load 2.16 kg, Temperature 230 °C |
3.6 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Braskem D036W6 Homopolymer Polypropylene Description: Injection Molding, General Purpose, Low Water CarryoverApplications: Suggested Uses Include Tape, Slit-film Fibers, Containers, Closures, HousewaresThis resin meets the requirements for.. |
|||
| Melt Flow | 3.6 g/10 min @Load 1.20 kg, Temperature 300 °C |
3.6 g/10 min @Load 2.65 lb, Temperature 572 °F |
Calculated from Volume Flow Rate of 3 cm<sup>3</sup>/10min.; ISO 1133 |
| Mitsubishi Xantar® 27 UR Polycarbonate Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances wher.. |
|||