- Polymer Property : Melt Flow = 3.5 g/10 min
Polymer Property : Melt Flow = 3.5 g/10 min Product List
Physical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 3.5 - 8.5 g/10 min | 3.5 - 8.5 g/10 min | (Condition L) ASTM D-1238 |
| Multibase Multi-Flex® TPE A 8502 BLK The fogging test value is 90% according to ASTM SAE-J275. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase. |
|||
| Melt Flow | 3.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
3.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Polimeri Europa Riblene® GM 20 Low Density Polyethylene - Coating Grade Riblene GM 20 is a medium fluidity low density polyethylene resin (LDPE).Main Applications: Riblene GM 20 is suitable for coating applications where a low neck-in is required. Moreover, for its rh.. |
|||
| Melt Flow | 3.5 g/10 min @Load 1.20 kg, Temperature 300 °C |
3.5 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| SABIC Innovative Plastics Lexan® 133 PC Nonhalogenated. 3.5 MFR. UV-stabilized. |
|||
| Melt Flow | 3.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
3.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| NOVA Chemicals Novapol® TD-9055-E Hexene LMDPE Film Resin Excellent stiffness and glossApplications: Diaper back sheet, BlendingAdditives: High temperature AOFilm properties are typical of cast film extruded at 280°C.Information provided by NOVA Chemicals.. |
|||
| Melt Flow | 3.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
3.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| NOVA Chemicals Novapol® TF-0338-E Hexene LMDPE Film Resin Excellent stiffness and glossApplications: Diaper back sheet, BlendingAdditives: High temperature AOFilm properties are typical of film extruded at 280°C.Information provided by NOVA Chemicals. |
|||
| Melt Flow | 3.5 g/10 min @Load 5.00 kg, Temperature 190 °C |
3.5 g/10 min @Load 11.0 lb, Temperature 374 °F |
Procedure A; ASTM D1238 |
| PolyOne Elastamax™ EG-9177 Thermoplastic Elastomer (TPE) The Elastamax™ EG 9100 Series is a new family of olefin-based TPE compounds offering outstanding elastomeric performance in a lightweight and easy to process material. The EG 9100 Series of compoun.. |
|||
| Melt Flow | 3.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
3.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Polimeri Europa Clearflex® H&T CMH 108 Octene Copolymer Linear Low Density Polyethylene Clearflex H&T CMH 108 is an octene copolymer linear low density polyethylene (C8-LLDPE), with antioxidants, suitable for cast film extrusion. Stretch films obtained from Clearflex H&T CMH 108 show e.. |
|||
| Melt Flow | 3.5 g/10 min | 3.5 g/10 min | ASTM D1238 |
| ExxonMobil LL 1235x70 Cast Film Resin
(discontinued **) LL 1235x70 is a butene LLDPE with improved stiffness. It can be used alone or as a component in packaging and industrial film.Information provided by ExxonMobil Chemical |
|||
| Melt Flow | 3.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
3.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
Condition E; ASTM D1238 |
| Formosa Plastics Formolene® L63935U Rotational Molding LLDPE
(discontinued **) Hexene CopolymerApplications: Tanks, toys and other non-tank rotational molding applicationsFormolene L63935U is fully heat and UV stabilized.Meets all requirements of the U.S. Food and Drug Adminis.. |
|||
| Melt Flow | 3.5 g/10 min | 3.5 g/10 min | ASTM D1238-62T |
| Chevron Phillips 4516 Extrusion Coating Resin
(discontinued **) Resin Type: HomopolymerCharacteristics: Good Processability, Good MVTR, Good Heat Seal, Kosher ApprovedApplications:Liquid Packaging, Cup Stock, Folding Carton, General CoatingData provided by Chevr.. |
|||
| Melt Flow | 3.5 g/10 min | 3.5 g/10 min | Cond. I; ASTM D1238 |
| Global ABS-1805 General Purpose ABS
(discontinued **) Information provided by Global Polymers Corporation. |
|||
| Melt Flow | 3.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
3.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| NOVA Chemicals Novapol® TR-0338-UI Hexene MDPE Rotational Molding Resin Excellent low temperature impact properties, Excellent ESCR, Good stiffness, Wide processing windowApplications: General purpose custom molding, Chemical containers, IBCs, Fish boxes, Septic tanks, .. |
|||
| Melt Flow | 3.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
3.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| NOVA Chemicals Novapol® TR-0338-UIG Hexene MDPE Rotational Molding Resin Excellent low temperature impact properties, Excellent ESCR, Good stiffness, Wide processing windowApplications: General purpose custom molding, Chemical containers, IBCs, Fish boxes, Septic tanks, .. |
|||
| Melt Flow | 3.5 g/10 min @Load 3.80 kg, Temperature 230 °C |
3.5 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
| LG Chemical LUPOS GP2206F ABS+GF20%, Flame Retardant Feature: Injection Molding, ABS+GF20%, Flame RetardantApplication: Electric & Electronic (Housing, Components)CAS No. 9003-56-9, 9003-54-7, 65997-17-3, 88497-56-7 and 1309-64-4Information provided b.. |
|||
| Melt Flow | 3.5 g/10 min @Load 5.00 kg, Temperature 200 °C |
3.5 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Ineos Nova FX530 Impact Polystyrene Features: Excellent environmental stress crack resistanceExcellent Izod impact strengthUL Classification 94 HBBalanced physical propertiesApplications: ExtrusionThermoformingSelected injection moldi.. |
|||
| Melt Flow | 3.5 g/10 min @Load 2.16 kg, Temperature 230 °C |
3.5 g/10 min @Load 4.76 lb, Temperature 446 °F |
Condition L; ASTM D1238 |
| LyondellBasell Pro-faxâ„¢ PH350 Polypropylene Homopolymer Description: Pro-faxâ„¢ PH350 general purpose polypropylene homopolymer resin is available as natural flake. Flake form resin is well suited for mixing with pigments and other additives to make p.. |
|||
| Melt Flow | 3.5 g/10 min @Load 5.00 kg, Temperature 200 °C |
3.5 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Samsung Cheil Industries Starex® AS-0151BS ABS, Unreinforced Anti-static material that can be used in the housing of OA devices, IC, LSI carrier etc.Information provided by Samsung Cheil Industries. |
|||
| Melt Flow | 3.5 g/10 min @Load 10.0 kg, Temperature 220 °C |
3.5 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Samsung Cheil Industries Starex® MG-0330 ABS, Unreinforced Heat Resistant Information provided by Samsung Cheil Industries. |
|||
| Melt Flow | 3.5 g/10 min @Load 10.0 kg, Temperature 220 °C |
3.5 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Samsung Cheil Industries Starex® SR-0320BM ABS, Unreinforced Heat Resistant Information provided by Samsung Cheil Industries. |
|||
| Melt Flow | 3.5 g/10 min @Load 5.00 kg, Temperature 200 °C |
3.5 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Samsung Cheil Industries Starex® NH-0700FX ABS, Unreinforced FR Information provided by Samsung Cheil Industries. |
|||
| Melt Flow | 3.5 g/10 min @Load 10.0 kg, Temperature 220 °C |
3.5 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Samsung Cheil Industries Starex® SR-0320BM ABS, Unreinforced Heat Resistant Information provided by Samsung Cheil Industries. |
|||
| Melt Flow | 3.5 g/10 min @Load 2.16 kg, Temperature 230 °C |
3.5 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| SCG Chemicals EL-Proâ„¢ P403J Polypropylene Injection Molding Key Characteristics:High stiffnessHigh glossGood processabilityOdorlessSafe for food contactRecommended Applications:General purpose housewaresFood containersMedical instrumentsInfant articles, toys.. |
|||
| Melt Flow | 3.5 g/10 min | 3.5 g/10 min | Exxon Method |
| ExxonMobil EXACT™ 4150 Plastomer Product Description: Exact 4150 is an ethylene-based hexane plastomer produced using ExxonMobil Chemical’s EXXPOL® Catalyst Technology. Exact 4150 is designed for multilayer coextruded cast film a.. |
|||
| Melt Flow | 3.5 g/10 min @Load 2.16 kg |
3.5 g/10 min @Load 4.76 lb |
Melt flow ratio I10/I2 is 8.5. |
| Dow AFFINITY™ PL 1845 Polyolefin Plastomer Film properties below based on a film thickness of 25 µm. Data provided by Dow Chemical. |
|||
| Melt Flow | 3.5 g/10 min @Load 2.16 kg, Temperature 230 °C |
3.5 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| ExxonMobil PP2252E1 Homopolymer Product Description: Medium melt flow rate homopolymer designed for high speed extrusion of woven fabrics exhibiting low water carry over.Availability: North America Features:Balanced Stiffness/To.. |
|||
| Melt Flow | 3.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
3.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Barlog Plastics KEBAFORM C 904 CF POM Copolymer, carbon fiber reinforced, electr. conductive POM-CF20Information provided by BARLOG plastics GmbH. |
|||
| Melt Flow | 3.5 g/10 min @Load 5.00 kg, Temperature 200 °C |
3.5 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Americas Styrenics STYRON® 693 High Heat Crystal Polystyrene Product CharacteristicsHigh heat resistanceHigh tensile strengthHigh stiffnessFood Contact CompliantUL Classification 94 HBTypical ApplicationsPackaging/Foam disposablesConsumer electronicsInformati.. |
|||
| Melt Flow | 3.5 g/10 min | 3.5 g/10 min | Condition G |
| Ineos Nova 5420 High Impact Polystyrene
(discontinued **) High impact, Good environmental stress crack resistance, USP Class VIApplications: Thermoformed containers and lids, Hot and cold beverage cups, Custom sheetProperties were determined on injection m.. |
|||
| Melt Flow | 3.5 g/10 min | 3.5 g/10 min | Condition G |
| Ineos Nova 1301 High Heat Crystal Polystyrene High heat resistance, High strength, Good processing characteristics, USP Class VIApplications: Electronics packaging, Medical packaging, Cosmetic cases, Profile extrusionExposure to gamma radiation.. |
|||
| Melt Flow | 3.5 g/10 min @Load 2.16 kg, Temperature 230 °C |
3.5 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Braskem H 501HC Thermoforming Polypropylene Homopolymer High-stiffness thermoformed parts.Information provided by Braskem. |
|||