Formosa Plastics Formolene® L63935U Rotational Molding LLDPE (discontinued **)

Category	Polymer , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Rotational Molding Grade
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Formosa Plastics Formolene® L63935U Rotational Molding LLDPE (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Hexene CopolymerApplications: Tanks, toys and other non-tank rotational molding applicationsFormolene L63935U is fully heat and UV stabilized.Meets all requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520, covering safe use of polyolefin articles intended for direct food contact.Information provided by Formosa Plastics Corporation, USA.

Physical Properties	Metric	English	Comments
Density	0.939 g/cc	0.0339 lb/in³	ASTM D1505
Environmental Stress Crack Resistance	400 hour	400 hour	(10% Igepal), F<sub>50</sub>; ASTM D1693
	>= 1000 hour	>= 1000 hour	(100% Igepal), F<sub>50</sub>; ASTM D1693
Melt Flow	3.5 g/10 min @Load 2.16 kg, Temperature 190 °C	3.5 g/10 min @Load 4.76 lb, Temperature 374 °F	Condition E; ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	22.8 MPa	3300 psi	2" (50mm) per min.; ASTM D638
Elongation at Yield	11.3 %	11.3 %	2" (50mm) per min.; ASTM D638
Flexural Modulus	0.758 GPa	110 ksi	1.3mm per min; ASTM D790
Dynatup @ -30°C	81.3 J @Thickness 3.17 mm	60.0 ft-lb @Thickness 0.125 in	ARM Std. Low Temp Impact; ARM Std.

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	54.0 °C	129 °F	ASTM D648