Samsung Cheil Industries Starex® MG-0330 ABS, Unreinforced Heat Resistant
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® MG-0330 ABS, Unreinforced Heat Resistant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.07 g/cc | 1.07 g/cc | ASTM D792 |
| Water Absorption | 0.30 % @Temperature 23.0 °C |
0.30 % @Temperature 73.4 °F |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0060 in/in @Thickness 0.126 in |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm @Thickness 3.20 mm |
0.0060 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 3.5 g/10 min @Load 10.0 kg, Temperature 220 °C |
3.5 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 111 | 111 | ASTM D785 |
| Tensile Strength, Yield | 43.1 MPa | 6260 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 15 % | 15 % | 5 mm/min; ASTM D638 |
| Flexural Strength | 61.8 MPa | 8960 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 2.16 GPa | 313 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 1.37 J/cm @Thickness 6.35 mm |
2.57 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 116 °C | 241 °F | B/50; ISO R306 |
Users viewing this material also viewed the following:
- Polycasa XT PMMA
- Ineos Nova Zylar® 220 Clear Impact Modified Acrylic Copolymer (discontinued **)
- LG Chemical Lupox® GP-1006F General Purpose PBT, Unreinforced, Flame Retardant, Non-Bleed
- LyondellBasell Hifaxâ„¢ CA138A Thermoplastic Polyolefin Elastomer
- A. Schulman POLYBLAK™ 2723Pm Premium Black Color Concentrate, 25% Carbon Black Based In HDPE
- Hexcel® HexWeb® CR-PAA™ 3/8-5056-0.001 Phosphoric Acid Anodized Aluminum Honeycomb
- ChevronTexaco HiPerSYN™ ISO 320 Oil
- Ceradyne Ceralloy® 1370CS AlN
- Aptek 2312-PMF Electrically conductive, low modulus adhesive
- 3M 8427-16 Cold Shrink Connector Insulators
Copyright © lookpolymers.com All Rights Reserved