Physical Properties | Metric | English | Comments |
---|---|---|---|
Linear Mold Shrinkage | 0.011 cm/cm @Thickness 3.20 mm |
0.011 in/in @Thickness 0.126 in |
Transverse; DAM |
DuPont Performance Polymers Zytel® HTN 51G15HSL BK083 Polyphthalamide (PPA)
(Unverified Data**) Zytel® HTN51G15HSL BK083 is a 15% glass reinforced, heat stabilized, lubricated high performance polyamide resin. It is also a PPA resin.Information provided by DuPont Performance Polymers |
|||
Linear Mold Shrinkage | 0.011 cm/cm @Thickness 3.20 mm |
0.011 in/in @Thickness 0.126 in |
Transverse; DAM |
DuPont Performance Polymers Zytel® 151 NC010 Nylon 612
(Unverified Data**) Zytel® 151 NC010 is a PA 612 resin.Information provided by DuPont Performance Polymers |
|||
Linear Mold Shrinkage | 0.011 cm/cm @Thickness 6.40 mm |
0.011 in/in @Thickness 0.252 in |
Transverse; DAM |
DuPont Performance Polymers Zytel® 77G33L BK031 Nylon 612
(Unverified Data**) Zytel® 77G33L BK031 is a 33% glass fiber reinforced, black polyamide 612 resin for injection molding.Information provided by DuPont Performance Polymers |
|||
Linear Mold Shrinkage | 0.011 cm/cm @Thickness 6.35 mm |
0.011 in/in @Thickness 0.250 in |
ASTM D955 |
Fiberfil® PP-60/CC/40 Polypropylene Homopolymer, 40% Calcium Carbonate Information provided by FIBERFIL Engineered Plastics |
|||
Linear Mold Shrinkage | 0.011 cm/cm @Thickness 3.17 mm |
0.011 in/in @Thickness 0.125 in |
ASTM D955 |
Fiberfil® PP-60/CC/40 Polypropylene Homopolymer, 40% Calcium Carbonate Information provided by FIBERFIL Engineered Plastics |
|||
Linear Mold Shrinkage | 0.011 - 0.012 cm/cm @Thickness 6.35 mm |
0.011 - 0.012 in/in @Thickness 0.250 in |
ASTM D955 |
Fiberfil® PP-60/TC/24/D/HS Polypropylene Homopolymer, Talc Filled, Heat Stabilized Information provided by FIBERFIL Engineered Plastics |
|||
Linear Mold Shrinkage | 0.011 cm/cm @Thickness 6.35 mm |
0.011 in/in @Thickness 0.250 in |
ASTM D955 |
Fiberfil® PP-60/TC/30 Polypropylene Homopolymer, 30% Talc Filled Information provided by FIBERFIL Engineered Plastics |
|||
Linear Mold Shrinkage | 0.011 - 0.014 cm/cm @Thickness 3.17 mm |
0.011 - 0.014 in/in @Thickness 0.125 in |
ASTM D955 |
Fiberfil® PP-62/MI/25 Polypropylene Copolymer, 25% Mica Reinforced Information provided by FIBERFIL Engineered Plastics |
|||
Linear Mold Shrinkage | 0.011 cm/cm @Thickness 6.35 mm |
0.011 in/in @Thickness 0.250 in |
ASTM D955 |
Fiberfil® PP-60/CC/30 Polypropylene Homopolymer, 30% Calcium Carbonate Information provided by FIBERFIL Engineered Plastics |
|||
Linear Mold Shrinkage | 0.011 cm/cm @Thickness 3.17 mm |
0.011 in/in @Thickness 0.125 in |
ASTM D955 |
Fiberfil® PP-60/CC/30 Polypropylene Homopolymer, 30% Calcium Carbonate Information provided by FIBERFIL Engineered Plastics |
|||
Linear Mold Shrinkage | 0.011 - 0.016 cm/cm @Thickness 3.20 mm |
0.011 - 0.016 in/in @Thickness 0.126 in |
48 hr, at 121°C; ASTM D955 |
A. Schulman POLYPUR™ FPU 1109 Thermoplastic Polyurethane Compound Information provided by A. Schulman. |
|||
Linear Mold Shrinkage | 0.011 - 0.016 cm/cm @Thickness 3.20 mm |
0.011 - 0.016 in/in @Thickness 0.126 in |
48 hr, at 121°C; ASTM D955 |
A. Schulman POLYPUR™ FPU 1112 Thermoplastic Polyurethane Compound (15% Glass) Information provided by A. Schulman. |
|||
Linear Mold Shrinkage | 0.011 - 0.016 cm/cm @Thickness 3.20 mm |
0.011 - 0.016 in/in @Thickness 0.126 in |
48 hr, at 121°C; ASTM D955 |
A. Schulman POLYPUR™ FPU 1109 Thermoplastic Polyurethane Compound Information provided by A. Schulman. |
|||
Linear Mold Shrinkage | 0.011 - 0.015 cm/cm @Thickness 3.20 mm |
0.011 - 0.015 in/in @Thickness 0.126 in |
aged 48 hrs at 121°C; ISO 294 |
A. Schulman FORMION™ FI 389 Ionomer Information provided by A. Schulman. |
|||
Linear Mold Shrinkage | 0.011 - 0.016 cm/cm @Thickness 3.20 mm |
0.011 - 0.016 in/in @Thickness 0.126 in |
48 hr, at 121°C; ASTM D955 |
A. Schulman POLYPUR™ FPU 1109 Thermoplastic Polyurethane Compound Information provided by A. Schulman. |
|||
Linear Mold Shrinkage | 0.011 - 0.016 cm/cm @Thickness 3.20 mm |
0.011 - 0.016 in/in @Thickness 0.126 in |
48 hr, at 121°C; ASTM D955 |
A. Schulman POLYPUR™ FPU 1109 Thermoplastic Polyurethane Compound Information provided by A. Schulman. |
|||
Linear Mold Shrinkage | 0.011 - 0.015 cm/cm @Thickness 3.20 mm |
0.011 - 0.015 in/in @Thickness 0.126 in |
aged 48 hrs at 121°C; ISO 294 |
A. Schulman FORMION™ FI 389 Ionomer Information provided by A. Schulman. |
|||
Linear Mold Shrinkage | 0.011 - 0.015 cm/cm @Thickness 3.20 mm |
0.011 - 0.015 in/in @Thickness 0.126 in |
aged 48 hrs at 121°C; ISO 294 |
A. Schulman FORMION™ FI 389 Ionomer Information provided by A. Schulman. |
|||
Linear Mold Shrinkage | 0.011 - 0.016 cm/cm @Thickness 3.20 mm |
0.011 - 0.016 in/in @Thickness 0.126 in |
48 hr, at 121°C; ASTM D955 |
A. Schulman POLYPUR™ FPU 1112 Thermoplastic Polyurethane Compound (15% Glass) Information provided by A. Schulman. |
|||
Linear Mold Shrinkage | 0.011 - 0.016 cm/cm @Thickness 3.20 mm |
0.011 - 0.016 in/in @Thickness 0.126 in |
48 hr, at 121°C; ASTM D955 |
A. Schulman POLYPUR™ FPU 1109 Thermoplastic Polyurethane Compound Information provided by A. Schulman. |
|||
Linear Mold Shrinkage | 0.011 cm/cm @Thickness 3.20 mm |
0.011 in/in @Thickness 0.126 in |
Flow; DAM |
DuPont Performance Polymers Zytel® FR7025V0F NC010 Nylon 66
(Unverified Data**) Zytel® FR7025V0F NC010 is a flame retardant polyamide 66 resin for injection molding. It does not contain elemental phosphorous, halogens or heavy metals.Information provided by DuPont Performance.. |
|||
Linear Mold Shrinkage | 0.011 cm/cm @Thickness 1.60 mm |
0.011 in/in @Thickness 0.0630 in |
Transverse; DAM |
DuPont Performance Polymers Zytel® FR70G25V0 NC010 Nylon 66
(Unverified Data**) Zytel® FR70G25V0 NC010 is a 25% glass fiber reinforced, heat stabilized, flame retardant polyamide 66 resin for injection molding.Information provided by DuPont Performance Polymers |
|||
Linear Mold Shrinkage | 0.011 cm/cm @Thickness 3.20 mm |
0.011 in/in @Thickness 0.126 in |
Transverse; DAM |
DuPont Performance Polymers Zytel® FR70G25V0 NC010 Nylon 66
(Unverified Data**) Zytel® FR70G25V0 NC010 is a 25% glass fiber reinforced, heat stabilized, flame retardant polyamide 66 resin for injection molding.Information provided by DuPont Performance Polymers |
|||
Linear Mold Shrinkage | 0.011 cm/cm @Thickness 3.20 mm |
0.011 in/in @Thickness 0.126 in |
Transverse; DAM |
DuPont Performance Polymers Zytel® FE3734 NC010 Nylon 612
(Unverified Data**) Zytel® FE3734 NC010 is an unreinforced, lubricated polyamide 612 resin suitable for injection molding.Information provided by DuPont Performance Polymers |
|||
Linear Mold Shrinkage | 0.011 - 0.015 cm/cm @Thickness 3.20 mm |
0.011 - 0.015 in/in @Thickness 0.126 in |
aged 48 hrs at 121°C; ISO 294 |
A. Schulman FORMION™ FI 389 Ionomer Information provided by A. Schulman. |