- Fiberfil® PP-60/TC/30 Polypropylene Homopolymer, 30% Talc Filled
Fiberfil® PP-60/TC/30 Polypropylene Homopolymer, 30% Talc Filled
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | FiberFil |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Fiberfil® PP-60/TC/30 Polypropylene Homopolymer, 30% Talc Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by FIBERFIL Engineered Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.15 g/cc | 1.15 g/cc | ASTM D792 |
| Water Absorption | 0.030 % | 0.030 % | 24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.0090 cm/cm @Thickness 3.17 mm |
0.0090 in/in @Thickness 0.125 in |
ASTM D955 |
| 0.011 cm/cm @Thickness 6.35 mm |
0.011 in/in @Thickness 0.250 in |
ASTM D955 | |
| Melt Flow | 10 g/10 min | 10 g/10 min | 230/2.16 (typical); ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 90 - 95 | 90 - 95 | ASTM D785 |
| Tensile Strength, Yield | 33.1 MPa | 4800 psi | ASTM D638 |
| Elongation at Yield | 15 % | 15 % | ASTM D638 |
| Tensile Modulus | 2.96 GPa | 430 ksi | ASTM D638 |
| Flexural Strength | 48.3 MPa | 7000 psi | ASTM D790 |
| Flexural Modulus | 2.76 GPa | 400 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 0.267 J/cm @Thickness 3.17 mm |
0.500 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 132 °C | 270 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ASTM D648 |
Users viewing this material also viewed the following:
- Plaskolite Optix® CA - 75 HID General Purpose Acrylic Resin
- Resin Technology Group Fusion 85 Low Viscosity Methyl Fusion Cyanoacrylate
- 3M Dyneon™ CC191-HE Custom Fluoropolymer Compound (discontinued **)
- Overview of materials for Nylon 612, Impact Modified
- Silberline Sil-O-Wet® 270NL-PA
- Schmolz + Bickenbach UGICHROM 4028 Martensitic Chrome Plated Bar
- ExxonMobil Exxon Hyjet V
- 3M 914 Repulpable Forms-Splicing Tape
- BASF Lupranate® 281 Isocyanate
Copyright © lookpolymers.com All Rights Reserved