TIMET TIMETAL® 5111 Titanium Alloy (Ti-5Al-1Sn-1Zr-1V-0.8Mo; ASTM Grade 32)
| Category | Metal , Nonferrous Metal , Titanium Alloy , Alpha/Near Alpha Titanium Alloy |
| Manufacturer | TIMET |
| Trade Name | TIMETAL® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | TIMET TIMETAL® 5111 Titanium Alloy (Ti-5Al-1Sn-1Zr-1V-0.8Mo; ASTM Grade 32).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High Toughness, Heavy Section Weldable AlloyFeatures: A near alpha alloy with excellent weldability, seawater stress corrosion cracking resistance and high dynamic toughness. It is ideally suited for applications in marine environments where toughness and corrosion resistance are essential. The alloy has been produced on a commercial scale. It was developed jointly with the Navy, and has been selected as the material of choice for a submarine application.Data provided by TIMET.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 4.43 g/cc | 0.160 lb/in³ | Typical |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 862 MPa | 125000 psi | Typical |
| Tensile Strength, Yield | 758 MPa @Strain 0.200 % |
110000 psi @Strain 0.200 % |
Typical |
| Elongation at Break | 15 % | 15 % | Typical |
| Reduction of Area | 30 % | 30 % | |
| Modulus of Elasticity | 107 - 114 GPa | 15500 - 16500 ksi | Typical |
| Bend Radius, Minimum | 5.0 t | 5.0 t | Typical; on 0.078 in (2 mm) sheet |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 8.20 µm/m-°C @Temperature 50.0 °C |
4.56 µin/in-°F @Temperature 122 °F |
|
| 9.30 µm/m-°C @Temperature 250 °C |
5.17 µin/in-°F @Temperature 482 °F |
||
| Specific Heat Capacity | 0.533 J/g-°C | 0.127 BTU/lb-°F | |
| Thermal Conductivity | 7.50 W/m-K | 52.0 BTU-in/hr-ft²-°F | |
| Beta Transus | 980 °C | 1800 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Aluminum, Al | 4.5 - 5.5 % | 4.5 - 5.5 % | |
| Carbon, C | <= 0.080 % | <= 0.080 % | |
| Hydrogen, H | <= 0.015 % | <= 0.015 % | |
| Iron, Fe | <= 0.25 % | <= 0.25 % | |
| Molybdenum, Mo | 0.60 - 1.2 % | 0.60 - 1.2 % | |
| Nitrogen, N | <= 0.030 % | <= 0.030 % | |
| Oxygen, O | <= 0.11 % | <= 0.11 % | |
| Silicon, Si | 0.060 - 0.14 % | 0.060 - 0.14 % | |
| Tin, Sn | 0.60 - 1.4 % | 0.60 - 1.4 % | |
| Titanium, Ti | 88.5 - 93 % | 88.5 - 93 % | Calculated as remainder |
| Vanadium, V | 0.60 - 1.4 % | 0.60 - 1.4 % | |
| Zirconium, Zr | 0.60 - 1.4 % | 0.60 - 1.4 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.000153 ohm-cm | 0.000153 ohm-cm |