- Sharadaa Ceramics VELECRETE RC 101 Rodding Castables
Sharadaa Ceramics VELECRETE RC 101 Rodding Castables
| Category | Ceramic |
| Manufacturer | Sharadaa Ceramics |
| Trade Name | VELECRETE |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sharadaa Ceramics VELECRETE RC 101 Rodding Castables.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: The Rodding Castables offered by us are user friendly in nature and does not require high energy mixing machines and vibrators. Free flowing in nature, these castables are designed in compliance with international standards.Bond: UltrafineAggregate: Cal. ClayType of Setting: HydraulicInformation provided by Sharadaa Ceramics Pvt. Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 2.30 g/cc | 0.0831 lb/in³ | After Drying at 110°C |
| Porosity | 16 % @Temperature 1300 °C |
16 % @Temperature 2370 °F |
|
| Grain Size | <= 10000 µm | <= 10000 µm |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Rupture | 0.0150 GPa @Temperature 1100 °C |
2.18 ksi @Temperature 2010 °F |
Hot |
| 0.0150 GPa @Temperature 1000 °C |
2.18 ksi @Temperature 1830 °F |
Cold | |
| 0.0200 GPa @Temperature 110 °C |
2.90 ksi @Temperature 230 °F |
Cold | |
| 0.0200 GPa @Temperature 1400 °C |
2.90 ksi @Temperature 2550 °F |
Cold | |
| Compressive Strength | 60.0 MPa @Temperature 1000 °C |
8700 psi @Temperature 1830 °F |
Cold Crushing |
| 80.0 MPa @Temperature 110 °C |
11600 psi @Temperature 230 °F |
Cold Crushing | |
| 80.0 MPa @Temperature 1400 °C |
11600 psi @Temperature 2550 °F |
Cold Crushing |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 1.16 W/m-K @Temperature 600 °C |
8.05 BTU-in/hr-ft²-°F @Temperature 1110 °F |
Hot Face |
| Maximum Service Temperature, Air | 1600 °C | 2910 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | 46 % | 46 % | |
| Fe2O3 | 4.0 % | 4.0 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Permanent Linear Change | <-0.9% | 1600°C |
| Thermal Expansion | 0.9 | at 1100°C |
| Thermal Shock Resistance | Excellent |