SABIC Innovative Plastics Lexan® FXD104R PC (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® FXD104R PC (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
FXD104R is a Light Diffusion effect, which is part of the VisualFX family. Color Package may affect properties.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D 792
Density 1.20 g/cc
0.0434 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.15 %
0.15 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.35 %

@Temperature 23.0 °C
0.35 %

@Temperature 73.4 °F
ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0070 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 6.0 g/10 min

@Load 5.00 kg,
Temperature 220 °C
6.0 g/10 min

@Load 11.0 lb,
Temperature 428 °F
[cm^3/10 min] Melt Volume Rate; ISO 1133
7.0 g/10 min

@Load 3.80 kg,
Temperature 200 °C
7.0 g/10 min

@Load 8.38 lb,
Temperature 392 °F
ASTM D 1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 69.0 MPa
10000 psi
Type I, 50 mm/min; ASTM D 638
70.0 MPa
10200 psi
50 mm/min; ISO 527
Tensile Strength, Yield 62.0 MPa
8990 psi
Type I, 50 mm/min; ASTM D 638
63.0 MPa
9140 psi
50 mm/min; ISO 527
Elongation at Break 115 %
115 %
Type I, 50 mm/min; ASTM D 638
120 %
120 %
50 mm/min; ISO 527
Elongation at Yield 6.0 %
6.0 %
50 mm/min; ISO 527
7.0 %
7.0 %
Type I, 50 mm/min; ASTM D 638
Tensile Modulus 2.30 GPa
334 ksi
5 mm/min; ASTM D 638
2.35 GPa
341 ksi
1 mm/min; ISO 527
Flexural Yield Strength 90.0 MPa
13100 psi
2 mm/min; ISO 178
94.0 MPa
13600 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 2.30 GPa
334 ksi
2 mm/min; ISO 178
2.37 GPa
344 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 1.40 J/cm

@Temperature -30.0 °C
2.62 ft-lb/in

@Temperature -22.0 °F
ASTM D 256
9.02 J/cm

@Temperature 23.0 °C
16.9 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Notched (ISO) 12.0 kJ/m²

@Temperature -30.0 °C
5.71 ft-lb/in²

@Temperature -22.0 °F
80*10*3; ISO 180/1A
70.0 kJ/m²

@Temperature 23.0 °C
33.3 ft-lb/in²

@Temperature 73.4 °F
80*10*3; ISO 180/1A
Izod Impact, Unnotched (ISO) NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
80*10*3; ISO 180/1U
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
80*10*3; ISO 180/1U
Charpy Impact Unnotched NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eU
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eU
Charpy Impact, Notched 1.50 J/cm²

@Temperature -30.0 °C
7.14 ft-lb/in²

@Temperature -22.0 °F
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA
7.50 J/cm²

@Temperature 23.0 °C
35.7 ft-lb/in²

@Temperature 73.4 °F
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA
Impact Test 63.0 J

@Temperature 23.0 °C
46.5 ft-lb

@Temperature 73.4 °F
Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 69.7 µm/m-°C

@Temperature -40.0 - 40.0 °C
38.7 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
71.1 µm/m-°C

@Temperature -40.0 - 40.0 °C
39.5 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 70.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
38.9 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
71.9 µm/m-°C

@Temperature -40.0 - 40.0 °C
39.9 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 127 °C
261 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
126 °C

@Thickness 3.20 mm
259 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Vicat Softening Point 144 °C
291 °F
Rate B/50; ISO 306
145 °C
293 °F
Rate B/120; ISO 306
154 °C
309 °F
Rate B/50; ASTM D 1525