SABIC Innovative Plastics LNP Thermocomp MF0069S PP (Asia Pacific)

Category Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Thermocomp MF0069S PP (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Thermocomp* MF0069S is a compound based on Polypropylene resin containing Glass Fiber, Flame Retardant. Added features of this material include: Chemically Coupled, Flame Retardant, Heat Stabilized.This data was supplied by SABIC-IP for the Asia Pacific region.
Physical Properties Metric English Comments
Density 1.46 g/cc
0.0527 lb/in³
ASTM D 792
Linear Mold Shrinkage, Flow 0.0060 cm/cm

@Time 86400 sec
0.0060 in/in

@Time 24.0 hour
ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 71.0 MPa
10300 psi
ASTM D 638
Elongation at Break 1.8 %
1.8 %
ASTM D 638
Tensile Modulus 9.30 GPa
1350 ksi
50 mm/min; ASTM D 638
Flexural Strength 117 MPa
17000 psi
ASTM D 790
Flexural Modulus 8.12 GPa
1180 ksi
ASTM D 790
Izod Impact, Notched 0.740 J/cm

@Temperature 23.0 °C
1.39 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Unnotched 4.66 J/cm

@Temperature 23.0 °C
8.73 ft-lb/in

@Temperature 73.4 °F
ASTM D 4812
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 146 °C

@Thickness 3.20 mm
295 °F

@Thickness 0.126 in
unannealed; ASTM D 648