Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 8.14 GPa | 1180 ksi | ASTM D790 |
Omni Plastics OmniTech™ ABS GRC30 NA Glass Reinforced OmniTech™ is a family of non-standard products custom developed for applications with unique functional requirements, including but not limited to: Flame Retardant, Conductive, Wear Resistant, and .. |
|||
Flexural Modulus | 8.15 GPa | 1180 ksi | ISO 178 |
Radici Radilon® CARV300 L (dry) Copolyamide 66/6 Glass-fiber reinforcedInformation provided by Radici group. |
|||
Flexural Modulus | 8.14 GPa | 1180 ksi | ASTM D790 |
Polymer Resources PPX/NY G30 PPO/Nylon 66 Alloy , 30% Glass Reinforced Polyphenylene Oxide/Nylon 66 Alloy , 30% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Informa.. |
|||
Flexural Modulus | 8.16 GPa | 1180 ksi | ISO 178 |
SABIC Innovative Plastics LNP KONDUIT MT00E PP LNP KONDUIT* MT00E is a compound based on Polypropylene resin containing 70% Proprietary Thermal Filler. Added features of this material include: Thermally Conductive. |
|||
Flexural Modulus | 8.16 GPa | 1180 ksi | ISO 178 |
SABIC Innovative Plastics LNP KONDUIT MT00E PP (Asia Pacific) LNP KONDUIT* MT00E is a compound based on Polypropylene resin containing Proprietary Thermal Filler. Added features of this material include: Thermally Conductive. |
|||
Flexural Modulus | 8.16 GPa | 1180 ksi | ISO 178 |
SABIC Innovative Plastics LNP KONDUIT MT00E PP (Europe-Africa-Middle East) LNP KONDUIT* MT00E is a compound based on Polypropylene resin containing Proprietary Thermal Filler. Added features of this material include: Thermally Conductive. |
|||
Flexural Modulus | 8.14 GPa | 1180 ksi | (50.8 mm Span) 1mm/min; ASTM D790 |
LNP ULTEM® UCF1205 Polyetherimide, 12% Carbon Fiber Reinforcement, 5% PTFE Lubricant
(discontinued **) Office equipment internal parts.Features: Lubricated, Good Wear ResistanceForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labe.. |
|||
Flexural Modulus | 8.16 - 10.4 GPa | 1180 - 1510 ksi | Average value: 9.12 GPa Grade Count:10 |
Overview of materials for Phenolic, Novolac, Heat Resistant Grade, Filled This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Novolac, Heat Resistant Grade, Filled". Each property range of values reported is minimum and .. |
|||
Flexural Modulus | 8.16 GPa | 1180 ksi | ASTM D790 |
Plenco 4246 Phenolic, Granular, Injection Molded
(discontinued **) Two-stage Phenolic. PLENCO 04246 flow 18 is a black two-stage, medium heat resistant phenolic molding compound. It has excellent electrical, moldability and molded finish characteristics. It is use.. |
|||
Flexural Modulus | 8.11 GPa | 1180 ksi | ASTM D 790 |
SABIC Innovative Plastics Valox® 507 PBT+PC (Asia Pacific) This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Flexural Modulus | 8.13 GPa | 1180 ksi | ASTM D790 |
SABIC Innovative Plastics LNP STAT-KON DX09315C PC (Asia Pacific) LNP* Stat-Kon* DX09315C is carbon fiber filled polycarbonate composite with good flow ability, and high level of cleanliness for the most demanding application. A unique feature of this material is .. |
|||
Flexural Modulus | 8.17 GPa | 1180 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP STAT-KON RFD04 PA 66 LNP STAT-KON* RFD04 is a compound based on Nylon 66 resin containing 20% Glass Fiber. Added features of this material include: Electrically Conductive. |
|||
Flexural Modulus | 8.12 GPa | 1180 ksi | ASTM D 790 |
SABIC Innovative Plastics LNP Thermocomp MF0069S PP (Asia Pacific) LNP* Thermocomp* MF0069S is a compound based on Polypropylene resin containing Glass Fiber, Flame Retardant. Added features of this material include: Chemically Coupled, Flame Retardant, Heat Stabi.. |
|||
Flexural Modulus | 8.14 GPa | 1180 ksi | ASTM D790 |
Samyang Tramid® 910 PA66/PA6 Strong with excellent thermal resistance. Abrasion resistance, chemical resistance and oil resistance are excellent.Applications:Automotive knob types, door handles and mirror housingsConnectorsCab.. |
|||
Flexural Modulus | 8.16 GPa | 1180 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP RF0049SP PA 66 LNP* THERMOCOMP* RF0049SP is a compound based on Nylon 66 containing 20% Glass Fiber. Added features of this grade include: Flame Retardant, Heat Stabilized. |
|||
Flexural Modulus | 8.15 GPa | 1180 ksi | ASTM D790 |
SABIC Innovative Plastics NORYL GTX CRN530 PPE+PA6 (Asia Pacific) 30%GF GTX grade for Non Auto market |
|||
Flexural Modulus | 8.13 GPa | 1180 ksi | ASTM D 790 |
SABIC Innovative Plastics Noryl GTX GTX880 PPE+PA6 (Asia Pacific) This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Flexural Modulus | 8.13 GPa | 1180 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics NORYL GTX RNX130 PPE+PS+PA 30% glass reinforced PPE+PS+PA alloy for automotive and nonautomotive applications. Recycle grade in black/gray only. |
|||
Flexural Modulus | 8.16 GPa | 1180 ksi | ISO 178 |
SABIC Innovative Plastics LNP Stat-kon DX96690 PC LNP STAT-KON* DX96690 is a compound based on Polycarbonate resin containing PTFE. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for the America.. |
|||
Flexural Modulus | 8.14 GPa | 1180 ksi | ASTM D790 |
Techmer ES HiFill® PA6 0325 Availability: North AmericaForms: PelletsFiller/Reinforcement: Unspecified Filler/ReinforFeatures: High Specific GravityTPC# 6066102Information provided by TP Composites, Inc. |
|||
Flexural Modulus | 8.14 GPa | 1180 ksi | ASTM Value |
BASF Capron® 8333G HI HS BK-102 Impact Modified, 33% Glass-Filled Nylon 6 (Dry)
(discontinued **) Capron 8333G HI HS BK-102 is a 33% glass reinforced, impact modified polyamide 6 injection molding compound pigmented black developed for applications requiring improved dry as molded toughness in c.. |
|||
Flexural Modulus | 8.14 GPa | 1180 ksi | ASTM Data |
BASF Capron® SEG6 H1 BK-122 30% Glass-Filled Nylon 6 (Dry)
(discontinued **) Capron SEG6 H1 BK-122 is a black pigmented, 30% glass reinforced nylon 6 injection molding compound. This material is currently under development as XA-2678. It exhibits exceptional surface aesthet.. |
|||
Flexural Modulus | 8.15 GPa @Temperature 90.0 °C |
1180 ksi @Temperature 194 °F |
ASTM D790 |
LATI LASULF G/30 30% Glass Reinforced Polysulfone (PSU)
(Unverified Data**) Description: Lasulf products are composed of polysulfone (PSU). They feature good thermal and mechanical properties such as excellent toughness, even at low temperatures, excellent dimensional stabi.. |
|||
Flexural Modulus | 8.14 GPa | 1180 ksi | 2.8mm/min; ASTM D790 |
Asia International Enterprise (Hong Kong) 30G6F Polybutylene terephthalate, 30% Glass Fiber Filled Information provided by Asia International Enterprise (Hong Kong) Ltd. |
|||
Flexural Modulus | 8.14 GPa | 1180 ksi | ASTM Test |
BASF Ultramid® 8333G HI HS BK-102 33% Glass Filled PA6 (Dry) Ultramid 8333G HI HS BK-102 is a 33% glass reinforced, heat stabilized, impact modified, pigmented black, PA6 injection molding compound developed for applications requiring improved dry as molded t.. |
|||
Flexural Modulus | 8.14 GPa | 1180 ksi | ASTM D790 |
Polymer Resources PPX/NY G30 Modified PPO, 30% Glass Reinforced PPX/Nylon 6,6 Alloy
(Unverified Data**)&l Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||
Flexural Modulus | 8.14 GPa | 1180 ksi | ASTM D790 |
PlastxWorld CEVIAN® S5230 30% GF PC/ABS alloy Glass fiber reinforced and flame retarded PC/ABS alloy.These are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by PlastxWorld .. |
|||
Flexural Modulus | 8.12 GPa | 1180 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics NORYL FE1630PW PPE+PS (Europe-Africa-Middle East) Noryl* FE1630PW Polyphenylene Oxide (PPO) + Polystyrene (PS) resin is a 30 % Glass Reinforced, injection moldable grade with improved hydrolytic stability; this grade has been developed for fluid en.. |