SABIC Innovative Plastics LNP THERMOCOMP DF005 PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP DF005 PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* DF005 is a compound based on Polycarbonate containing 25% Glass Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.40 g/cc | 1.40 g/cc | ASTM D792 |
| Moisture Absorption | 0.140 % | 0.140 % | 50% RH, 24 hrs; ASTM D570 |
| 0.200 % | 0.200 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0050 cm/cm @Time 86400 sec |
0.0020 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0080 cm/cm @Time 86400 sec |
0.0050 - 0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 107 MPa | 15500 psi | 5 mm/min; ISO 527 |
| 108 MPa | 15700 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 109 MPa | 15800 psi | Type I, 5 mm/min; ASTM D638 |
| 109 MPa | 15800 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 3.3 % | 3.3 % | 5 mm/min; ISO 527 |
| 3.4 % | 3.4 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 2.7 % | 2.7 % | 5 mm/min; ISO 527 |
| 3.0 % | 3.0 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 7.89 GPa | 1140 ksi | 1 mm/min; ISO 527 |
| 8.33 GPa | 1210 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 180 MPa | 26100 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 180 MPa | 26100 psi | ISO 178 | |
| Flexural Yield Strength | 180 MPa | 26100 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 6.99 GPa | 1010 ksi | 2 mm/min; ISO 178 |
| 7.02 GPa | 1020 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 1.09 J/cm | 2.04 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 9.01 J/cm | 16.9 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 54.0 kJ/m² | 25.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 16.0 J @Temperature 23.0 °C |
11.8 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 2.00 µm/m-°C @Temperature -30.0 - 30.0 °C |
1.11 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 7.00 µm/m-°C @Temperature -30.0 - 30.0 °C |
3.89 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 145 °C | 293 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 144 °C @Thickness 3.20 mm |
291 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 141 °C | 286 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 141 °C @Thickness 3.20 mm |
286 °F @Thickness 0.126 in |
unannealed; ASTM D648 |