Precision Polymer Engineering V70A Fluoroelastomer Compound
| Category | Polymer , Thermoset , Fluoropolymer, TS , Thermoset Fluoroelastomer , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | Precision Polymer Engineering Limited |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Precision Polymer Engineering V70A Fluoroelastomer Compound.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Blue Fluoroelastomer Rubber, 65-75 °IRHD. Copolymer of vinylidene fluoride and hexafluoropropylene. To meet ASTM D2000 line call-out: M2HK710, A1-10, B38, EF31, EO78, F15, Z1, Z2, where Z1 = comp-set 30% max, Z2 = Blue. ASTM designation = FKM. ISO designation = FPM.Applications: Excellent resistance to oils, fuels and hydraulic fluids at high temperature.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 70 | 70 | °IRHD; ASTM D1415 |
| 80 | 80 | °IRHD, +10 change after 72 hours @ 250°C; ASTM D1415 | |
| Tensile Strength, Yield | 7.50 MPa | 1090 psi | -25% change after 72 hours @ 250°C; ASTM D412 |
| 10.0 MPa | 1450 psi | ASTM D412 | |
| Elongation at Break | 131.25 % | 131.25 % | -25% change after 72 hours @ 250°C; ASTM D412 |
| 175 % | 175 % | ASTM D412 | |
| Compression Set | 30 % | 30 % | 22 hours @ 175°C; ASTM D395 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 200 °C | 392 °F | |
| Minimum Service Temperature, Air | -10.0 °C | 14.0 °F | |
| Flash Point | >= 315 °C | >= 599 °F |