Overview of materials for Nylon 66, Carbon Fiber/PTFE Filled

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Carbon Fiber/PTFE Filled
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Nylon 66, Carbon Fiber/PTFE Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Carbon Fiber/PTFE Filled". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.18 - 1.54 g/cc
0.0426 - 0.0556 lb/in³
Average value: 1.32 g/cc Grade Count:86
Filler Content 5.00 - 50.0 %
5.00 - 50.0 %
Average value: 22.7 % Grade Count:32
Water Absorption 0.100 - 1.00 %
0.100 - 1.00 %
Average value: 0.690 % Grade Count:57
Linear Mold Shrinkage 0.000200 - 0.0160 cm/cm
0.000200 - 0.0160 in/in
Average value: 0.00278 cm/cm Grade Count:82
Linear Mold Shrinkage, Transverse 0.00100 - 0.0110 cm/cm
0.00100 - 0.0110 in/in
Average value: 0.00708 cm/cm Grade Count:6
Mechanical Properties Metric English Comments
Hardness, Rockwell R 110 - 120
110 - 120
Average value: 118 Grade Count:27
Tensile Strength, Ultimate 75.8 - 241 MPa
11000 - 35000 psi
Average value: 176 MPa Grade Count:75
105 - 170 MPa

@Temperature 60.0 - 150 °C
15200 - 24700 psi

@Temperature 140 - 302 °F
Average value: 135 MPa Grade Count:1
Tensile Strength, Yield 112 - 200 MPa
16200 - 29000 psi
Average value: 171 MPa Grade Count:12
Elongation at Break 0.900 - 182 %
0.900 - 182 %
Average value: 5.21 % Grade Count:65
2.50 - 3.80 %

@Temperature 60.0 - 150 °C
2.50 - 3.80 %

@Temperature 140 - 302 °F
Average value: 3.25 % Grade Count:1
Elongation at Yield 1.10 - 6.00 %
1.10 - 6.00 %
Average value: 2.86 % Grade Count:22
Modulus of Elasticity 3.45 - 32.4 GPa
500 - 4710 ksi
Average value: 16.1 GPa Grade Count:64
8.30 - 22.5 GPa

@Temperature 60.0 - 150 °C
1200 - 3260 ksi

@Temperature 140 - 302 °F
Average value: 14.5 GPa Grade Count:1
Flexural Yield Strength 107 - 372 MPa
15500 - 54000 psi
Average value: 260 MPa Grade Count:82
Flexural Modulus 2.76 - 24.8 GPa
400 - 3600 ksi
Average value: 12.8 GPa Grade Count:83
Compressive Yield Strength 89.6 - 172 MPa
13000 - 25000 psi
Average value: 134 MPa Grade Count:12
Izod Impact, Notched 0.320 - 2.40 J/cm
0.600 - 4.50 ft-lb/in
Average value: 0.882 J/cm Grade Count:64
Izod Impact, Unnotched 3.20 - 10.7 J/cm
6.00 - 20.0 ft-lb/in
Average value: 6.85 J/cm Grade Count:45
Izod Impact, Notched (ISO) 5.00 - 10.9 kJ/m²
2.38 - 5.19 ft-lb/in²
Average value: 8.52 kJ/m² Grade Count:4
Izod Impact, Unnotched (ISO) 41.0 - 68.5 kJ/m²
19.5 - 32.6 ft-lb/in²
Average value: 55.2 kJ/m² Grade Count:4
Charpy Impact Unnotched 2.60 - 6.50 J/cm²
12.4 - 30.9 ft-lb/in²
Average value: 4.16 J/cm² Grade Count:20
3.00 - 4.00 J/cm²

@Temperature -30.0 - -20.0 °C
14.3 - 19.0 ft-lb/in²

@Temperature -22.0 - -4.00 °F
Average value: 3.50 J/cm² Grade Count:8
Charpy Impact, Notched 0.500 - 1.20 J/cm²
2.38 - 5.71 ft-lb/in²
Average value: 0.889 J/cm² Grade Count:9
0.600 - 0.900 J/cm²

@Temperature -30.0 - -20.0 °C
2.86 - 4.28 ft-lb/in²

@Temperature -22.0 - -4.00 °F
Average value: 0.713 J/cm² Grade Count:8
Coefficient of Friction 0.0900 - 0.600
0.0900 - 0.600
Average value: 0.196 Grade Count:19
Coefficient of Friction, Static 0.0700 - 0.560
0.0700 - 0.560
Average value: 0.166 Grade Count:19
K (wear) Factor 10.1 - 30.2 x 10-8 mm³/N-M
5.00 - 15.0 x 10-10 in³-min/ft-lb-hr
Average value: 16.3 x 10<sup>-8</sup> mm³/N-M Grade Count:10
Limiting Pressure Velocity 0.771 - 3.30 MPa-m/sec
22000 - 94200 psi-ft/min
Average value: 1.45 MPa-m/sec Grade Count:5
Thermal Properties Metric English Comments
CTE, linear 14.0 - 80.0 µm/m-°C
7.78 - 44.4 µin/in-°F
Average value: 25.5 µm/m-°C Grade Count:29
Thermal Conductivity 0.330 - 1.15 W/m-K
2.29 - 8.00 BTU-in/hr-ft²-°F
Average value: 0.553 W/m-K Grade Count:15
Melting Point 249 - 275 °C
480 - 527 °F
Average value: 261 °C Grade Count:6
Maximum Service Temperature, Air 90.0 - 160 °C
194 - 320 °F
Average value: 137 °C Grade Count:19
Deflection Temperature at 0.46 MPa (66 psi) 144 - 270 °C
292 - 518 °F
Average value: 250 °C Grade Count:34
Deflection Temperature at 1.8 MPa (264 psi) 139 - 260 °C
283 - 500 °F
Average value: 245 °C Grade Count:73
Vicat Softening Point 200 - 255 °C
392 - 491 °F
Average value: 241 °C Grade Count:13
Flammability, UL94 HB - V-2
HB - V-2
Grade Count:37
Electrical Properties Metric English Comments
Electrical Resistivity 0.100 - 1.00e+8 ohm-cm
0.100 - 1.00e+8 ohm-cm
Average value: 1260 ohm-cm Grade Count:45
Surface Resistance 1.00 - 1.00e+10 ohm
1.00 - 1.00e+10 ohm
Average value: 4.17e+8 ohm Grade Count:28
Insulation Resistance 1000 - 1.00e+10 ohm
1000 - 1.00e+10 ohm
Average value: 5.56e+8 ohm Grade Count:18
Processing Properties Metric English Comments
Processing Temperature 274 - 293 °C
525 - 560 °F
Average value: 287 °C Grade Count:42
Nozzle Temperature 280 - 300 °C
536 - 572 °F
Average value: 290 °C Grade Count:19
Melt Temperature 260 - 310 °C
500 - 590 °F
Average value: 296 °C Grade Count:45
Mold Temperature 65.6 - 121 °C
150 - 250 °F
Average value: 93.5 °C Grade Count:64
Drying Temperature 75.0 - 107 °C
167 - 225 °F
Average value: 87.6 °C Grade Count:43
Moisture Content 0.200 %
0.200 %
Average value: 0.200 % Grade Count:18
Dew Point -17.8 °C
0.000 °F
Average value: -17.8 °C Grade Count:15
Injection Pressure 68.9 - 124 MPa
10000 - 18000 psi
Average value: 101 MPa Grade Count:34