NatureWorks® Ingeo™ 6302D Fiber Grade PLA

Category Polymer , Renewable/Recycled Polymer , Thermoplastic , Polylactic Acid (PLA) Biopolymer
Manufacturer NatureWorks LLC
Trade Name Ingeo™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF NatureWorks® Ingeo™ 6302D Fiber Grade PLA.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
NatureWorks® PLA polymer 6302D is an amorphous thermoplastic fiber-grade resin derived primarily from annually renewable resources. Available in pellet form, 6302D is designed for extrusion into mechanically drawn staple fibers using conventional fiber spinning and drawing equipment. NatureWorks® PLA 6302D can be used as a low melt binder polymer in a sheath-core configuration. Potential applications for PLA polymer 6302D include Thermal bonded nonwovens
Physical Properties Metric English Comments
Specific Gravity 1.24 g/cc
1.24 g/cc
ASTM D792
Melt Density 1.08 g/cc

@Temperature 230 °C
0.0390 lb/in³

@Temperature 446 °F
ASTM D1238
Viscosity Measurement 3.0
3.0
Relative Viscosity; CD Internal Viscotek Method
Melt Flow 20 g/10 min

@Load 2.16 kg,
Temperature 210 °C
20 g/10 min

@Load 4.76 lb,
Temperature 410 °F
ASTM D1238
Mechanical Properties Metric English Comments
Elongation at Break 50 %
50 %
Fiber; ASTM D2256/ASTM D3822
Tenacity 0.309 N/tex
3.50 g/denier
ASTM D2256/ASTM D3822
Thermal Properties Metric English Comments
Melting Point 125 - 135 °C
257 - 275 °F
ASTM D3418
Glass Transition Temp, Tg 55.0 - 60.0 °C
131 - 140 °F
ASTM D3417
Shrinkage 2.0 %

@Temperature 85.0 °C,
Time 900 sec
2.0 %

@Temperature 185 °F,
Time 0.250 hour
Hot Air
Processing Properties Metric English Comments
Dew Point -35.0 °C
-31.0 °F
Drying Air Flow Rate >= 14.2 l/min
>= 0.500 ft³/min (CFM)