I. Stern 913 High Impact Polystyrene Extrusion Grade
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified |
| Manufacturer | I. Stern & Company |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | I. Stern 913 High Impact Polystyrene Extrusion Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features:Good processing characteristicsExcellent toughness and environmental stress crackingApplicationsThermoformed containers and lids for food packagingCustom extruded sheetInformation provided by I. Stern & Co. Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 2.6 g/10 min | 2.6 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 29.0 MPa | 4200 psi | ASTM D638 |
| Elongation at Yield | 67 % | 67 % | ASTM D638 |
| Flexural Strength | 42.1 MPa | 6100 psi | ASTM D790 |
| Flexural Modulus | 2.14 GPa | 310 ksi | ASTM D790 |
| Izod Impact, Notched | 1.92 J/cm | 3.60 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 83.9 °C | 183 °F | ASTM D648 |
| Vicat Softening Point | 92.2 °C | 198 °F | ASTM D1525 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
|
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |