Honeywell ACLAR® Cx™ 8A Heat Sealable, Co-Extruded CTFE Film (discontinued **)
| Category | Polymer , Film , Thermoplastic , Fluoropolymer , Polychlorotrifluoroethylene (PCTFE); Molded |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Honeywell ACLAR® Cx™ 8A Heat Sealable, Co-Extruded CTFE Film
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: ACLAR® Cx™ 8A is a heat sealable coextruded CTFE film.Information provided by Honeywell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | gas pycnometer |
| Water Vapor Transmission | 0.780 g/m²/day | 0.0502 g/100 in²/day | 100°F (37.8°C) / 100%RH; ASTM F1249 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 75 - 100 % | 75 - 100 % | ASTM D882 |
| Film Elongation at Break, TD | 225 - 325 % | 225 - 325 % | ASTM D882 |
| Secant Modulus, MD | 0.448 - 0.586 GPa | 65.0 - 85.0 ksi | ASTM D882 |
| Secant Modulus, TD | 0.448 - 0.586 GPa | 65.0 - 85.0 ksi | ASTM D882 |
| Tear Strength Test | 350 - 375 | 350 - 375 | graves tear MD, grams/mil; ASTM D1004 |
| 350 - 375 | 350 - 375 | graves tear TD, grams/mil; ASTM D1004 | |
| Film Tensile Strength at Break, MD | 26.2 - 31.7 MPa | 3800 - 4600 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 17.9 - 20.0 MPa | 2600 - 2900 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | <= 3.0 % | <= 3.0 % | ASTM D1003 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Interlayer Bond Strength | min 450 g/in | ASTM F904 |
| Puncture Strength | 250-300 g | ASTM F1309 |
Users viewing this material also viewed the following:
- Mo-Sci Corporation GL-0263 Cu Coated Borosilicate Glass Spheres
- Karina 36/234-FC-LMP (SDB) Brown Color Concentrate for PVC
- Karina 837-10/119-E-ERYB White PVC Compound
- H.C. Starck HPM 1700 Tungsten High Density Composite
- SABIC Innovative Plastics ULTEM 1010M PEI (Asia Pacific)
- A. Schulman PP 1255-01 Polypropylene General Purpose Homopolymer Polypropylene
- Polyram BondyRam® 1001 Maleic Anhydride modified Homo-polypropylene coupling agent
- Loctite® 609 General Purpose Retaining Compound
- Cresset Powers Cress-Alon™ NE6040-ST 4% Nano Clay Loaded, 6.0 r.v. Super Tough Grade Nylon 6, 50% RH
- Entec Hylac® EX18 ABS
Copyright © lookpolymers.com All Rights Reserved