Hexcel® HexWeb® CR-PAA™ 3/16-5052-0.003 Phosphoric Acid Anodized Aluminum Honeycomb

Category Metal , Metal Foam, Mesh, or Honeycomb , Nonferrous Metal , Aluminum Alloy , 5000 Series Aluminum Alloy
Manufacturer Hexcel
Trade Name HexWeb®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Hexcel® HexWeb® CR-PAA™ 3/16-5052-0.003 Phosphoric Acid Anodized Aluminum Honeycomb.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Grade is designated as "Cell Size-Alloy-Foil Gauge." The life cycle of aluminum honeycomb sandwich structures in a given application can be directly related to the quality of the bond between the face sheets that carry bending loads and the honeycomb that carries the shear loads. The adhesive is the interface between the facing and the core in the same way that the oxide on the aluminum and the primer that has been applied to it is the interface between the honeycomb substrate material and the bonding adhesive. This interface is critical to the performance of honeycomb bonded assemblies.HexWeb® CR-PAA™ is designed for aircraft structures that are exposed to demanding environmental conditions. HexWeb® CR-PAA™ outperforms standard MIL-C-7438 core in salt spray and HexWeb® crack propagation tests.
Physical Properties Metric English Comments
Density 0.130 g/cc
0.00469 lb/in³
Nominal
Mechanical Properties Metric English Comments
Compressive Yield Strength >= 6.89 MPa
>= 1000 psi
Bare, min
>= 7.58 MPa
>= 1100 psi
Stabilized, min
11.0 MPa
1600 psi
Bare, typ
11.9 MPa
1720 psi
Stabilized, typ
Compressive Modulus 2.41 GPa
350 ksi
Stabilized, typ
Shear Modulus 0.372 GPa
54.0 ksi
Plate Shear, W Direction, typ
0.931 GPa
135 ksi
Plate Shear, L Direction, typ
Shear Strength >= 2.76 MPa
>= 400 psi
Plate Shear, W Direction, min
3.31 MPa
480 psi
Plate Shear, W Direction, typ
>= 4.62 MPa
>= 670 psi
Plate Shear, L Direction, min
5.00 MPa
725 psi
Plate Shear, L Direction, typ