Haysite SDL® H400 Polyester Composite
| Category | Polymer , Thermoset , Polyester, TS |
| Manufacturer | Haysite |
| Trade Name | SDL® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Haysite SDL® H400 Polyester Composite.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
H400 is an advanced composite that combines high temperature resistant and high strength characteristics with static dissipative properties for use as wave and reflow solder pallets. SDL Grade H400 may be used as dedicated or adjustable flow solder carriers as well as surface mount pallets. Listed below are the expected performance properties of this material. H400 is available in sanded thicknesses from 3, 5, 6, 8, 10 and 12mm and in sheet sizes 36" x 72" and 48" x 96". Standard color is Black.Information provided by Haysite
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.84 g/cc | 1.84 g/cc | ASTM D792 |
| Water Absorption | 0.23 % @Time 86400 sec |
0.23 % @Time 24.0 hour |
ASTM D651 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Barcol | 45 - 50 | 45 - 50 | ASTM D2583 |
| Flexural Strength | 47.00 MPa @Temperature 200 °C |
6817 psi @Temperature 392 °F |
LW; ASTM D790 |
| 50.00 MPa @Temperature 200 °C |
7252 psi @Temperature 392 °F |
CW; ASTM D790 | |
| 73.526 MPa @Temperature 150 °C |
10664 psi @Temperature 302 °F |
LW; ASTM D790 | |
| 77.50 MPa @Temperature 150 °C |
11240 psi @Temperature 302 °F |
CW; ASTM D790 | |
| 223.02 MPa @Temperature 25.0 °C |
32347 psi @Temperature 77.0 °F |
LW; ASTM D790 | |
| 238.00 MPa @Temperature 25.0 °C |
34519 psi @Temperature 77.0 °F |
CW; ASTM D790 | |
| Flexural Modulus | 0.00615 GPa @Temperature 200 °C |
0.892 ksi @Temperature 392 °F |
LW; ASTM D790 |
| 0.00680 GPa @Temperature 200 °C |
0.986 ksi @Temperature 392 °F |
CW; ASTM D790 | |
| 0.007129 GPa @Temperature 150 °C |
1.034 ksi @Temperature 302 °F |
LW; ASTM D790 | |
| 0.007963 GPa @Temperature 150 °C |
1.155 ksi @Temperature 302 °F |
CW; ASTM D790 | |
| 0.01532 GPa @Temperature 25.0 °C |
2.222 ksi @Temperature 77.0 °F |
LW; ASTM D790 | |
| 0.01616 GPa @Temperature 25.0 °C |
2.344 ksi @Temperature 77.0 °F |
CW; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 24.1 µm/m-°C | 13.4 µin/in-°F | VSM 77110 |
| Specific Heat Capacity | 0.946 J/g-°C | 0.226 BTU/lb-°F | ASTM E-1269-05 |
| Thermal Conductivity | 0.428 W/m-K | 2.97 BTU-in/hr-ft²-°F | ASTM E-1925-06 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1e+05 - 1.00e+9 ohm-cm | 1e+05 - 1.00e+9 ohm-cm | ASTM D257 |
Users viewing this material also viewed the following:
- Polykemi AB POLYblend 85V PC/ABS-Blend, Flame Retardant
- SABIC Innovative Plastics Lexan® AD4820 PC
- Lanxess Durethan® BKV 230 H2.0 901510 Copolyamide, 30% Glass Fiber
- A. Schulman PP 2268-01 Polypropylene High Flow, Impact Copolymer Polypropylene
- A. Schulman POLYFORT™ FPP 1434 Couple Mica In Copolymer Polypropylene (25% Mineral Filled)
- Chase Plastics CP Pryme® A110 ABS, 10% Glass Fiber Reinforced
- CIMBAR MV 610 Talc
Copyright © lookpolymers.com All Rights Reserved