ExxonMobil Bicor™ 120 XRG-2 OPP Film
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade |
| Manufacturer | Exxon Chemical |
| Trade Name | Bicor™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil Bicor™ 120 XRG-2 OPP Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: Bicor 120 XRG-2 is a one-side sealable OPP film that can be used as the inside web of a lamination where exceptional seal performance is required. The high-energy surface is intended as the print and laminating side.Availability: Latin America, North America and South AmericaKey Features:Low MST, very broad seal range with excellent hot tack.High-energy surface for excellent ink adhesion and bond strengths in adhesive and extrusion laminations.Lap seals to coex sealants without thermal stripe. Features:In Lamination Lap SealableVery Broad Seal RangeApplications:BakeryBiscuits/Cookie/Crackers Crisps and SnacksFrozen FoodIce Cream Uses:HFFS Flexible Packaging VFFS Flexible PackagingProcessing Method: Inner Web Adhesive Lamination, Inner Web Extrusion Lamination, Solvent Flexographic Printing, Solvent Rotogravure Printing, Surface Print Unsupported and Water-based Flexographic PrintingInformation provided by ExxonMobil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Thickness | 30.5 microns | 1.20 mil | ExxonMobil Method |
| Coating Weight | 27.0 g/m² | 16.9 lb/ream | ExxonMobil Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 182 % | 182 % | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
| Film Elongation at Break, TD | 46 % | 46 % | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
| Coefficient of Friction | 0.40 | 0.40 | Untreated Surface; ExxonMobil Method |
| Film Tensile Strength at Break, MD | 131 MPa | 19000 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
| Film Tensile Strength at Break, TD | 283 MPa | 41000 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 4.0 % @Temperature 135 °C |
4.0 % @Temperature 275 °F |
ExxonMobil Method |
| Shrinkage, TD | 3.0 % @Temperature 135 °C |
3.0 % @Temperature 275 °F |
ExxonMobil Method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 3.2 % | 3.2 % | ExxonMobil Method |
| Gloss | 82 % | 82 % | 45°; ExxonMobil Method |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Crimp Seal MST | 192°F | Untreated |
| Crimp Seal Strength | 460 g/in | Treated/Treated, 240°F (116°C), 20 psi (0.1 MPa), 0.8 sec |
| 460 g/in | Untreated/Untreated, 240°F (116°C), 20 psi (0.1 MPa), 0.8 sec | |
| Wetting Tension | 0.8 receding cos theta | Treated Surface |
| Yield | 254000 in2/lb |